Understanding API ICP653 Reading 15-Worksheet-11a
Q11.What pipe fillet weld test positions are not to be rotated during welding? (a) 2F-3F-4F-5F (b) 1 F-3F-5F (c) 2F-4F-5F ANS: a Q12. What pipe fillet weld test positions are allowed to be rotated during welding? (a) 1F-2F-2FR (b) 1F-2FR-3F (c) 1F-2FR ANS: Charlie Chong/ Fion Zhang
Q13. Procedure and performance macro-examination specimens are etched to give clear definition of: · (a) weld metal and heat affected zone. (b) inclusions and porosity. (c) root of the weld. ANS: a Q14. Under what conditions are tension tests considered acceptable if the specimen breaks in the base metal outside the weld or fusion line? (a) Lf there are no open defects exceeding 1/16" measured In any direction. (b) If the strength is not more than 5% below the specified minimum tensile strength of the base metal. (c) Lf there are no open defects exceeding 1/8” in the bond line. ANS: a Charlie Chong/ Fion Zhang
- Page 1 and 2: Charlie Chong/ Fion Zhang
- Page 3 and 4: Expert at Works Charlie Chong/ Fion
- Page 5 and 6: Expert at Works Charlie Chong/ Fion
- Page 7 and 8: Charlie Chong/ Fion Zhang Fion Zhan
- Page 9 and 10: The Magical Book of Tank Inspection
- Page 11 and 12: API 653 Exam Administration -- Publ
- Page 13 and 14: • API Recommended Practice 575, I
- Page 15 and 16: Charlie Chong/ Fion Zhang
- Page 17 and 18: ASME SECTION IX EXERCISES Charlie C
- Page 19 and 20: TASK# 1 Read the following paragrap
- Page 21 and 22: Q5. Where are notch-toughness requi
- Page 23: Q9. How is the minimum specimen cur
- Page 27 and 28: Charlie Chong/ Fion Zhang #2
- Page 29 and 30: QW-191.1 Radiographic Examination Q
- Page 31 and 32: Q3. When may longitudinal-bend test
- Page 33 and 34: QW-100.3 Welding Procedure Specific
- Page 35 and 36: Q8. What are the test orientations
- Page 37 and 38: Task#2 Ref Para. 1. A QW-10()3 2. B
- Page 39 and 40: Reading: General Requirements QW-10
- Page 41 and 42: Q5. What constitutes a "set" of red
- Page 43 and 44: Q7. The WPS must list ___ variables
- Page 45 and 46: Task#3 Ref Para 1. A QW-484 2. C QW
- Page 47 and 48: Reading: Procedure Qualifications Q
- Page 49 and 50: Q5. The qualification of the ___is
- Page 51 and 52: QW-200.4 (b) For GTAW, SMAW, GMAW,
- Page 53 and 54: Charlie Chong/ Fion Zhang #5
- Page 55 and 56: QW-200.4 Combination of Welding Pro
- Page 57 and 58: Discussion: GTAW PQR variables: T=1
- Page 59 and 60: Q5. What limitation is invoked when
- Page 61 and 62: Q9: An organization's operational c
- Page 63 and 64: Q12. The ____ is a true record of t
- Page 65 and 66: Charlie Chong/ Fion Zhang #6
- Page 67 and 68: Reading: Performance Qualifications
- Page 69 and 70: Q5. How are the thickness limits de
- Page 71 and 72: Q9. What welding positions on pipe
- Page 73 and 74: QW-304 Welders Except for the speci
Q13. Procedure and performance macro-examination specimens are etched<br />
to give clear definition of: ·<br />
(a) weld metal and heat affected zone.<br />
(b) inclusions and porosity.<br />
(c) root of the weld.<br />
ANS: a<br />
Q14. Under what conditions are tension tests considered acceptable if the<br />
specimen breaks in the base metal outside the weld or fusion line?<br />
(a) Lf there are no open defects exceeding 1/16" measured In any direction.<br />
(b) If the strength is not more than 5% below the specified minimum tensile<br />
strength of the base metal.<br />
(c) Lf there are no open defects exceeding 1/8” in the bond line.<br />
ANS: a<br />
Charlie Chong/ Fion Zhang