Chapter 5 Cytotoxicity assay, Cell Adhesion <strong>and</strong> Spreading See Chapter 4, experimental section. Electrospinning Process Polymers (PLA, PTAm or PTAm-b-PLA-b-PTAm) were dissolved in dichloromethane to achieve a certain concentration. The solution was stirred for 48 h at ice water bath <strong>and</strong> then loaded into the spinner with a capillary outlet <strong>of</strong> 1 mm in diameter, which as an anode was 20 cm apart from the grounded collecting drum. The voltage applied between the spinner outlet <strong>and</strong> the drum was 15 kV. The resulted mats were collected on an aluminum sheet fixed on the rotating drum for 3 h. Then the obtained product was dried in a vacuum oven for 24 h. Reference 1. M. F. Semmelhack, C. R. Schmid, D. A. Cortes, C. S. Chou, J. Am. Chem. Soc. 1984, 106, 3374. 2. H. Nishide, T. Kaneko, Magnetic properties <strong>of</strong> organic material. Dekker: New York, 1999. 3. E. E. Voest, E. Vanfaassen, J. J. M. Marx, Free Radical Biol. Med. 1993, 15, 589. 4. K. Koshika, N. Sano, K. Oyaizu, H. Nishide, Chem. Commun. 2009, 7, 836. 5. R. Barbey, L. Lavanant, D. Paripovic, N. Schuwer, C. Sugnaux, S. Tugulu, H. A. Klok, Chem. Rev. 2009, 109, 5437. 6. A. Vora, K. Singh, D. C. Webster, Polymer 2009, 50, 2768. 7. J. L. Zhu, X. Z. Zhang, H. Cheng, Y. Y. Li, Cheng, S. X.; Zhuo, R. X., J. Polym. Sci., Part A: Polym. Chem. 2007, 45, 5354. 8. A. K. Ekaputra, Y. F. Zhou, S. M. Cool, D. W. Hutmacher, Tissue Engineering Part A 2009, 15, 3779. 9. X. L. Xu, X. S. Chen, A. X. Liu, Z. K. Hong, X. B. Jing, Eur. Polym. J. 2007, 43, 3187. 10. Y. L. Hong, Y. A. Li, X. L. Zhuang, X. S. Chen, X. B. Jing, J. Biomed. Mater. Res. Part A 2009, 89A, 345. 11. M. Li, M. J. Mondrinos, M. R. G<strong>and</strong>hi, F. K. Ko, A. S. Weiss, P. I. Lelkes, Biomaterials 2005, 26, 5999. 12. J. A. Matthews, G. E. Wnek, D. G. Simpson, G. L. Bowlin, Biomacromolecules 2002, 3, 232. ‐ 110 ‐
‐ 111 ‐ <strong>Synthesis</strong> <strong>of</strong> Triblock Copolymers <strong>of</strong> TEMPO‐Acrylamide <strong>and</strong> Lactate by RAFT Polymerization 13. J. M. Deitzel, J. Kleinmeyer, D. Harris, N. C. Beck Tan, Polymer 2001, 42, 261. 14. Y. J. Ryu, H. Y. Kim, K. H. Lee, H. C. Park, D. R. Lee, Eur. Polym. J. 2003, 39, 1883.