2.B-28 API RECOMMENDED PRACTICE 581Table 2.B.3.9—High Temperature Sulfidic and Naphthenic Acid Corrosion—Estimated CorrosionRates for 316 SS with < 2.5 % Mo (mpy)Sulfur(wt%)TAN(mg/g)Temperature (°F)≤450 500 550 600 650 700 750 >7500.2 1 1 1 1 1 1 1 10.23.0 1 1 1 1 1 2 2 24.0 1 1 1 2 4 5 7 100.2 1 1 1 1 1 1 1 10.43.0 1 1 1 1 2 2 2 24.0 1 1 2 3 4 5 7 100.2 1 1 1 1 1 1 1 10.83.0 1 1 1 1 2 2 2 34.0 1 1 2 3 5 5 7 100.2 1 1 1 1 1 1 1 11.53.0 1 1 1 1 3 3 3 44.0 1 1 3 5 5 5 7 100.2 1 1 1 1 1 1 1 12.53.0 1 1 1 2 3 3 4 54.0 1 1 3 5 5 6 8 100.2 1 1 1 1 1 1 1 23.03.0 1 1 1 2 4 5 5 64.0 1 2 3 5 5 6 8 10NOTEIncludes stainless steels with < 2.5 % Mo, e.g. 316, 316L, 316H, etc.
RISK-BASED INSPECTION METHODOLOGY, PART 2, ANNEX 2.B—DETERMINATION OF CORROSION RATES 2.B-29Table 2.B.3.9M—High Temperature Sulfidic and Naphthenic Acid Corrosion—Estimated CorrosionRates for 316 SS with < 2.5 % Mo (mm/y)Sulfur(wt%)TAN(mg/g)Temperature (°C)≤232 260 288 315 343 371 399 >3990.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.030.23.0 0.03 0.03 0.03 0.03 0.03 0.05 0.05 0.054.0 0.03 0.03 0.03 0.05 0.10 0.13 0.18 0.250.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.030.43.0 0.03 0.03 0.03 0.03 0.05 0.05 0.05 0.054.0 0.03 0.03 0.05 0.08 0.10 0.13 0.18 0.250.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.030.83.0 0.03 0.03 0.03 0.03 0.05 0.05 0.05 0.084.0 0.03 0.03 0.05 0.08 0.13 0.13 0.18 0.250.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.031.53.0 0.03 0.03 0.03 0.03 0.08 0.08 0.08 0.104.0 0.03 0.03 0.08 0.13 0.13 0.13 0.18 0.250.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.032.53.0 0.03 0.03 0.03 0.05 0.08 0.08 0.10 0.134.0 0.03 0.03 0.08 0.13 0.13 0.15 0.20 0.250.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.053.03.0 0.03 0.03 0.03 0.05 0.10 0.13 0.13 0.154.0 0.03 0.05 0.08 0.13 0.13 0.15 0.20 0.25NOTEIncludes stainless steels with < 2.5 % Mo, e.g. 316, 316L, 316H, etc.
- Page 207 and 208: RISK-BASED INSPECTION METHODOLOGY,
- Page 209 and 210: RISK-BASED INSPECTION METHODOLOGY,
- Page 211 and 212: CONTENTSTABLE 2.A.1—LEADERSHIP AN
- Page 213 and 214: 2.A-2 API RECOMMENDED PRACTICE 581T
- Page 215 and 216: 2.A-4 API RECOMMENDED PRACTICE 581T
- Page 217 and 218: 2.A-6 API RECOMMENDED PRACTICE 581T
- Page 219 and 220: 2.A-8 API RECOMMENDED PRACTICE 581T
- Page 221 and 222: 2.A-10 API RECOMMENDED PRACTICE 581
- Page 223 and 224: 2.A-12 API RECOMMENDED PRACTICE 581
- Page 225 and 226: 2.A-14 API RECOMMENDED PRACTICE 581
- Page 227 and 228: PART 2, ANNEX 2.BDETERMINATION OF C
- Page 229 and 230: 2.B.8 AMINE CORROSION .............
- Page 231 and 232: Risk-Based Inspection MethodologyPa
- Page 233 and 234: RISK-BASED INSPECTION METHODOLOGY,
- Page 235 and 236: RISK-BASED INSPECTION METHODOLOGY,
- Page 237 and 238: RISK-BASED INSPECTION METHODOLOGY,
- Page 239 and 240: RISK-BASED INSPECTION METHODOLOGY,
- Page 241 and 242: RISK-BASED INSPECTION METHODOLOGY,
- Page 243 and 244: RISK-BASED INSPECTION METHODOLOGY,
- Page 245 and 246: RISK-BASED INSPECTION METHODOLOGY,
- Page 247 and 248: RISK-BASED INSPECTION METHODOLOGY,
- Page 249 and 250: RISK-BASED INSPECTION METHODOLOGY,
- Page 251 and 252: RISK-BASED INSPECTION METHODOLOGY,
- Page 253 and 254: RISK-BASED INSPECTION METHODOLOGY,
- Page 255 and 256: RISK-BASED INSPECTION METHODOLOGY,
- Page 257: RISK-BASED INSPECTION METHODOLOGY,
- Page 261 and 262: RISK-BASED INSPECTION METHODOLOGY,
- Page 263 and 264: RISK-BASED INSPECTION METHODOLOGY,
- Page 265 and 266: RISK-BASED INSPECTION METHODOLOGY,
- Page 267 and 268: RISK-BASED INSPECTION METHODOLOGY,
- Page 269 and 270: RISK-BASED INSPECTION METHODOLOGY,
- Page 271 and 272: RISK-BASED INSPECTION METHODOLOGY,
- Page 273 and 274: RISK-BASED INSPECTION METHODOLOGY,
- Page 275 and 276: RISK-BASED INSPECTION METHODOLOGY,
- Page 277 and 278: RISK-BASED INSPECTION METHODOLOGY,
- Page 279 and 280: RISK-BASED INSPECTION METHODOLOGY,
- Page 281 and 282: RISK-BASED INSPECTION METHODOLOGY,
- Page 283 and 284: RISK-BASED INSPECTION METHODOLOGY,
- Page 285 and 286: RISK-BASED INSPECTION METHODOLOGY,
- Page 287 and 288: RISK-BASED INSPECTION METHODOLOGY,
- Page 289 and 290: RISK-BASED INSPECTION METHODOLOGY,
- Page 291 and 292: RISK-BASED INSPECTION METHODOLOGY,
- Page 293 and 294: RISK-BASED INSPECTION METHODOLOGY,
- Page 295 and 296: RISK-BASED INSPECTION METHODOLOGY,
- Page 297 and 298: RISK-BASED INSPECTION METHODOLOGY,
- Page 299 and 300: RISK-BASED INSPECTION METHODOLOGY,
- Page 301 and 302: RISK-BASED INSPECTION METHODOLOGY,
- Page 303 and 304: RISK-BASED INSPECTION METHODOLOGY,
- Page 305 and 306: RISK-BASED INSPECTION METHODOLOGY,
- Page 307 and 308: RISK-BASED INSPECTION METHODOLOGY,
RISK-BASED INSPECTION METHODOLOGY, PART 2, ANNEX 2.B—DETERMINATION OF CORROSION RATES 2.B-29
Table 2.B.3.9M—High Temperature Sulfidic and Naphthenic Acid Corrosion—Estimated Corrosion
Rates for 316 SS with < 2.5 % Mo (mm/y)
Sulfur
(wt%)
TAN
(mg/g)
Temperature (°C)
≤232 260 288 315 343 371 399 >399
0.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03
0.2
3.0 0.03 0.03 0.03 0.03 0.03 0.05 0.05 0.05
4.0 0.03 0.03 0.03 0.05 0.10 0.13 0.18 0.25
0.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03
0.4
3.0 0.03 0.03 0.03 0.03 0.05 0.05 0.05 0.05
4.0 0.03 0.03 0.05 0.08 0.10 0.13 0.18 0.25
0.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03
0.8
3.0 0.03 0.03 0.03 0.03 0.05 0.05 0.05 0.08
4.0 0.03 0.03 0.05 0.08 0.13 0.13 0.18 0.25
0.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03
1.5
3.0 0.03 0.03 0.03 0.03 0.08 0.08 0.08 0.10
4.0 0.03 0.03 0.08 0.13 0.13 0.13 0.18 0.25
0.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.03
2.5
3.0 0.03 0.03 0.03 0.05 0.08 0.08 0.10 0.13
4.0 0.03 0.03 0.08 0.13 0.13 0.15 0.20 0.25
0.2 0.03 0.03 0.03 0.03 0.03 0.03 0.03 0.05
3.0
3.0 0.03 0.03 0.03 0.05 0.10 0.13 0.13 0.15
4.0 0.03 0.05 0.08 0.13 0.13 0.15 0.20 0.25
NOTE
Includes stainless steels with < 2.5 % Mo, e.g. 316, 316L, 316H, etc.