FLUXES, STRIPS & WIRES

FLUXES, STRIPS & WIRESFor ELECTROSLAG and SUBMERGED ARC WELD OVERLAYDoc FLUXES, STRIPS & WIRES•S•2011•EN

›Strip feed & regulation›Strip feed & regulationSTRIP CLADDING PROCESS1I SUBMERGED ARC STRIP CLADDING I SAW‹ Direction of cladding› High deposition ratesFlux feed hopper ›‹ Flux feed hopper› High quality weld metal› Easy slag removal± 30 mm stick-out ›Solified slag›Liquid slag›‹ ± 5 mm‹ ± 5 mm‹ 1 > 1,5 mmBase metal ›2I ELECTROSLAG STRIP CLADDING I ESW› Lower penetrationFlux feed hopper ›‹ Direction of cladding› Lower dilution (down to 7%)› High current density resultingto higher deposition rate (up to 50kg/h)› Open weld pool› Special high speed fluxes (up to 45cm/min)± 30 mm stick-out ›Base metal ›Liquid slag›Solidified slag›‹ ± 5 mm‹ ± 5 mm‹ 0,3 > 0,4 mm› High deposition rate (up to 1,2m 2 /h)› Perfect overlap and very flat bead surfacewith magnetic steering› Low flux consumtionI Both Electroslag and submerged arc strip cladding processesoffer a very wide range of overlaying possibilities with many typesof alloys, which are presented to you in the following pages, eachof them being clearly represented by a colour ( ).We tried to be as much complete as possible.I Nevertheless, please always keep in mind that the possibilities are notlimited to the alloys listed in this catalogue and that we can offer you newsolutions adapted to your specific needs, such as the already long list ofcustomized products we propose for serveral areas(“P” fluxes for pipes, “Q5” products for the nuclear field, etc.).

CHARACTERISTICS1I DEPOSITION RATESI DEPOSITION RATE0 2 4 6 8 10 12 14 16 18 20 22 24 26 28 30 32 34 36 38 40 42 44 46 48 50 52Manual Metal ArcSubmerged Arc SinglewireSubmerged Arc Double WireFlux Cored Wire Open ArcPlasma Transfered Arc PowderPlasma MigMigSUBMERGED ARC - Strip 30mm [SAW]SUBMERGED ARC - Strip 60mm [SAW]SUBMERGED ARC - Strip 90mm [SAW]SUBMERGED ARC - Strip 120mm [SAW]ELECTROSLAG - Strip 30mm [ESW]ELECTROSLAG - Strip 60mm [ESW]ELECTROSLAG - Strip 90mm [ESW]ELECTROSLAG - Strip 120mm [SAW]kg/hourI DEPOSITION RATE I WELDING CURRENT [kg/h]I DEPOSITION RATE I WELDING SPEED [m 2 /h]DEPOSITION RATE [kg/hour]DEPOSITION RATE IN kg/h as a function of the welding current and the strip width6050120mm4090mm302060mm1030mm0200 700 1200 1700 2200 2700WELDING CURRENT [A]EXECUTION TIME [h]700600EXECUTION TIME to cover 100m 2 as a function of the welding speedand the number of layers required [60x0,5mm strip]500Two layers standard speed400300Two layers high speed200100One single layer standard speedOne single layer high speed010 15 20 25 30 35 40WELDING SPEED [cm/min]I ESW STRIP CLADDING I WELDING CURRENTStrip width Average current Cable section Bead width Beach Thickness*15 mm (0,59 inch) 350 A 1 x 95 mm 2 18-19 mm (0,7-0,74 inch) 3-5 mm (0,12-0,19 inch)20 mm (0,78 inch) 400 A 1 x 95 mm 2 23-24 mm (0,9-0,94 inch) 3-5 mm (0,12-0,19 inch)30 mm (1,18 inch) 600 A 2 x 95 mm 2 32-37 mm (1,26-1,45 inch) 3-5 mm (0,12-0,19 inch)60 mm (2,36 inch) 1200 A 4 x 95 mm 2 63-68 mm (2,48-2,68 inch) 3-5 mm (0,12-0,19 inch)90 mm (3,54 inch) 1800 A 5 x 95 mm 2 93-99 mm (3,66-3,90 inch) 3-5 mm (0,12-0,19 inch)120 mm (4,72 inch) 2400 A 5 x 120 mm 2 124-128 mm (4,88-5,04 inch) 3-5 mm (0,12-0,19 inch)* On request according to specifications and application2I COMPARISON: SAW - ESW STRIP CLADDINGI SAWI ESWPROCESS: SAW ESWELECTRIC ARC YES NOMAGNETIC STEERING DEVICE NO YESDILUTION 18% 7%DEPOSITION RATE 14kg/h (30,9 lbs/h) 23 kg (50,7 lbs/h)C 1 ste LAYER on 0,18C STEEL 0,045 0,034 I 5

Chemical analysis (typical) (weight -%)C Mn Si Cr Ni Mo Cu N Nb Fe CoOtherelements0,025 0,2 0,01 bal.0,33 1,1 0,4 6,8 0,4 1,7 bal. 1,7 W0,025 0,4 0,4 12,7 bal.0,33 0,4 0,4 13,6 bal.0,045 0,4 0,3 16,2 0,038 bal.0,015 0,4 0,3 16,4 0,015 bal.0,013 1,7 0,4 20,3 10,4 0,1 0,04 bal.0,012 1,8 0,4 23,7 13,3 0,1 0,048 bal.0,010 1,8 0,3 21,2 11,3 0,1 0,035 bal.0,014 1,7 0,4 18,3 12,6 2,9 0,045 bal.0,016 1,5 0,4 18,8 13,6 3,5 0,045 bal.0,014 1,7 0,3 20,3 14,2 2,9 0,033 bal.0,017 2,1 0,4 23,7 12,5 0,2 0,05 0,7 bal.0,016 1,7 0,4 19,7 10,5 0,1 0,046 0,5 bal.0,016 1,8 0,3 21,4 11,3 0,036 0,7 bal.0,025 0,4 0,4 12,7 bal.0,33 0,4 0,4 13,6 bal.0,045 0,4 0,3 16,2 0,038 bal.0,015 0,4 0,3 16,4 0,015 bal.0,012 4,5 0,2 25,1 22 2,2 0,13 bal.0,022 1,4 0,3 22,5 5,5 3,2 0,16 bal.0,012 1,6 0,3 19,9 24,3 4,3 1,5 0,05 bal.0,013 0,5 0,4 20 17,8 6 0,6 0,208 bal.0,09 4,4 0,4 21 10 0,04 bal.0,17 7,3 0,2 31,8 27 bal.0,01 0,8 0,3 22,5 bal. 3,1 2,4 30,5 0,75Ti0,015 0,1 0,1 22 bal. 9 3,6 0,3 0,23Ti0,015 3,2 0,2 20,6 bal. 2,7 0,3 0,35Ti0,02 3,5 0,2 bal. 29,4 0,3 2,3Ti0,023 0,3 0,1 bal. 0,1 3,9Ti0,017 2,8 0,2 30,5 bal. 0,1 1,8 8,8 0,35Ti0,005 0,2 0,03 21,4 bal. 13,5 2,4 2,8W0,005 0,2 0,04 22,7 bal. 15,5 0,70,005 0,5 0,03 16 bal. 15,8 0,1 5,5 3,5W0,006 0,1 0,03 15,5 bal. 15 0,5 0,35Ti0,025 3,2 0,2 20,6 bal. 2,7 1 0,3 Ti0,03 0,2 0,02 bal. 27,8 0,11,1 0,6 0,1 31,5 2,1 0,8 bal. 5 W0,25 0,4 0,5 27,2 3,3 5,5 bal.0,025 0,8 0,1 30,7 bal. 0,7 0,45 Ti6 I 7

PRODUCTS2I WELDING FLUXES:RECORDPRODUCTS RECORDWELDING FluxesProcess STANDARDS EN 760WELDING FluxesProcess STANDARDS EN 760RECORDRECORDRecord 13 BLFT SAW SA AB 2 Record EST 310MM-SP ESW (E) SA FB 2 Cr Ni MoRecord 8B308T2 Q5 SAW SA AB 2 Cr Record EST 316-1 ESW (E) SA FB 2 Cr Ni MoRecord 9V308T1 Q5 SAW SA CS 2 Cr Record EST 317-1 ESW (E) SA FB 2 Cr Ni MoRecord CrMo 15TW SAW SA AB 3 Cr Mo Record EST 320 ESW (E) SA FB 2 Cr Ni Mo CuRecord CrMo 21LC-TW SAW SA CS 3 C Cr Mo Record EST 347-1 ESW (E) SA FB 2 Cr NiRecord CrMo 21TW SAW SA CS 3 C Cr Mo Record EST 347-1 HS ESW (E) SA FB 2 Cr Ni NbRecord CrMo25TW SAW SA AB 3 Cr Mo Record EST 385-1 ESW (E) SA FB 2 Cr Ni Mo CuRecord CuAlW SAW SA AB 2 Record EST 400 ESW (E) SA FB 2 CuRecord CuNi 30 T SAW SA AB 2 Record EST 423 ESW (E) SA FB 3 MoRecord CuNiW SAW SA AB 2 Record EST 426 ESW (E) SA FB 3Record EST 115P ESW (E) SA FB 2 Record EST 4462-1 ESW (E) SA FB 2 Cr Ni MoRecord EST 122 ESW (E) SA FB 2 Record EST 452 ESW (E) SA FB 3 Ni MoRecord EST 126 ESW (E) SA FB 2 Record EST 453 ESW (E) SA FB 3 Ni MoRecord EST 129 ESW (E) SA FB 2 Record EST 625-1 ESW (E) SA FB 2 Cr Mo NbRecord EST 130 ESW (E) SA FB 2 Nb Record EST 690 ESW (E) SA FB 2 Cr NbRecord EST 136 ESW (E) SA FB 2 Record EST 743 ESW (E) SA FB 3 Ni Mo Nb V CRecord EST 136Mo ESW (E) SA FB 2 Mo Record EST 904Mo-1 ESW (E) SA FB 2 Cr Ni Mo CuRecord EST 138 ESW (E) SA FB 2 Cr Ni Mo Record IN SAW SA AB 2 CrRecord EST 200 ESW (E) SA FB 2 Record INC SAW SA FB 2 Ni CRecord EST 201 ESW (E) SA FB 2 Record IND 24 SAW SA FB 2Record EST 201-B ESW (E) SA FB 2 Record IND 27 SAW SA FB 2 CrRecord EST 225P ESW (E) SA FB 2 Record IND 45 SAW SA AB 2Record EST 229 ESW (E) SA FB 2 Record INT 101 SAW SA AB 2 CrRecord EST 236 ESW (E) SA FB 2 Record INT 101 Mo SAW SA AB 2 Cr MoRecord EST 236 ESW (E) SA FB 2 Record INT 102 SAW SA AB 2Record EST 237 ESW (E) SA FB 2 Cr Record INT 109 SAW SA CS 2Record EST 2584 ESW (E) SA FB 2 Cr Ni Mo Record INT 110 SAW SA CS 2 Cr Ni MoRecord EST 259 ESW (E) SA FB 2 Record NFT 690 SAW SA AF 2Record EST 307 ESW (E) SA FB 3 Cr Mn Record NFT201 SAW SA AB 2Record EST 308-1 ESW (E) SA FB 2 Cr Ni Record NiCr3T SAW SA AB 2 Cr NbRecord EST 310MM ESW (E) SA FB 2 Cr Ni Mo Record NiCrT SAW SA AB 2

WELDING FluxesProcess STANDARDS EN 760RECORDRecord NiCrW SAW SA FB 2Record NiCuT SAW SA CS 2Record NiCuW SAW SA CS 2Record NiMo 15T SAW SA AB 3 Ni MoRecord NiT SAW SA AB 2Record R 250 SAW SA MS 3 Cr MoRecord R 400S SAW SA MS 3 C Cr MoRecord RT 146 SAW SA AB 1Record RT 152 SAW SA CS 3 Ni MoRecord RT 155 SAW SA CS 3Record RT 157 SAW SA CS 3 C Cr Ni Mo Nb VRecord RT 159 SAW SA CS 3Record RT 161 SAW SA CS 3 Ni MoRecord RT 162 SAW SA CS 3 Cr Ni MoRecord RT 168 SAW SA CS 3 Ni MoRecord RT 177 SAW SA CS 3 C Cr Ni Mo Nb VRecord RT 179 SAW SA CS 3 CrRecord RT 184 SAW SA CS 3 Ni MoRecord RT 250 SAW SA MS 3 Cr MoRecord RT 350 SAW SA AB 3 Cr MoRecord RT 356 SAW SA CS 3 CrRecord RT 400 D SAW SA AB 3 C Cr MoRecord RT 500 SAW SA CS 3 Cr Ni CRecord RT 505 SAW SA CS 3 Cr Ni Mo VRecord RT 600 SAW SA AB 3 C Cr MoRecord RT 742 SAW SA CS 3 Ni Mo Nb VRecord S Mo TW SAW SA AB 3 MoRecord S46T SAW SA AB 1Record SA SAW SA FB 3Record SK SAW SA FB 3Record SO SAW SA FB 1578 I 9

DEPOSIT TYPESDEPOSIT TYPES LOW ALLOY & MARTENSITIC1I Low alloy & martensitic IA Rebuilding & HardfacingType ofdeposited alloyUnalloyed steel0,5Mo1Ni - 0,5Mo1,5Cr - 0,5Mo1,5Cr - 2Ni - 0,5Mo2,0Cr - 1,0 Mo2Cr - 0,5 Mo3Cr - 0,5 Mo5Cr - 0,9MoWeldingprocessSAWSAWSAWSAWSAWSAWSAWSAWSAW0,15C - 6Cr - 1Mo SAW0,35C - 6Cr - 3Mo SAW0,4C - 6Cr - 0,7Mo SAW258(C-Cr-Mo 50HRc)258 NiMoAll given values are typicalSAWESWLayer1st+2nd L:strip2nd L:deposit1st+2nd L:strip2nd L:deposit1st+2nd L:strip2 nd L: deposit1st+2nd L:strip2nd L:deposit1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd+3rd+4th+5th L:strip5th L:deposit1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd+3rd L:strip3rd L:deposit1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit1st+2nd+3rd+4th L:strip3rd L:deposit4th L:deposit1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd+3rd L:strip2nd L:deposit3rd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st+2nd+3rd L:strip2nd L:deposit3rd L:depositType of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N NbSoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape ASoudotape 258Soudotape 258Soudotape 258Soudotape 258Soudotape 258Soudotape 258Soudotape 258Soudotape 258Soudotape 258++++++++++++Record S 46 TRecord RT 1460,0250,0550,0250,0550,0250,0420,0250,1160,0250,0600,0360,0250,2400,2600,2600,0250,1000,0900,0900,21,00,21,00,21,00,20,70,20,40,50,20,50,30,30,20,30,20,10,010,50,010,50,010,60,010,50,010,30,30,010,50,50,50,010,40,40,4Record SMoTW 0,6Record NiMo15T 0,9 0,5Record CrMo15TWRecord CrMo15TWRecord RT 505Record RT 505Record RT 505Record CrMo21TWRecord CrMo21TWRecord CrMo21TW1,31,31,11,41,41,72,22,31,62,02,10,60,60,40,50,60,70,91,00,025 0,2 0,01+ Record CrMo21 LC TW 0,060 0,1 0,3 2,4 1,0+++Record CrMo25TWRecord CrMo25TWRecord CrMo25TW0,0250,1400,1100,0800,0250,0800,0250,0700,0800,0250,1200,1200,0250,3000,3200,3400,0250,2900,3300,3400,3300,2500,2500,3300,2500,2500,3300,2500,2500,20,60,70,60,20,70,20,30,30,20,30,30,20,50,30,30,20,60,40,31,11,01,01,11,01,01,10,90,90,010,40,50,50,010,70,010,30,30,010,40,40,010,40,30,30,010,70,80,90,40,50,50,40,50,60,41,00,91,41,71,9+ Record RT 250 3,0 0,4++++++++++++++++Record RT 350Record RT 350Record RT 400 DRecord RT 400 DRecord RT 500Record RT 500Record RT 500Record RT 600Record RT 600Record RT 600Record RT 159Record RT 159Record EST 122Record EST 122Record RT 157Record RT 1574,65,05,55,84,55,66,03,44,65,36,86,46,66,85,46,46,86,46,52,22,83,00,40,30,30,40,20,30,41,91,90,50,60,60,80,90,90,90,50,60,71,71,31,61,71,31,51,72,22,20,30,3

Welding parameters(60 x 0,5 mm)LayerthicknessDeposition rateFe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/hbal.bal. 150HB 1150 28 15 5,9 4,4 0,17 22,0 48,6 0,63 971bal.bal. 150HB 1150 28 15 5,9 4,4 0,17 22,0 48,6 0,63 971bal.bal. 900 26 18 7,1 3,0 0,12 17,3 38,0 0,72 1114bal.bal. 210HB 1100 25 13 5,1 4,2 0,17 21,1 46,5 0,63 973bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.0,09V0,110V0,120V240HB235HB285HB320HB340HB260HB275HB275HB80080010001000100065065065024242828282828281717151515131313bal.bal. 230HB 900 28 13 5,1 4,3 0,17 17,3 38 0,5 777bal.bal.bal.bal.240HB240HB240HB6506506502828281313136,76,75,95,95,9bal.bal. 290HB 1275 24 15 5,9 4,4 0,17 24,4 53,9 0,69 1076bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.1,7W1,55W1,6W1,7W1,35W1,55W1,7W0,23V, 1,55W0,23V, 1,55W325HB325HB40HRc40HRc45 HRc45 HRc50 HRc45HRc50HRc55HRc45HRc50HRc45HRc45HRc45HRc50HRc900900120012001000100010009509509507507501250125090090028282828282828272727282824242626131321211515151717171212161613135,15,15,15,15,15,15,15,18,38,35,95,95,96,76,76,74,74,76,36,35,15,13,53,543,83,84444443,83,83,1343,83,84443,23,254,84,34,30,140,140,160,150,150,160,160,160,160,160,160,150,150,120,120,160,150,150,160,160,160,130,130,200,190,170,1715,315,319,219,219,212,512,512,512,512,512,517,317,323,023,019,219,219,218,218,218,214,414,424,024,017,317,333,833,842,342,342,327,527,527,527,527,527,538,038,050,750,742,342,342,340,140,140,131,731,752,852,838,038,00,550,550,600,630,630,390,390,390,390,390,390,570,570,930,960,600,630,630,570,570,570,560,560,600,620,500,5084984992897797760360360360360360387987914371485928977977882882882870870928967777777@DEPOSIT TYPES LOW ALLOY & MARTENSITIC10 I 11

DEPOSIT TYPES1I Low alloy & martensitic IB OverlayingType ofdeposited alloyWeldingprocessLayerType of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N Nb1st+2nd+3rd L:stripSoudotape 4300,0450,40,316,20,1SAW1st L:depositSoudotape 430+Record RT 1550,0830,50,710,84102nd L:depositSoudotape 430+Record RT 1550,0750,40,813,4ESW1st L:strip1st L:depositSoudotape 430Soudotape 430 + Record EST 1220,0450,0550,40,40,30,516,212,90,11st+2nd L:stripSoudotape 4200,3300,40,413,6410HCSAW1st L:depositSoudotape 420+Record RT 3560,2900,70,711,02nd L: depositSoudotape 420+Record RT 3560,3100,60,712,61st+2nd+3rd L:stripSoudotape 4200,330 0,4 0,4 13,61st L:depositSoudotape 420+Record RT 1590,190 0,2 0,7 9,22nd L:depositSoudotape 420+Record RT 1590,2000,20,811,6SAW3rd L:deposit1st+2nd+3rd L:stripSoudotape 420Soudotape 420+Record RT 1590,2000,3300,20,40,80,412,213,64201st L:depositSoudotape 420+Record RT 1550,2200,50,88,82nd L:depositSoudotape 420+Record RT 1550,2300,30,911,93rd L:depositSoudotape 420+Record RT 1550,2300,21,012,91st+2nd L:stripSoudotape 4200,3300,40,413,6ESW1st L:depositSoudotape 420+Record EST 4260,2900,40,410,62nd L:depositSoudotape 420+Record EST 4260,3100,30,212,6DEPOSIT TYPES LOW ALLOY & MARTENSITIC420 Mo ESW14Cr2Ni1MoNbESWSAW1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st L:strip1st L:deposit1st+2nd+3rd L:strip1st L:deposit2nd L:depositSoudotape 420Soudotape 420Soudotape 420Soudotape 420+++Record EST 423Record EST 423Record EST 4230,3300,2700,2800,2900,40,40,20,30,40,20,10,113,610,512,812,91,41,81,8Soudotape 430 (4)0,045 0,4 0,3 16,2 0,1 0,02Soudotape 430 (4) + Record EST 743 0,140 0,2 0,2 13,0 2,2 0,8 0,2Soudotape 430 0,045 0,4 0,3 16,2 0,1 0,02Soudotape 430 + RECORD RT 177 0,180 0,6 0,5 11,1 2,0 1,0 0,3Soudotape 430 + RECORD RT 177 0,170 0,5 0,6 13,3 2,3 1,1 0,33rd L:depositSoudotape 430 + RECORD RT 177 0,175 0,6 0,5 13,8 2,4 1,2 0,3All given values are typical(4) 30mm strip

Welding parameters(60 x 0,5 mm)LayerthicknessDeposition rateFe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/hbal.bal.bal.340HB260HB900900262612124,74,74,13,81,610,15171738,038,00,530,57815879LOW ALLOY & MARTENSITICbal.bal. 280HB 1250 24 20 7,9 4,5 0,18 24 52,8 0,67 1031bal.bal.bal.50HRc55HRc11001100262612144,75,55,04,40,200,1721,121,146,546,50,530,60817928DEPOSIT TYPESbal.bal. 45HRc 750 28 12 4,7 3,8 0,15 14 31,7 0,47 733bal.bal.bal.bal.45HRc 750 28 12 4,7 3,6 0,14 14 31,7 0,50 77450HRc 750 28 12 4,7 3,5 0,14 14 31,7 0,51 79650HRc 900 26 12 4,7 4,1 0,16 17 38,0 0,53 815@bal.50HRc90026124,73,80,151738,00,57879bal.50HRc90026124,73,80,151738,00,57879bal.bal.50HRc140024249,44,40,172759,20,761182bal.50HRc140024249,44,20,172759,20,801238bal.bal.50HRc125024176,74,30,172452,80,701079bal.50HRc125024176,74,20,172452,80,711105bal.50HRc125024176,74,20,172452,80,711105bal.bal. 0,33 V 45HRc 600 26 18 7,1 4,0 0,16 11,5 25,4 0,36 557bal.bal. 0,31 V 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690bal. 0,32 V 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 690bal. 0,33 V 45HRc 650 27 13 5,1 3,5 0,14 12,5 27,5 0,44 69012 I 13

DEPOSIT TYPES1I Low alloy & martensitic IB OverlayingType ofdeposited alloy14Cr2Ni1MoWeldingprocessSAWLayer1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:depositType of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo N NbSoudotape 430Soudotape 430Soudotape 430Soudotape 430Soudotape 430Soudotape 430Soudotape 430Soudotape 430++++++(continuation)Record RT 152Record RT 152Record RT 152Record RT 161Record RT 161Record RT 1610,0450,0680,0370,0330,0450,1420,1490,1370,40,60,50,50,40,60,50,50,30,60,90,90,30,81,01,016,212,213,914,016,211,613,614,30,12,93,83,80,11,11,51,50,020,70,90,90,020,40,50,5ESW1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:depositSoudotape 430Soudotape 430Soudotape 430Soudotape 430+++Record EST 452Record EST 452Record EST 4520,0450,0620,0520,0450,40,50,30,30,30,40,40,416,211,714,114,80,13,03,33,60,020,40,40,5SAW1st+2nd L:strip1st L:deposit2nd L:depositSoudotape 430Soudotape 430Soudotape 430++Record RT 162Record RT 1620,0450,0540,0390,40,60,50,31,01,116,213,116,20,14,05,30,020,70,914Cr4Ni1MoESW1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:depositSoudotape 430Soudotape 430Soudotape 430Soudotape 430+++Record EST 453Record EST 453Record EST 4530,0450,0580,0450,0410,40,30,20,20,30,30,30,316,212,514,314,60,13,34,54,60,020,81,01,113Cr3Ni1MoNbVSAW1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:depositSoudotape 430Soudotape 430Soudotape 430Soudotape 430+++Record RT 742Record RT 742Record RT 7420,0450,0850,0900,0900,40,40,30,30,30,80,90,916,212,013,013,50,12,02,32,40,020,91,01,00,10,10,21st+2nd+3rd L:strip2nd L:deposit3rd L:depositSoudotape 410LSoudotape 410LSoudotape 410L++Record RT 157Record RT 1570,0250,1400,1400,40,30,30,40,80,912,711,812,02,62,51,41,30,30,3DEPOSIT TYPES LOW ALLOY & MARTENSITIC13Cr6Ni2Mo43017 CrSAWSAWESWSAWESW1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd L:strip2nd L:deposit3rd L:deposit1st+2nd L:strip2nd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st+2nd L:strip1st L:deposit2nd L:depositSoudotape 430LSoudotape 430LSoudotape 430LSoudotape 430LSoudotape 430Soudotape 430Soudotape 430+++++Record RT 168Record RT 168Record RT 168Record RT 159Record RT 159Soudotape 430Soudotape 430 + Record EST 122Soudotape 430Soudotape 430Soudotape 430Soudotape 430Soudotape 430Soudotape 430++++Record RT 179Record RT 179Record EST 127Record EST 1270,0150,0750,0270,0170,0450,0600,0530,0450,0670,0450,0600,0710,0450,0550,0500,40,40,30,20,40,30,20,40,40,40,40,50,40,40,40,30,60,70,80,30,60,90,30,50,31,01,10,30,50,616,49,512,112,916,214,115,016,215,316,215,017,316,214,517,20,13,94,75,20,10,10,10,10,10,022,02,52,6All given values are typical

Welding parameters(60 x 0,5 mm)LayerthicknessDeposition rateFe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/hbal.bal.bal.bal.405HB390HB385HB6506506502727271313135,15,15,13,53,53,50,140,140,1412121227,527,527,50,440,440,44690690690LOW ALLOY & MARTENSITICbal.bal.bal.bal.bal.bal.bal.bal.45 HRc45 HRc45 HRc40 HRc40 HRc40 HRc7007007001100110011002727272424241313131616165,15,15,16,36,36,33,83,83,843,53,50,150,150,150,160,140,1413131321212129,629,629,646,546,546,50,440,440,440,660,750,75684684684102111671167DEPOSIT TYPESbal.bal.bal.40 HRc35 HRc650650272713135,15,1330,120,12121227,527,50,520,52805805@bal.bal.bal.bal.40 HRc40 HRc40 HRc9009009002424241616166,36,36,34440,160,160,1617171738,038,038,00,540,540,54835835835bal.bal.bal.bal.0,10V0,13V0,15V40HRc40HRc40HRc8008008002727271313135,15,15,13330,120,120,1215151533,833,833,80,640,640,64990990990bal.bal.bal.0,27W0,27W40HRc45HRc900900262613135,15,13,83,50,150,14171738,038,00,570,62879955bal.bal.bal.bal.35 HRc8008008002626261616166,36,36,32,82,82,80,110,110,1115,315,315,333,833,833,80,680,680,68106110611061bal.bal.bal.21HRC20HRC750750282812124,74,73,93,90,150,1514,414,431,731,70,460,46714714bal.bal. 22HRC 1250 24 17 6,7 4,5 0,18 24,0 52,8 0,67 1031bal.bal.bal.900900242415155,95,94,14,10,160,1617,317,338,038,00,530,53815815bal.bal.bal.12501250242420207,97,94,54,50,180,18242452,852,80,670,671031103114 I 15

DEPOSIT TYPESDEPOSIT TYPES STAINLESS STEEL2I STAINLESS STEELType ofdeposited alloyWeldingprocessLayer307 ESW1st+2nd L:strip1st L:deposit2nd L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st L:stripSAW1st L:deposit2nd L:strip2nd L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit308 L1st L:strip1st L:depositESW2nd L:strip2nd L:deposit1st L:strip1st L:depositESW 1st L:stripSingle layer 1st L:deposit1st L:stripESW 1st L:depositHigh speed 2nd L:strip2nd L:deposit1st L:strip1st L:deposit2nd L:stripSAW2nd L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st L:strip1st L:deposit1st L:strip316 L1st L:depositESW2nd L:strip2nd L:deposit1st L:strip1st L:depositESW 1st L:stripSingle layer 1st L:deposit1st L:stripESW 1st L:depositHigh speed 2nd L:strip2nd L:depositAll given values are typical*Ferrite measurement with Fischer Ferritescope according to AWS A4.2Type of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo NSoudotape 308 L 0,013 1,7 0,4 20,3 10,4Soudotape 308 L + Record EST 307 0,079 4,9 0,5 17,7 8,8Soudotape 308 L + Record EST 307 0,071 5,3 0,6 18,6 9,2Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record INT 101 0,037 1,6 0,8 19,7 10,7Soudotape 308 L0,013 1,7 0,4 20,3 10,4 0,1 0,040Soudotape 308 L + Record INT 101 0,022 1,6 0,8 19,7 10,2Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record INT 109 0,045 0,9 0,8 19,3 10,6Soudotape 308 L0,013 1,7 0,4 20,3 10,4 0,1 0,040Soudotape 308 L + Record INT 109 0,030 1,0 0,8 19,5 10,2Soudotape 309 L Q50,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L Q5 + Record 9V308T1 Q5 0,053 1,5 0,7 18,0 9,5Soudotape 308 L Q50,013 1,7 0,4 20,3 10,4 0,1 0,040Soudotape 308 L Q5 + Record 8B308T2 Q5 0,030 1,5 0,9 19,3 9,9Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309L + Record EST 122 0,035 1,3 0,6 19,2 10,6Soudotape 308 L0,013 1,7 0,4 20,3 10,4 0,1 0,040Soudotape 308 L + Record EST 122 0,020 1,4 0,6 19,3 10,2Soudotape 22.11 L0,010 1,8 0,3 21,2 11,3 0,1 0,035Soudotape 22.11 L + Record EST 122 0,029 1,1 0,5 18,5 9,70,028Soudotape 308 L0,013 1,7 0,4 20,3 10,4 0,1 0,040Soudotape 308 L + Record EST 308-1 0,024 1,3 0,4 19,8 10,0Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record EST 136 0,050 1,5 0,5 18,4 10,2Soudotape 308 L0,013 1,7 0,4 20,3 10,4 0,1 0,040Soudotape 308 L + Record EST 136 0,025 1,3 0,4 19,2 10,1Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record INT 101 0,040 1,6 0,9 19,8 11,0Soudotape 316 L0,014 1,7 0,4 18,3 12,6 2,9 0,045Soudotape 316 L + Record INT 101 0,025 1,5 0,5 18,3 12,2 2,4Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record INT 109 0,058 0,8 0,8 18,3 9,6 0,1Soudotape 316 L0,014 1,7 0,4 18,3 12,6 2,9 0,045Soudotape 316 L + Record INT 109 0,029 0,7 0,9 18,6 11,7 2,0Soudotape 21.13.3 L0,014 1,7 0,3 20,3 14,2 2,9 0,033Soudotape 21.13.3 L + Record EST 115P 0,030 1,4 0,4 18,5 12,4 2,5Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record EST 122 0,046 1,4 0,5 20,6 10,8 0,2Soudotape 316 L0,014 1,7 0,4 18,3 12,6 2,9 0,045Soudotape 316 L + Record EST 122 0,021 1,5 0,6 18,8 12,2 2,4 0,046Soudotape 21.13.3 L0,014 1,7 0,3 20,3 14,2 2,9 0,033Soudotape 21.13.3 L + Record EST 122 0,025 1,3 0,4 18,2 12,6 2,6Soudotape 316 L0,014 1,7 0,4 18,3 12,6 2,9 0,045Soudotape 316 L + Record EST 316-1 0,020 1,2 0,3 19,4 12,8 2,6 0,058Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record EST 136 0,050 1,5 0,5 18,4 10,2Soudotape 316 L0,014 1,7 0,4 18,3 12,6 2,9 0,045Soudotape 316 L + Record EST 136 0,025 1,4 0,4 18,2 12,0 2,3 0,046

Welding parameters(60 x 0,5 mm)Layer thicknessDeposition rateNb Fe FN* A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/hbal.bal. 1250 24 17 6,7 4,5 0,18 24 52,8 0,67 1031bal. 1250 24 17 6,7 4,5 0,18 24 52,8 0,67 1031bal.bal. 6 750 27 12 4,7 4,2 0,17 14,4 31,7 0,43 663bal.bal. 7 750 27 12 4,7 4,1 0,16 14,4 31,7 0,44 679bal.bal. 4 900 28 12 4,7 4,5 0,18 17,3 38,0 0,48 743bal.bal. 6 900 28 12 4,7 4,2 0,17 17,3 38,0 0,51 796bal.bal. 2,4 750 26 14 5,5 4,1 0,16 14,4 31,7 0,44 679bal.bal. 8 750 26 12 4,7 3,9 0,15 14,4 31,7 0,46 714bal.bal. 6 1250 24 16 6,3 4,9 0,19 24,0 52,8 0,61 947bal.bal. 8 1250 24 16 6,3 4,5 0,18 24,0 52,8 0,67 1031bal.bal. 5 1250 24 15 5,9 5 0,20 24,0 52,8 0,60 928bal.bal. 7 1250 24 18 7,1 4 0,16 24,0 52,8 0,75 1160bal.bal. 2 1450 24 35 13,8 3,1 0,12 27,8 61,3 1,12 1737bal.bal. 6 1450 24 35 13,8 3 0,12 27,8 61,3 1,16 1795bal.bal. 4 750 26 14 5,5 4,2 0,17 14,4 31,7 0,43 663bal.bal. 7 750 26 14 5,5 3,7 0,15 14,4 31,7 0,49 753bal.bal. 2 750 28 13 5,1 3,5 0,14 14,4 31,7 0,51 796bal.bal. 5 750 28 13 5,1 3,5 0,14 14,4 31,7 0,51 796bal.bal. 5 1250 24 16 6,3 5 0,20 24,0 52,8 0,60 928bal.bal. 7,5 1250 24 20 7,9 3,6 0,14 24,0 52,8 0,83 1289bal.bal. 7 1250 24 20 7,9 3,6 0,14 24,0 52,8 0,83 1289bal.bal. 6 1250 24 16 6,3 5 0,20 24,0 52,8 0,60 928bal.bal. 6,5 1250 24 16 6,3 4,8 0,19 24,0 52,8 0,62 967bal.bal. 2 1450 24 35 13,8 3,1 0,12 27,8 61,3 1,12 1737bal.bal. 5 1450 24 35 13,8 3 0,12 27,8 61,3 1,16 1795STAINLESS STEELDEPOSIT TYPES16 I 17

DEPOSIT TYPESDEPOSIT TYPES STAINLESS STEEL2I STAINLESS STEELType ofdeposited alloy347317 L318WeldingprocessSAWESWESWESWSingle layerESWHigh speedSAWESWESWSingle layerESWHigh speedESWLayer1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st L:strip1st L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st L:strip1st L:deposit1st L:strip1st L:deposit1st L:strip1st L:deposit1st L:strip1st L:deposit1st L:strip1st L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st L:strip1st L:deposit2nd L:deposit1st L:strip1st L:deposit1st L+2nd L:strip1st L:deposit2nd L:deposit1st L: strip1st L:deposit2nd L:strip2nd L:deposit(continuation)Type of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo NSoudotape 24.12 LNb0,017 2,1 0,4 23,7 12,5 0,2 0,050Soudotape 24.12 LNb + Record INT 109 0,050 0,8 0,8 18,6 10,00,040Soudotape 3470,016 1,7 0,4 19,7 10,5 0,1 0,046Soudotape 347 + Record INT 109 0,035 0,8 0,9 19,2 10,00,040Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record INT 109 0,045 0,9 0,8 18,2 9,7Soudotape 3470,016 1,7 0,4 19,7 10,50,046Soudotape 347 + Record INT 109 0,035 0,8 0,9 19,3 10,0 0,1Soudotape 21.11 LNb0,016 1,8 0,3 21,4 11,3 0,03 0,036Soudotape 21.11 LNb + Record EST 122 0,030 1,4 0,4 19,0 10,1Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record EST 122 0,033 1,2 0,4 19,3 10,60,034Soudotape 3470,016 1,7 0,4 19,7 10,5 0,1 0,046Soudotape 347 + Record EST 122 0,015 1,3 0,4 19,1 10,50,030Soudotape 3470,016 1,7 0,4 19,7 10,5 0,1 0,046Soudotape 347 + Record EST 347-1 0,025 1,2 0,4 18,4 9,7Soudotape 21.11 LNbSoudotape 21.11 LNb + Record EST 129Soudotape 24.12 LNbSoudotape 24.12 LNb + Record EST 129Soudotape 24.12 LNbSoudotape 24.12 LNb + Record EST 136Soudotape 21.11 LNbSoudotape 21.11 LNb + Record 347-1 HSSoudotape 21.13.3 LSoudotape 21.13.3 L + Record INT 101 MoSoudotape 316 LSoudotape 316 L + Record INT 101 MoSoudotape 21.13.3 LSoudotape 21.13.3 L + Record EST 122Soudotape 317 LSoudotape 317 L + Record EST 122Soudotape 316 LSoudotape 316 LSoudotape 316 L++Record EST 317-2Record EST 317-2Soudotape 21.13.3 LSoudotape 21.13.3 L + Record EST 317-1Soudotape 21.13.3 LSoudotape 21.13.3 LSoudotape 21.13.3 LSoudotape 21.11 LNbSoudotape 21.11 LNbSoudotape 316 LSoudotape 316 L++++Record EST 136 MoRecord EST 136 MoRecord EST 130Record EST 1300,0160,0350,0170,0400,0170,0450,0160,0390,0140,0410,0140,0250,0140,0270,0160,0150,0140,0220,0160,0140,0220,0140,0420,0210,0160,0300,0140,0201,81,42,11,32,11,41,81,21,71,41,71,41,71,31,51,21,71,31,31,71,11,71,21,31,81,21,71,20,30,30,40,40,40,40,30,40,30,70,40,70,30,40,40,50,40,40,40,30,20,30,30,30,30,40,40,621,418,423,718,923,719,321,418,320,317,918,318,620,318,318,818,518,317,019,020,318,520,315,318,221,419,018,318,511,39,512,510,412,510,511,39,314,211,512,612,614,212,713,613,412,612,413,914,213,414,211,013,311,310,312,612,20,03 0,0360,0300,2 0,0500,0400,2 0,0500,0400,03 0,0362,92,82,93,12,92,53,53,22,92,93,32,93,22,92,73,30,032,92,40,0330,0450,0470,0330,0310,0450,0450,0330,0350,0330,0300,0330,0310,0370,0360,0450,034ESWSingle layer1st L:strip1st L:depositSoudotape 21.13.3 LSoudotape 21.13.3 L + Record EST 130All given values are typical*Ferrite measurement with Fischer Ferritescope according to AWS A4.20,0140,0301,71,30,30,320,318,014,212,22,92,60,0330,030

Welding parameters(60 x 0,5 mm)Layer thicknessDeposition rateNb Fe FN* A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/h0,70,30,50,40,50,40,70,50,50,40,50,30,70,50,70,50,70,50,70,5bal.bal.bal.bal.46750750282815135,95,13,33,80,130,1514,414,431,731,70,580,50899779bal.bal. 2 750 28 15 5,9 3,3 0,13 14,4 31,7 0,54 844bal.bal. 6 750 28 15 5,9 3,1 0,12 14,4 31,7 0,58 898bal.bal. 7 1250 24 17 6,7 4,8 0,19 24,0 52,8 0,62 967bal.bal.1250 24 17 7 5 0,20 24 52,8 0,60 928bal.bal. 5 1250 24 17 7 5 0,20 24 52,8 0,60 928bal.bal. 6 1250 24 18 7,1 4 0,16 24,0 52,8 0,75 1160bal.bal. 4 1350 24 22 8,7 4,2 0,17 25,9 57,0 0,77 1194bal.bal. 4 1350 24 30 11,8 3,5 0,14 25,9 57,0 0,92 1432bal.bal. 5 1450 24 35 13,8 3,1 0,12 27,8 61,3 1,12 1737bal.bal. 5 1650 24 35 13,8 2,8 0,11 31,6 69,7 1,41 2188bal.bal. 7,3 750 26 11 4,3 4,7 0,19 14,4 31,7 0,38 593bal.bal. 7,1 750 26 12 4,7 4,2 0,17 14,4 31,7 0,43 663bal.bal. 4,3 1250 24 18 7,1 4,3 0,17 24,0 52,8 0,70 1079bal.bal. 6,3 1250 24 18 7,1 4 0,16 24,0 52,8 0,75 1160bal.bal.bal. 4,712501250242418187,17,14,54,20,180,1725,925,957,057,00,770,7711941194bal.bal. 7 1350 24 25 9,8 4 0,16 25,9 57,0 0,81 1253bal.bal.bal.2,66,6140014002424353513,813,83,83,80,150,1526,826,859,259,20,880,8813681368STAINLESS STEELDEPOSIT TYPES0,70,50,3bal.bal.bal.bal.2512501250242417176,76,754,50,200,1824,024,052,852,80,600,6792810310,3bal.bal. 5,8 1250 24 17 6,7 4,7 0,19 24,0 52,8 0,64 98818 I 19

DEPOSIT TYPES3I SPECIAL STAINLESS STEEL (fully austenitic)Type ofdeposited alloy310 MMWeldingprocessSAWESWESWHigh speed28.23.3 L ESWSAWLayer1st+2nd+3rd L:strip1st L:deposit2nd L:deposit3rd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st L:strip1st L:deposit2nd L:strip2nd L:deposit1st+2nd+3rd L:strip2nd L:deposit3rd L:depositType of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo NSoudotape 310 MM0,012 4,5 0,2 25,1 22 2,2 0,13Soudotape 310 MM + Record 13 BLFT 0,040 3,5 0,6 21 19,8 1,9 0,13Soudotape 310 MM + Record 13 BLFT 0,033 3,6 0,6 23 21,3 2,0 0,12Soudotape 310 MM + Record 13 BLFT 0,025 3,7 0,6 24,5 22,2 2,1 0,12Soudotape 310 MM0,012 4,5 0,2 25,1 22 2,2 0,13Soudotape 310 MM + Record EST 122 0,045 3,6 0,4 21,5 20 1,8 0,13Soudotape 310 MM + Record EST 122 0,030 3,8 0,4 24 22,5 2,0 0,15Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record EST 122 0,039 1,3 0,5 18,9 10,7 0,0 0,053Soudotape 310 MM0,012 4,5 0,2 25,1 22 2,2 0,13Soudotape 310 MM + Record EST 310 MM-SP 0,014 2,8 0,3 27,4 22,7 2,7 0,131Soudotape 310 MM0,012 4,5 0,2 25,1 22 2,2 0,13Soudotape 310 MM + Record EST 310 MM 0,045 3,3 0,3 22,3 20,5 2,0 0,11Soudotape 310 MM + Record EST 310 MM 0,029 3,8 0,3 24,3 22,5 2,3 0,12Soudotape 309 L0,012 1,8 0,4 23,7 13,3 0,1 0,048Soudotape 309 L + Record EST 310 MM-SP 0,034 1 0,4 24,4 14,8 1,1 0,053Soudotape 310 MM0,012 4,5 0,2 25,1 22 2,2 0,13Soudotape 310 MM + Record EST 310 MM-SP 0,017 3 0,3 28,1 23,4 2,9 0,096Soudotape 22.6.3 L0,022 1,4 0,3 22,5 5,5 3,2 0,16Soudotape 22.6.3 L + Record INT 110 0,028 0,8 0,9 20,9 5,9 2,8 0,14Soudotape 22.6.3 L + Record INT 110 0,020 0,9 1 21,7 6,6 2,9 0,15DuplexESWSingle layer1st L:strip1st L:depositSoudotape 22.6.3 LSoudotape 22.6.3 L + RECORD EST 4462-10,0220,0331,41,00,30,422,521,85,57,33,22,90,1600,110DEPOSIT TYPES SPECIALSTAINLESS STEELSuper DuplexESWESW254 SMO ESW904 L904 L MoSAWESWESWSingle layerESWSingle layer1st+2nd L:strip1st L:deposit2nd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st+2nd L:strip1st L:deposit2nd L:deposit1st L:strip1st L:deposit1st L:strip1st L:depositAll given values are typical*Ferrite measurement with Fischer Ferritescope according to AWS A4.2Soudotape 22.6.3 LSoudotape 22.6.3 LSoudotape 22.6.3 LSoudotape 22.6.3 LSoudotape 22.6.3 LSoudotape 22.6.3 LSoudotape 254SMoSoudotape 254SMoSoudotape 254SMoSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCuSoudotape 20.25.5 LCu++Record EST 122Record EST 1220,020,050,030,022+ Record EST 2584 0,029+ Record EST 2584 0,0200,013+ Record EST 122 0,024+ Record EST 122 0,0270,012+ Record INT 101 0,05+ Record INT 101 0,03+ 0,012+ Record EST 122 0,030+ Record EST 122 0,0200,012+ Record EST 385-1 0,0150,012+ Record EST 904Mo-1 0,0141,41,041,381,40,80,80,50,40,31,61,61,71,61,41,41,62,51,610,30,410,440,30,30,30,40,50,40,30,70,80,30,40,50,30,10,30,222,518,320,9022,524,926,72018,720,219,916,318,819,917,419,519,919,419,920,25,55,15,305,58,99,817,816,317,124,321,224,324,322,72524,32524,3253,22,312,703,23,94,26,05,35,74,33,74,24,34,14,54,34,44,36,10,160,100,150,160,10,100,2080,1790,1890,050,050,050,05

Welding parameters(60 x 0,5 mm)Layer thicknessDeposition rateFe Others FN* A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/hbal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.556075075075012001200282828242412121218184,74,74,77,17,14,54,14,14,74,50,180,160,160,190,1814,414,414,423,023,031,731,731,750,750,70,40,440,440,610,646196796799489901250 24 18 7,1 4 0,16 24,0 52,8 0,75 11601000 24 16 6,3 4 0,16 19,2 42,3 0,6 928150014502424352413,89,434,50,120,1828,827,863,461,31,20,77185711971000 24 16 6,3 4 0,16 19,2 42,3 0,6 9281000 24 16 6,3 4 0,16 19,2 42,3 0,6 928750750262617176,76,73,43,30,130,1314,414,431,731,70,530,54819844SPECIAL STAINLESS STEELDEPOSIT TYPESbal.bal. 36 1250 24 18 7,1 4,5 0,18 24,0 52,8 0,67 1031bal.bal.bal. 6712501250242420207,97,94,64,80,190,19222248,548,50,600,57927888bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.bal.545712501250242418180,6Cu0,5Cu1250 24 180,5Cu1250 24 181,5 Cu1,20 Cu 750 26 141,40 Cu 750 26 141,5 Cu1,3 Cu 1050 24 181,45 Cu 1050 24 181,5 Cu7,17,1550,200,2024,024,052,852,80,60,69289287,1 5 0,20 24,0 52,8 0,6 9287,1 5 0,20 24,0 52,8 0,6 9285,5 4 0,16 14,4 31,7 0,45 6965,5 3,8 0,15 14,4 31,7 0,47 7337,1 4,2 0,17 20,1 44,4 0,6 9287,1 4 0,16 20,1 44,4 0,63 9751,33 Cu 1250 24 18 7,1 5 0,20 24 52,8 0,6 9281,5 Cu1,30Cu 1250 24 18 7,1 5 0,20 24 52,8 0,6 92820 I 21

DEPOSIT TYPESDEPOSIT TYPES NICKEL ALLOYS4I NICKEL ALLOYSType ofdeposited alloyWeldingprocess20 ESW825ESWESW825 C ESW625600SAWESWESWSingle layerESWHigh speedSAWESWESWHigh speedESWHigh speedAll given values are typical(1) Parameters for welding with 30 x 0,5mm stripType of strip(60 x 0,5 mm)Chemical analyses on a 0,2% C plate(typical) (weight - %)LayerType of fluxSOUDOTAPE + RECORD C Mn Si Cr Ni Mo Nb1st L:strip Soudotape 825 0,010 0,8 0,3 22,5 bal. 3,11st L:deposit Soudotape 825 + Record EST 320 0,020 0,6 0,3 24 bal. 2,81st L:strip Soudotape 825 0,010 0,8 0,3 22,6 bal. 3,21st L:deposit Soudotape 825 + Record EST 138 0,013 0,8 0,7 23,7 bal. 31st L:strip Soudotape 825 0,01 0,8 0,3 22,6 bal. 3,21st L:deposit Soudotape 825 + Record EST 201 0,03 0,8 0,7 18,2 37,20 2,52nd L:deposit Soudotape 825 + Record EST 201 0,02 0,7 0,7 19,7 39,90 2,71st L:strip Soudotape 825 C 0,010 0,8 0,3 22,5 bal. 3,11st L:deposit Soudotape 825 C + Record EST 138 0,020 0,7 0,6 21,1 39,1 2,61st+2nd L:strip Soudotape 625 0,015 0,1 0,1 22 bal. 9 3,61st L:deposit Soudotape 625 + Record NFT 201 0,040 0,9 0,4 18,5 bal. 7,8 2,72nd L:deposit Soudotape 625 + Record NFT 201 0,020 1 0,3 20,5 bal. 8,5 2,91st+2nd+3rd L:strip Soudotape 625 0,015 0,1 0,1 22 bal. 9 3,62nd L:deposit Soudotape 625 + Record NiCrT 0,020 0,1 0,5 20,7 bal. 8,8 3,43rd L:deposit Soudotape 625 + Record NiCrT 0,020 0,1 0,5 21 bal. 8,8 3,51st+2nd+3rd L:strip Soudotape 625 (1) 0,015 0,1 0,1 22 bal. 9 3,61st L:deposit Soudotape 625 + Record NiCr3T 0,048 1 0,4 19,9 bal. 7,8 2,62nd L:deposit Soudotape 625 + Record NiCr3T 0,037 1 0,3 21,9 bal. 8,7 2,83rd L:deposit Soudotape 625 + Record NiCr3T 0,032 1 0,4 21,9 bal. 8,5 2,61st+2nd L:strip Soudotape 625 0,015 0,1 0,1 22 bal. 9 3,61st L:deposit Soudotape 625 + Record EST 201 0,030 0,3 0,4 19,5 bal. 8 2,82nd L:deposit Soudotape 625 + Record EST 201 0,020 0,1 0,3 21,5 bal. 8,8 31st L:strip Soudotape 625 0,015 0,1 0,1 22 bal. 9 3,61st L:deposit Soudotape 625 + Record EST 237 0,030 0,1 0,2 21,3 bal. 8,2 2,81st+2nd L:strip Soudotape 625 (1) 0,015 0,1 0,1 22 bal. 9 3,61st L:deposit Soudotape 625 + Record EST 215 P 0,031 0,3 0,4 19,4 bal. 7,9 2,62nd L:deposit Soudotape 625 + Record EST 215 P 0,025 0,2 0,4 21,3 bal. 8,6 2,91st L:strip Soudotape 625 0,015 0,1 0,1 22 bal. 9 3,61st L:deposit Soudotape 625 + Record EST 625-1 0,025 0,2 0,3 21,5 bal. 9 3,51st+2nd L:strip Soudotape 625 0,015 0,1 0,1 22 bal. 9 3,61st L:deposit Soudotape 625 + Record EST 236 0,035 0,3 0,3 17 bal. 7,8 2,62nd L:deposit Soudotape 625 + Record EST 236 0,025 0,1 0,3 21 bal. 8,7 3,11st+2nd L:strip Soudotape NiCr3 0,015 3,2 0,2 20,6 bal. 2,71st L:deposit Soudotape NiCr3 + Record NFT 201 0,030 3,5 0,3 17,6 bal. 22nd L:deposit Soudotape NiCr3 + Record NFT 201 0,020 3,6 0,3 19,8 bal. 2,21st+2nd+3rd L:strip Soudotape NiCr3 0,015 3,2 0,2 20,6 bal. 2,72nd L:deposit Soudotape NiCr3 + Record NiCrT 0,030 2,7 0,6 18,7 bal. 2,43rd L:deposit Soudotape NiCr3 + Record NiCrT 0,020 2,9 0,6 19,3 bal. 2,51st+2nd+3rd L:strip Soudotape NiCr3 0,015 3,2 0,2 20,6 bal. 2,73rd L:deposit Soudotape NiCr3 + Record NiCr3T 0,020 3,6 0,3 20,6 bal. 2,51st+2nd L:strip Soudotape NiCr3 0,015 3,2 0,2 20,6 bal. 2,71st L:deposit Soudotape NiCr3 + Record EST 201 0,030 2,7 0,2 18,2 bal. 2,22nd L:deposit Soudotape NiCr3 + Record EST 201 0,021 2,8 0,3 19,4 bal. 2,51st+2nd L:strip Soudotape NiCr3 0,015 3,2 0,2 20,6 bal. 2,71st L:deposit Soudotape NiCr3 + Record EST 229 0,043 2,7 0,2 18,8 bal. 2,12nd L:deposit Soudotape NiCr3 + Record EST 229 0,032 2,8 0,1 21,1 bal. 2,41st+2nd L:strip Soudotape NiCr3 0,015 3,2 0,2 20,6 bal. 2,71st L:deposit Soudotape NiCr3 + Record EST 236 0,035 2,5 0,4 16 bal. 22nd L:deposit Soudotape NiCr3 + Record EST 236 0,025 2,8 0,4 19,8 bal. 2,4

Welding parameters(60 x 0,5 mm)LayerthicknessDeposition rateFe Cu Others A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/h30,5 2,4 0,75 Ti33,8 4,5 1000 24 16 6,3 4,8 0,19 19,16 42,3 0,49 75531,1 2 0,81 Ti34 1,1 1000 24 16 6,3 4,8 0,19 19,16 42,3 0,49 75531,1 2,00 0,81 Ti38,8 1150 24 15 4,8 0,19 22 48,6 0,56 86833,8 1,85 1150 24 15 4,3 0,17 22 48,6 0,63 96930,5 2,4 0,75 Ti34,1 1,6 1000 24 16 6,3 4,8 0,19 19,16 42,3 0,49 7550,3 0,02 0,23 Ti13 750 26 11 4,3 4,9 0,19 14,37 31,7 0,36 5553 750 26 11 4,3 4,2 0,17 14,37 31,7 0,42 6470,3 0,02 0,23 Ti3 750 24 11 4,3 4,7 0,19 14,37 31,7 0,37 5781 750 24 11 4,3 4,6 0,18 14,37 31,7 0,38 5910,3 0,02 0,23 Ti14,5 600 27 21 8,3 4 0,16 11,5 24,2 0,35 5437,5 600 27 21 8,3 4 0,16 11,5 24,2 0,35 5435,5 600 27 21 8,3 4 0,16 11,5 24,2 0,35 5430,3 0,02 0,23 Ti10 1100 24 16 6,3 4,2 0,17 21,08 46,5 0,61 9492,5 1100 24 16 6,3 4,2 0,17 21,08 46,5 0,61 9490,3 0,02 0,23 Ti9,4 1450 24 26 10,2 4,3 0,17 27,79 61,3 0,79 12220,3 0,02 0,23 Ti11 550 24 16 6,3 4,3 10 22,0 0,3 4653 550 24 16 6,3 4,3 10 22,0 0,3 4650,3 0,02 0,23 Ti6,8 1250 24 20 7,9 5 0,2 23,95 52,8 0,58 9060,3 0,02 0,23 Ti16 1450 24 35 13,8 3,1 0,12 27,79 61,3 1,09 16954,9 1450 24 35 13,8 3 0,12 27,79 61,3 1,13 17510,3 0,35 Ti11,6 750 26 11 4,3 4,5 0,18 14,37 31,7 0,39 6043 750 26 11 4,3 4,2 0,17 14,37 31,7 0,42 6470,3 0,35 Ti3,8 750 24 11 4,3 4,7 0,19 14,37 31,7 0,37 5781,6 750 24 11 4,3 4,6 0,18 14,37 31,7 0,38 5910,3 0,35 Ti2 1400 28 28 11 4,5 0,18 26,83 59,2 0,73 11270,3 0,35 Ti11,8 1000 24 18 7,1 4 0,16 19,16 42,3 0,58 9063,8 1000 24 18 7,1 3,6 0,14 19,16 42,3 0,65 10060,3 0,35 Ti12,1 1200 24 25 9,8 3,6 0,14 23 50,7 0,78 12084,3 1200 24 25 9,8 3,6 0,14 23 50,7 0,78 12080,3 0,35 Ti19 1450 24 35 13,8 3,1 0,12 27,79 61,3 1,09 16955 1450 24 35 13,8 3 0,12 27,79 61,3 1,13 1751NICKEL ALLOYSDEPOSIT TYPES22 I 23

DEPOSIT TYPESDEPOSIT TYPES NICKEL ALLOYS4I NICKEL ALLOYS (continuation)Type ofdeposited alloy400200690C22C276WeldingprocessSAWESWSAWESWSAWESWESWESW59 ESWB2C4All given values are typicalESWESWLayerType of strip(60 x 0,5 mm)Type of flux2nd L:deposit Soudotape NiTi + Record EST 200 0,023 0,3 0,9 bal.Soudotape3rd L:deposit Soudotape NiTi + Record EST 200 0,021 0,3 0,8 bal.Chemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo Nb1st+2nd L:strip Soudotape NiCu7 0,020 3,5 0,2 bal.1st L:deposit Soudotape NiCu7 + Record NiCuT 0,032 2,9 1,0 bal.2nd L:deposit Soudotape NiCu7 + Record NiCuT 0,018 3,2 1,0 bal.1st+2nd L:strip Soudotape NiCu7 0,020 3,5 0,2 bal.1st L:deposit Soudotape NiCu7 + Record EST 400 0,038 3,0 0,6 bal.2nd L:deposit Soudotape NiCu7 + Record EST 400 0,016 3,3 0,5 bal.1st+2nd+3rd L:strip Soudotape NiTi 0,023 0,3 0,1 bal.1st L:deposit Soudotape NiTi + Record NiT 0,058 1,7 0,5 bal.2nd L:deposit Soudotape NiTi + Record NiT 0,034 1,7 0,7 bal.3rd L:deposit Soudotape NiTi + Record NiT 0,026 1,8 0,8 bal.1st+2nd+3rd L:strip Soudotape NiTi 0,023 0,3 0,1 bal.1st L:deposit Soudotape NiTi + Record EST 200 0,035 0,4 0,9 bal.1st+2nd+3rd L:strip Soudotape 690 0,017 2,8 0,2 30,5 bal. 0,1 1,81st L:deposit Soudotape 690 + Record NFT 690 0,050 2,2 0,5 22,1 bal. 1,52nd L:deposit Soudotape 690 + Record NFT 690 0,038 2,5 0,5 26,1 bal. 1,73rd L:deposit Soudotape 690 + Record NFT 690 0,022 2,6 0,5 28,5 bal. 1,91st+2nd+3rd L:strip Soudotape 690 0,017 2,8 0,2 30,5 bal. 0,1 1,81st L:deposit Soudotape 690 + Record EST 690 0,035 2,2 0,3 26,5 bal. 1,42nd L:deposit Soudotape 690 + Record EST 690 0,025 2,4 0,2 28 bal. 1,53rd L:deposit Soudotape 690 + Record EST 690 0,020 2,3 0,2 29 bal. 1,41st+2nd L:strip Soudotape NiCrMo22 0,005 0,2 0,03 21,4 bal. 13,51st L:deposit Soudotape NiCrMo22 + Record EST 259 0,030 0,3 0,3 19,4 bal. 11,72nd L:deposit Soudotape NiCrMo22 + Record EST 259 0,014 0,2 0,3 21,2 bal. 13,01st L:strip Soudotape NiCrMo59 0,005 0,2 0,04 22,7 bal. 15,51st L:deposit Soudotape NiCrMo59 + Record EST 259 0,019 0,2 0,4 21,4 bal. 14,62nd L:strip Soudotape NiCrMo4 0,005 0,5 0,03 16 bal. 15,82nd L:deposit Soudotape NiCrMo4 + Record EST 259 0,010 0,2 0,3 16,4 bal. 15,41st+2nd L:strip Soudotape NiCrMo59 0,005 0,2 0,04 22,7 bal. 15,51st L:deposit Soudotape NiCrMo59 + Record EST 259 0,019 0,2 0,4 19,5 bal. 14,62nd L:deposit Soudotape NiCrMo59 + Record EST 259 0,010 0,2 0,5 21,7 bal. 15,01st+2nd L:strip Soudotape NiMo7 0,030 0,2 0,02 bal. 27,81st L:deposit Soudotape NiMo7 + Record EST 201-B 0,022 0,4 0,3 bal. 23,92nd L:deposit Soudotape NiMo7 + Record EST 201-B 0,006 0,1 0,3 bal. 27,71st+2nd+3rd L:strip Soudotape NiCrMo7 0,006 0,1 0,03 15,5 bal. 15,01st L:deposit Soudotape NiCrMo7 + Record EST 259 0,027 0,3 0,4 13,3 bal. 14,22nd L:deposit Soudotape NiCrMo7 + Record EST 259 0,013 0,1 0,3 14,8 bal. 14,83rd L:deposit Soudotape NiCrMo7 + Record EST 259 0,010 0,1 0,3 15 bal. 15,2

Welding parameters(60 x 0,5 mm)LayerthicknessDeposition rateFe Cu Others A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/h0,3 29,4 2,3 Ti18,1 25,3 900 26 14 5,5 4,9 0,19 17,25 38 0,43 6657,1 28,1 900 26 14 5,5 4,7 0,19 17,25 38 0,45 6940,3 29,4 2,3 Ti10,9 26,3 1100 26 16 6,3 5 0,2 21,08 46,5 0,51 7972 28,2 1100 26 16 6,3 5 0,2 21,08 46,5 0,51 7970,1 3,9 Ti28,6 1,87 Ti 750 27 12 4,7 4 0,16 14,37 31,7 0,44 67912,1 2,07 Ti 750 27 12 4,7 3,8 0,15 14,37 31,7 0,46 7152,9 2,12 Ti 750 27 12 4,7 3,8 0,15 14,37 31,7 0,46 7150,1 3,9 Ti14,2 2,37 Ti 1600 24 20 7,9 5,5 0,22 30,66 67,6 0,68 10543,7 2,59 Ti 1600 24 20 7,9 5,3 0,21 30,66 67,6 0,71 10941,3 2,68 Ti 1600 24 20 7,9 5,3 0,21 30,66 67,6 0,71 10948,8 0,01 0,35 Ti31,5 750 29 16 6,3 3,5 0,14 14,37 31,7 0,5 77620,2 750 29 16 6,3 3,4 0,13 14,37 31,7 0,52 79912,7 750 29 16 6,3 3,4 0,13 14,37 31,7 0,52 7998,8 0,01 0,35 Ti17 900 24 17 6,7 3,8 0,15 17,25 38 0,55 85812 900 24 17 6,7 3,6 0,14 17,25 38 0,58 90610 900 24 17 6,7 3,6 0,14 17,25 38 0,58 9062,4 0,01 2,8 W13,2 2,7 W 950 24 18 7,1 3,5 0,14 18,2 40,1 0,63 9834,9 2,9 W 950 24 18 7,1 3,2 0,13 18,2 40,1 0,69 10750,79 900 24 18 7,1 3,8 0,15 17,25 38 0,6 9325,5 0,1 3,5 W7,2 2,71 W 900 24 18 7,1 3,2 0,13 17,25 38 0,66 10190,79,0 900 24 18 7,1 3,8 0,15 17,3 38 0,55 8583,3 900 24 18 7,1 3,5 0,12 17,25 38 0,7 10870,111,7 900 25 15 5,9 5,2 0,20 17,25 38 0,4 6272,4 900 25 15 5,9 4,9 0,19 17,25 38 0,43 6650,5 0,35 Ti12,6 900 24 18 7,1 3,5 0,14 17,25 38 0,6 9322,4 900 24 18 7,1 3,5 0,14 17,25 38 0,6 9321,7 900 24 18 7,1 3,5 0,14 17,25 38 0,6 932NICKEL ALLOYSDEPOSIT TYPES24 I 25

DEPOSIT TYPES5I cobalt ALLOYSCOBALT ALLOYSType ofdeposited alloyCobalt alloy 6WeldingprocessESWLayerType of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo Co1st+2nd L:strip Soudotape SCoCr 6 1,1 0,6 0,1 31,5 2,1 0,8 bal.1st L:deposit Soudotape SCoCr 6 + Record EST 126 1 0,4 0,3 28,5 bal.2nd L:deposit Soudotape SCoCr 6 + Record EST 126 1,05 0,5 0,3 29,0 bal.1st+2nd L:strip Soudotape SCoCr 21 0,250 0,4 0,5 27,2 3,3 5,5 bal.Cobalt alloy 21ESW1st L:deposit Soudotape SCoCr 21 + Record EST 126 0,300 0,2 0,4 24,5 1,5 5,3 bal.All given values are typical2nd L:deposit Soudotape SCoCr 21 + Record EST 126 0,250 0,4 0,5 25,7 3 5,3 bal.6I copper alloySType ofdeposited alloyWeldingprocessLayerType of strip(60 x 0,5 mm)Type of fluxChemical analyses on a 0,2% C plate(typical) (weight - %)SOUDOTAPE + RECORD C Mn Si Cr Ni Mo Nb1st L:strip Soudotape NiCu7 0,02 3,5 0,2 bal.COPPER ALLOYS70Cu - 30NiSAW1st L:deposit Soudotape NiCu7 + Record NiCuT 0,04 2,7 1 bal.2nd+3rd L:strip Soudotape CuNi30 0,025 0,8 0,1 30,72nd L:deposit Soudotape CuNi30 + Record CuNi30T 0,03 1 0,4 383rd L:deposit Soudotape CuNi30 + Record CuNi30T 0,02 0,9 0,3 32All given values are typical

Welding parameters(60 x 0,5 mm)LayerthicknessDeposition rateFe Others Hardness A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/h5 WCOBALT ALLOYS6 4,8 W 40 HRc 1000 26 10 3,9 5 0,20 19,2 42,3 0,48 7433 4,5 W 42 HRc 1000 26 10 3,9 4,5 0,18 19,2 42,3 0,53 825COPPER ALLOYS10 30 HRc 1000 26 10 3,9 5 0,20 19,2 42,3 0,48 7433 31 HRc 1000 26 10 3,9 4,5 0,18 19,2 42,3 0,53 825DEPOSIT TYPESWelding parameters(60 x 0,5 mm)LayerthicknessDeposition rateFe Cu Others A V cm/min inch/min mm inch kg/h lbs/h m²/h inch²/h0,3 29,4 2,3 Ti16 24 0,4 900 26 14 5,5 5 0,2 17,3 38 0,39 6010,7 bal. 0,45 Ti5 bal. 0,25 750 28 14 4,7 4 0,16 14,4 31,7 0,4 6262 bal. 0,2 750 28 14 4,7 4 0,16 14,4 31,7 0,4 62626 I 27

STRIP CLADDING APPLICATIONS1I IN PETROCHEMICALS AND CHEMICALS2I IN offshoreI Hydrogenation reactor:Type of strip(60 x 0,5 mm)Type of fluxSoudotape 21.13.3L + Record EST 122I Heat exchanger outlet (courtesy by MWL)Type of strip(30 x 0,5 mm)Type of fluxSoudotape 21.11 LNb + Record EST 122I Pressure vessels (courtesy by Technip):Type of strip(60 x 0,5 mm)Type of fluxSoudotape 24.12 LNb + Record EST 136I High pressure separator:Type of strip(60 x 0,5 mm)Type of fluxSoudotape 825 + Record EST 138I Ball valves:Type of strip(30 x 0,5 mm)Soudotape 625 (ESW)Type of flux+ Record EST 236 (ESW)Record NFT 201 (SAW)I For more information, please consultour catalogue “(Petro)Chemicals”

3I for maintenance and repairI Offshore separator vessel:Type of strip(60 x 0,5 mm)Type of fluxSoudotape 625 + Record EST 625-1I Paper industry: RollsType of strip(90 x 0,5 mm)Type of fluxSoudotape 430 + Record EST 452I Offshore separator vessel:Type of strip(60 x 0,5 mm)Type of fluxSoudotape 316 L + Record EST 316-1I Steelworks: continuous casting rollType of strip(60 x 0,5 mm)Type of fluxSoudotape 430 + Record RT 152I Offshore separator vessel:Type of strip(60 x 0,5 mm)Type of fluxSoudotape Nicu7 + Record EST 400 (ESW)I Forging: punching toolsType of strip(60 x 0,5 mm)Type of fluxSoudotape NiCrMo4 + Record EST 259I Pipe:Type of strip(30 x 0,5 mm)Type of fluxSoudotape 825 + Record EST 138I RailwaysType of strip(30 x 0,5 mm)Type of fluxSoudotape 309 L + Record EST 307I For more information, please consultour catalogue “Offshore”I For more information, please consultour catalogues “Steelworks” and “Forging”28 I 29

STRIP CLADDING APPLICATIONS4I IN NUCLEAR POWER INDUSTRYI Reactor vesselType of strip(90 x 0,5 mm)Type of fluxSoudotape 309 L “Q5” + Record 6/74 “Q5”I Vessel shell ring (courtesy by Areva)Type of stripType of fluxTAPE AWS 308 L + Record 8B308T1 “Q5”I Reactor vesselType of strip(90 x 0,5 mm)Type of fluxTAPE AWS 308 L / 309 L + Record 8B308T1 “Q5”Record 9V308T1 “Q5”5I SOUDOKAY “Q5” NUCLEAR PRODUCTSI All Soudokay products can be specifically produced for an application in thenuclear field and be classified into our socalled “Q5” category.This international designation is an indication for the customer that theproduct has been produced following the nuclear program of our ASMEcertified Quality Insurance manual and is qualified, according to ourQSC380 certificate, for use in the nuclear field.

1CLAD PLATESI STRIP CLADDING OF WELDED JOINTS OF ROLL BONDED CLAD PLATESI When the use of the Strip Cladding Process is not chosen in favour of rollbonded clad plates, this one stays the best solution for the cladding of thewelded joints. Indeed, due to its low penetration and therefore low dilution,the electroslag strip cladding offers equivalent chemistry and corrosionproperties as the clad plate itself even in a one single layer. If the chemistryof the strip cladding does not match exactly the one of the clad, then as analternative, an alloy given a higher corrosion resistance is choosen.CLAD THICKNESS45° 45°STRIP WIDTHCLAD MATERIAL CARBON STEEL GROOVE DEPTHGROOVE WIDTHClad Material EN NumberStrip Cladding Solution matching the clad chemistry (or equivalent)Strip ESW Flux ** Number of LayersAlloy 410S 1.4000 * Soudotape 430 L RECORD EST 122 1Alloy 304W 1.4301 * Soudotape 308 L RECORD EST 308-1 1Alloy 308L 1.4306 Soudotape 308 L RECORD EST 308-1 1Alloy 321 1.4541 * Soudotape 21.11 LNb RECORD EST 122 1Alloy 347 1.4550 Soudotape 24.12 LNb RECORD EST 136 1STAINLESSAlloy 316 1.4401 Soudotape 21.13.3 L RECORD EST 122 1STEELAlloy 316L 1.4404 Soudotape 21.13.3 L RECORD EST 122 1Alloy 316L > 2,5Mo 1.4432 Soudotape 21.13.3 L RECORD EST 122 Mo 1Alloy 317L 1.4438 Soudotape 21.13.3 L RECORD EST 317-1 1Alloy 316Ti 1.4571 * Soudotape 21.13.3 L RECORD EST 130 1Alloy 904L 1.4539 Soudotape 20.25.5 LCu RECORD EST 385-1 1Alloy 800 1.4876 * Soudotape 625 RECORD EST 625-1 1Alloy 28 1.4563 Soudotape 27.31.4 LCu RECORD EST 201 1Alloy 926 1.4529 * Soudotape 625 RECORD EST 625-1 1Alloy 20 2.4660 * Soudotape 625 RECORD EST 625-1 1Alloy 825 2.4858 Soudotape 825 RECORD EST 138 1Alloy 625 2.4856 Soudotape 625 RECORD EST 625-1 1Alloy C22 2.4602 Soudotape NiCrMo22 RECORD EST 259 1NICKELAlloy C4 2.4610 Soudotape NiCrMo7 RECORD EST 259 1ALLOYSAlloy C276 2.4819 Soudotape NiCrMo4 RECORD EST 259 2Alloy 59 2.4605 Soudotape NiCrMo59 RECORD EST 259 1Alloy B2 2.4617 Soudotape NiMo7 RECORD EST 201-B 1Alloy 600 2.4816 Soudotape NiCr3 RECORD EST 201 1Alloy 400 2.4360 Soudotape NiCu7 RECORD EST 400 1Alloy 200 2.4066 Soudotape NiTi RECORD EST 200 1Alloy 201 2.4068 * Soudotape NiTi RECORD EST 200 1COPPER ALLOYS - SAW PROCESS ONLYSAW FluxCOPPERALLOYSAlloy CuNi 90/10 CW352HSoudotape NiCu7Soudotape CuNi30RECORD NiCuTRECORD CuNi30T2Alloy CuNi 70/30CW354H* not exact chemistry of the clad but adviced solution ** for SAW technique, please take contactSoudotape NiCu7Soudotape CuNi30RECORD NiCuTRECORD CuNi30T230 I 31

CLADDING NOZZLES1I TYPES OF STRIP CLADDING NOZZLESI SK 20-ES1-35›››I SK 30-ES2-75 I SK 60-ES3-207 I SK 125-ES1-300TYPEsk 20-es1-35 sk 30-es2-75 sk 60-es3-207 sk 125-es1-300 sk 180-es1-315*allowed strip width (mm) 10 - 20 15 - 20 - 30 30 - 60 30 - 60 - 90 - 120 120 - 150 - 180min. interNal diameter (mm):DIMENSIONS:longitudinal ** 150 220 380 550 700circular ** - 300 550 700 900200 x 80 x 60 mm7,9 x 3,2 x 2,4 inch125 x 150 x 220 mm4,9 x 5,9 x 8,7 inch265 x 280 x 270 mm10,4 x 11 x 10,6 inch300 x 450 x 270 mm11,8 x 17,7 x 10,6 inch500 x 370 x 350 mm19,7 x 14,6 x 13,8 inchWEIGHT:3 kg6,6 LBS4 kg8,8 LBS10 kg22,1 LBS18 kg39,8 LBS36 kg79,6 LBS* Only available on request** May vary depending on drive motor and equipment positioningFittings available on request for use with different gear boxes and for adaptation according to strip size

Extremely compact and fastest solutionfor cladding medium size pipes !›I SOUDO-BEAM 30-ESI Our SK Soudo-beams are composed by:› 1 SK Cladding nozzle 30 ES or 20 Es› 1 beam for longitudinal or circular welding› 1 moto-reducer› 1 aspirator› 1 electrical boxI Other items (camera, etc.) available on requestTYPESOUDO-BEAM 30LL1300 D300SOUDO-BEAM 30CL1300 D300SOUDO-BEAM 20LL1000 D150allowed strip width (mm) 15 - 20 - 30 15 - 20 - 30 10 - 20min. interNal diameter (mm):WEIGHTS:longitudinal ** 300 - 150circular ** - 300 -46kg101,7 LBS46kg101,7 LBS30kg66,3 LBS** May vary depending on drive motor and equipment positioningFittings available on request for use with different gear boxes and for adaptation according to strip size2I MAGNETIC STEERING DEVICEI SK CED 1 1370 C22 • SK CED 1 1370 C11TYPE:SK CED 1 1370C22SK CED 1 1370C11INPUT VOLTAGE 230V 110VFREQUENCY 50Hz 60Hz32 I 33

WIRE CLADDING FLUXES1I FLUXES FOR OVERLAYING WITH SOLID WIRESLow alloyStainlesssteelNickelbasecopperbaseType ofdeposited alloyWeldingprocessChemical analysesType of flux(all weld metal, typical)(weight -%)WIRE + RECORD C Mn Si Cr Ni Mo Cu N Nb Fe Al OthersType of WIREUnalloyed steelSAW SK Soudor D + Record SA 0,08 1,3 0,3 Bal.SAW SK Soudor DMo + Record SA 0,08 1,3 0,3 0,4 Bal.1Cr - 0,5 Mo SAW SK Soudor ECrMo 15 + Record SA 0,08 1 0,2 1 0,4 Bal.2 Cr - 1 Mo SAW SK Soudor BCrMo 21 + Record SA 0,055 1 0,2 2,1 0,9 Bal.3 Cr - 0,5Mo SAW SK Soudor B + Record R 250 0,06 0,9 0,9 3,1 0,5 Bal.3 Cr - 0,5 Mo - 2Mn SAW SK Soudor B + Record R 400 S 0,14 2,1 0,8 2,6 0,3 Bal.SK Soudor 308 L + Record IN 0,02 1,3 0,9 19,9 9,8 Bal.308L SAW SK Soudor 308 L + Record INC 0,07 1,4 0,6 18,8 9,3 Bal.SK Soudor 308 L + Record IND 24 0,02 1,2 0,6 19,5 9,6 Bal.SK Soudor 309 L + Record IND 24 0,02 1,3 0,6 22,8 12,9 Bal.309L SAWSK Soudor 309 L + Record IND 27 0,05 1,4 0,7 25,5 12,4 0,038 Bal.904L SAW SK Soudor 20.25.5 LCu + Record NiCrW 0,015 1,6 0,3 19,5 24,6 4,4 1,4 Bal.347 SAW SK Soudor 347 + Record IND 24 0,03 1,1 0,6 18,8 9,3 0,5 Bal.SK Soudor 22.9.3 L + Record IND 24 0,02 1,2 0,5 22 9 2,8 0,12 Bal.Super Duplex SAWSK Soudor 22.9.3 L + Record IND 45 0,011 1,3 0,5 21,8 8,3 3,1 0,14 Bal.625 SAW SK Soudor 625 Record NiCrW 412 0,015 2,1 0,3 21,5 Bal. 8,5 3,3 0,4 0,1TiC276 SAW SK Soudor NiCrMo 59 + Record NiCrW 0,02 0,3 0,2 22 Bal. 15,5 0,3400 SAW SK Soudor NiCu 7 + Record NiCuW 0,02 3,6 1,3 Bal. 29 0,6TiCuAl8SAWSK Soudor CuAl 8 + Record CuAlW 0,01 0,7 0,6 Bal. 3,0 7,5SK Soudor CuAl 10 + Record CuAlW 0,025 0,3 0,2 Bal. 3,5 7,9CuNi30 SAW SK Soudor CuNi30 + Record CuNiW 0,02 1 0,3 30 Bal.All those values are typical - *Ferrite measurement with Fischer Ferritescope according to AWS A4.22I FLUXES FOR SURFACING WITH CORED WIRESType ofapplicationManganese SteelTool SteelWeldingprocessLayerChemical analysesType of flux(all weld metal, typical)(weight -%)WIRE + RECORD C Mn Si Cr Ni Mo N Nb Fe CoType of WIRESAW SK 219-S SK 219-S + Record SA 0,95 18 1 4,6 bal.SAW SK AP-S SK AP-S + Record SA 0,45 16 0,5 13 bal.SAW SK 258-SA SK 258-SA + Record SA 0,5 1,5 0,6 6,2 1,8 bal.SAW SK 258L-SA SK 258L-SA + Record SA 0,18 1,5 0,5 5,6 1,8 bal.SAW SK D35-S SK D35-S + Record SA 0,12 0,2 0,5 15 2,3 bal. 13,5SAW SK 255-S SK 255-S + Record SA 4,6 0,9 0,5 27 bal.High metal Carbides SAW SK A43-S SK A43-S + Record SA 5,3 0,4 0,7 21,5 7 bal.SAW SK A45-S SK A45-S + Record SA 5,1 0,3 0,6 21,5 5,4 5,7 bal.Nickel alloys SAW SK Tool Alloy C-S SK Tool Alloy C-S + Record SA 0,05 0,2 0,6 16 bal. 16 7Cobalt alloysSAW SK Stelkay 6S SK Stelkay 6S + Record SK 0,95 0,9 1,5 28 3 bal.SAW SK Stelkay 306-SA SK Stelkay 306-SA + Record SK 0,5 1 1 24 5,5 7 4,5 bal.SAW SK 402-S SK 402-S + Record SA 0,07 6,6 1 17 8 bal.SAW SK 410NiMo-SA SK 410NiMo-SA + Record SA 0,04 1 0,3 12 5 0,9 bal.SAW SK 410-SA SK 410-SA + Record SA 0,1 1,3 0,3 12,5 bal.SAW SK 415-SA SK 415-SA + Record SA 0,09 0,9 0,5 13,5 2,1 1,1 0,2 bal.SAW SK 420-SA SK 420-SA + Record SA 0,27 1,4 0,4 13,5 bal.Stainless Steel SAW SK 430C-SA SK 430C-SA + Record SA 0,04 0,9 0,5 19,5 bal.SAW SK 461-SA SK 461-SA + Record SA 0,22 1 0,5 13,5 2 bal. 1,8SAW SK 740-SA SK 740-SA + Record SA 0,11 1,4 0,4 12,2 2,5 1,3 0,2 bal.SAW SK 742N-SK SK 742N-SK + Record SK 0,05 1,2 0,4 13,5 3,3 1,3 0,1 0,1 bal.SAW SK 740 H-SA SK 740 H-SA + Record SA 0,08 0,7 0,7 16,8 4,6 2 0,3 bal.SAW SK 740 L-SA SK 740 L-SA + Record SA 0,08 1 0,9 15,5 4 1,7 0,2 bal.

DIAMETER Welding parameters Depo Deposition rateHardness FN* (mm) (inch) A V cm/min inch/min kg/h lbs/h m²/h inch²/h180HB 4 0,16 450 - 550 28 - 30 40 - 50 15,8 - 19,7 5,4 11,9 0,2 298200HB 4 0,16 450 - 550 28 - 30 40 - 50 15,8 - 19,7 5,4 11,9 0,2 2984 0,16 450 - 550 28 - 30 40 - 50 15,8 - 19,7 5,4 11,9 0,2 2984 0,16 450 - 550 28 - 30 40 - 50 15,8 - 19,7 5,4 11,9 0,2 298280HB 4 0,16 450 - 550 28 - 30 40 - 50 15,8 - 19,7 5,4 11,9 0,2 29842HRc 4 0,16 450 - 550 28 - 30 40 - 50 15,8 - 19,7 5,4 11,9 0,2 2985 3,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 2765 3,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 2765 3,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 27610 3,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 2763,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 2763,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 2765 3,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 27635 3,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 2763,2 0,13 400 - 500 28 - 30 45 - 55 17,7 - 21,7 5,0 11,0 0,2 2761,6 0,06 200 - 300 28 - 30 40 - 50 15,8 - 19,7 2,1 4,6 0,1 1163,2 0,13 350 - 450 28 - 30 30 - 40 11,8 - 15,8 4,2 9,2 0,2 2323,2 0,13 300 - 400 32 - 35 30 - 40 11,8 - 15,8 4,2 9,2 0,2 232135HB 4 0,16 350 - 450 28 - 30 30 - 40 11,8 - 15,8 4,2 9,2 0,2 232135HB 4 0,16 350 - 450 28 - 30 30 - 40 11,8 - 15,8 4,2 9,2 0,2 2324 0,16 350 - 450 28 - 30 30 - 40 11,8 - 15,8 4,2 9,2 0,2 232DIAMETER Welding parameters Deposition rateOthers Hardness (mm) (inch) A V cm/min inch/min kg/h lbs/h m²/h inch²/h205HB 2,4 0,09 300 - 400 28 - 32 35 - 45 13,8 - 17,7 7,1 15,6 0,3 393200HB 2,4 0,09 300 - 400 28 - 32 35 - 45 13,8 - 17,7 7,1 15,6 0,3 3931,7W 57HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 4091,5W 44HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 40947HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 40958HRc 3,2 0,13 325 - 450 28 - 30 35 - 45 13,8 - 17,7 7 15,4 0,3 38763HRc 3,2 0,13 325 - 450 28 - 30 35 - 45 13,8 - 17,7 7 15,4 0,3 3871,9W 0,95V 64HRc 3,2 0,13 325 - 380 26 - 32 35 - 45 13,8 - 17,7 6,1 13,4 0,2 3374W 200HB 3,2 0,13 325 - 450 28 - 30 35 - 45 13,8 - 17,7 7 15,4 0,3 3874,2 W 40HRc 2,4 0,09 300 - 400 28 - 32 35 - 45 13,8 - 17,7 7,1 15,6 0,3 3932,8 W 35 HRc 3,2 0,13 325-500 28-30 30 - 35 11,8 - 13,8150HB 3,2 0,13 325 - 450 28 - 30 35 - 45 13,8 - 17,7 7 15,4 0,3 38739HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 40942HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 4090,3V 42HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 40953HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 409175HB 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 4090,9W 2V 43HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 4090,2V 46HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 4090,15V 44HRc 3,2 0,13 325 - 500 28 - 32 40 - 50 15,8 - 19,7 7,4 16,3 0,3 4090,25V 44HRc 3,2 0,13 325 - 450 28 - 30 30 - 50 11,8 - 19,7 7 15,4 0,3 3870,2V 43HRc 3,2 0,13 325 - 450 28 - 30 30 - 50 11,8 - 19,7 7 15,4 0,3 38734 I 35

I Soudokay,within the BöhlerWelding Group, isspecialised in research,production and sales offlux cored wires for hardfacingand strip/flux products forstrip cladding.Please contact us for more information.I SOUDOKAY SA II RUE DE L’YSER 2 II B-7180 SENEFFE I BELGIUM II T +32 (0)64 510 225 I F +32 (0)64 510 230 II soudokay@soudokay.be I www.soudokay.com II Soudokay can modify this document without any previous notice.The list of products present in the Soudokay catalogue is not restrictive.298·10·323