TECHNICAL POLYAMIDES POLIAMMIDI TECnICHE - Nilit
TECHNICAL POLYAMIDES POLIAMMIDI TECnICHE - Nilit
TECHNICAL POLYAMIDES POLIAMMIDI TECnICHE - Nilit
You also want an ePaper? Increase the reach of your titles
YUMPU automatically turns print PDFs into web optimized ePapers that Google loves.
PhisicAl<br />
fisicHe<br />
mechAnicAl<br />
meccAnicHe<br />
thermAl<br />
termicHe<br />
electricAl<br />
elettricHe<br />
flAmmAbility<br />
infiAmmAbilità<br />
<strong>TECHNICAL</strong> POLYAMIDE<br />
<strong>POLIAMMIDI</strong> <strong>TECnICHE</strong> UNFILLED<br />
TYPE - TIPO<br />
PROPERTIES UNIT STANDARD<br />
PROPRIETA ,<br />
UnITA ,<br />
METODO<br />
POlyNil<br />
P50 Fi<br />
PA6.6, unfilled,<br />
internAlly lubricAted, 2.7<br />
relAtive viscosity fAst<br />
cycling, fdA comPliAnt<br />
PA6.6, non rinforzAtA,<br />
lubrificAtA internAmente,<br />
viscosità 2,7 Per cicli<br />
di stAmPAggio rAPidi,<br />
conforme fdA<br />
POlyNil<br />
P50 Fl<br />
PA6.6, unfilled,<br />
nucleAted,<br />
2.7 viscosity,<br />
fAst cycling<br />
PA6.6, non rinforzAtA,<br />
nucleAtA, viscosità<br />
2,7, cicli di stAmPAggio<br />
rAPidi<br />
POlyNil<br />
P50 lHS<br />
PA6.6, unfilled,<br />
high heAt Aging<br />
resistAnt, 2.7 viscosity<br />
PA6.6, non rinforzAtA,<br />
mAssimA resistenzA<br />
Al cAlore, viscosità 2.7<br />
POlyNil<br />
P240 lHSV<br />
PA6.6, unfilled,<br />
high heAt Aging<br />
resistAnt,<br />
5 viscosity<br />
PA6.6, non<br />
rinforzAtA, mAssimA<br />
stAbilizzAzione Al<br />
cAlore, viscosità 5<br />
density 23°c<br />
densità 23°c g/cm 3 iso 1183 1,14 1,14 1,14 1,14<br />
mould shrinkAge PArAllel/normAl 23°c<br />
ritiro Allo stAmPAggio longitudinAle/trAsversAle 23°c % iso 294-4 1,3/1,3 1,1/1,1 1,3/1,3 1,3/1,3<br />
moisture AbsorPtion in wAter 23°c - 24h/sAturAtion<br />
Assorbimento umidità in AcquA 23°c - 24H/sAturAzione % iso 62 1,5/8,5 1,5/8,5 1,5/8,5 1,5/8,5<br />
notched izod imPAct strength 23°c<br />
resistenzA All'urto izod con intAglio 23°c KJ/m 2 iso 180/A 5,5 5,0 5,5 5,5<br />
notched izod imPAct strength -30°c<br />
resistenzA All'urto izod con intAglio -30°c KJ/m 2 iso 180/A 4,5 4,0 3,5 5,0<br />
unnotched chArPy imPAct strength 23°c<br />
resistenzA All'urto cHArPy senzA intAglio 23°c KJ/m 2 iso 179/1eu nb nb nb nb<br />
unnotched chArPy imPAct strength -30°c<br />
resistenzA All'urto cHArPy senzA intAglio -30°c KJ/m 2 iso 179/1eu nb nb nb nb<br />
notched chArPy imPAct strength 23°c<br />
resistenzA All'urto cHArPy con intAglio 23°c KJ/m 2 iso 179/1eA 5,0 4,5 5,0 5,0<br />
notched chArPy imPAct strength -30°c<br />
resistenzA All'urto cHArPy con intAglio -30°c KJ/m 2 iso 179/1eA 4,0 3,5 4,0 4,0<br />
tensile yield stress 23°c<br />
sforzo A snervAmento in trAzione 23°c mPa iso 527 81 85 85 85<br />
tensile modulus 23°c<br />
modulo elAstico in trAzione 23°c mPa iso 527 3100 3300 3100 3100<br />
tensile yield strAin 23°c<br />
deformAzione A snervAmento in trAzione 23°c % iso 527 6,0 5,0 5,0 4,4<br />
tensile strAin At breAk 23°c<br />
deformAzione A rotturA in trAzione 23°c % iso 527 50 35 40 40<br />
flexurAl yield stress 23°c<br />
sforzo A snervAmento in flessione 23°c mPa iso 178 120 130 120 115<br />
flexurAl yield stress 90°c<br />
sforzo A snervAmento in flessione 90°c mPa iso 178 30 35 30 30<br />
flexurAl modulus 23°c<br />
modulo elAstico A flessione 23°c mPa iso 178 2850 3000 2850 2900<br />
flexurAl modulus 90°c<br />
modulo elAstico A flessione 90°c mPa iso 178 800 850 800 800<br />
vicAt - softening temPerAture 49n<br />
vicAt - temPerAturA di rAmmollimento 49n °c iso 306 240 245 240 240<br />
hdt - deflection temPerAture under loAd 0.45n/mm2 2 Hdt - temPerAturA di deformAzione sotto cArico 0.45n/mm °c iso 75 225 230 225 230<br />
hdt - deflection temPerAture under loAd 1.82n/mm2 2 Hdt - temPerAturA di deformAzione sotto cArico 1.82n/mm °c iso 75 75 85 75 75<br />
heAt resistAnce - bAll test 125°c/165°c<br />
resistenzA Al cAlore - test dellA bigliA 125°c/165°c iec 60695-10-2 oK/oK oK/oK oK/oK oK/oK<br />
continuous service temPerAture 20000h<br />
temPerAturA di esercizio continuo 20000H °c iec 60216 85 85 130 130<br />
dielectric strength 2mm<br />
rigidità dielettricA 2mm Kv/mm iec 60243 18 18 18 18<br />
surfAce resistivity 23°c<br />
resistività di suPerficie 23°c ohm iec 60093 10*12 10*12 10*12 10*12<br />
volume resistivity 23°c<br />
resistività di volume 23°c iec 60093 10*13 10*13 10*13 10*13<br />
cti - comPArAtive trAcking index 3.2mm, sol. A<br />
cti - resistenzA Alle correnti strisciAnti 3.2mm, sol. A v iec 60112 600 600 600 600<br />
oxygen index<br />
indice di ossigeno % iso 4589 28 28 28 28<br />
flAmmAbility rAting 3.2 (1.6)mm<br />
clAsse d'infiAmmAbilità 3.2 (1.6)mm ul 94 v2 (v2) v2 (v2) v2(v2) v2 (v2)<br />
flAmmAbility rAting 0.8 (0.4)mm<br />
clAsse d'infiAmmAbilità 0.8 (0.4)mm ul 94 v2 v2 v2(v2) v2<br />
neddle test 2.0 (1.0)mm<br />
Ago iPodermico 2.0 (1.0)mm iec 60695-11-5 - - - -<br />
glow wire flAmmAbility index 3.2 (0.8)mm<br />
filo incAndescente (indice di infiAmmAbilità) 3.2 (0.8)mm °c iec 60695-2-12 850 (750) 850 (750) 850 (850) 850 (750)<br />
glow wire ignition test 3.2 (0.8)mm<br />
filo incAndescente (temPerAturA di ignizione) 3.2 (0.8)mm °c iec 60695-2-13 750 (775) 750 (775) 750 (775) 750 (775)<br />
flAmmAbility rAting 355 x 100 x 1mm<br />
clAsse d'infiAmmAbilità 355 x 100 x 1mm fmvss no.302 se se se se<br />
ul listed - certificAto ul