General Index - National Roofing Contractors Association

APP Modified Bitumen Part 2: Test Results1. COMPANY NAME AMERICAN BITECLUBRICANTS, INC.INC.2. PRODUCT NAME TIFFANY MDA3. PRODUCT DESCRIPTIONReinforcing POLYESTER POLYESTERTop surface SMOOTH GRANULE4. COMPLIES WITH:ASTM D 6222-98 Standard Specification for Atactic Polypropylene (APP) Modified BituminousSheet Materials Using Polyester Reinforcements (indicate type and grade, or NA)Type I, Grade G (granule surfaced)Type I, Grade S (smooth surfaced)Type II, Grade G (granule surfacedType II, Grade S (smooth surfaced)ASTM D 6223-98 Standard Specification for Atactic Polypropylene (APP) Modified BituminousSheet Material Using Polymer and Glass Fiber Reinforcements (indicate type and grade, or NA)Type I, Grade G (granule surfaced)Type I, Grade S (smooth surfaced)Type II, Grade G (granule surfacedType II, Grade S (smooth surfaced)5A. DIMENSIONS AND MASSES OF SHEET MATERIALS: POLYESTERREINFORCEMENTSThickness (min., mils) Grade S Type I: 140; Type II: 150 157Thickness (min., mils) Grade G Type I: 160; Type II: 170 160Net mass per unit area (min., lbs./100 sq. ft.) Grade S Type I: 70; Type II: 80Net mass per unit area (min., lbs./100 sq. ft.) Grade G Type I: 85; Type II: 100 110Bottom coating thickness (min., mils) Type I: 30; Type II: 40 805B. DIMENSIONS AND MASSES OF SHEET MATERIALS: COMBINATION OFPOLYESTER AND GLASS FIBER REINFORCEMENTSThickness (min., mils) Grade S 140Thickness (min., mils) Grade G 160Net mass per unit area (min., lbs./100 sq. ft.) Grade S 75Net mass per unit area (min., lbs./100 sq. ft.) Grade G 90Bottom coating thickness (min., mils) 406A. PHYSICAL PROPERTIES: POLYESTER REINFORCEMENTSMaximum load at 73.4 ±3.6 F MD and XMD, before and after heat conditioning, lbf.in., min. Type I: 50; Type II: 80 60.5Elongation at 73.4 ±3.6 MD and XMD, before and after heat conditioning, at max. load, % min. Type I: 23; Type II: 40 35Maximum load at 0 ±3.6 F MD and XMD, lbf/in., min. Type I: 60; Type II: 90 180 93.1Elongation at 0 ±3.6 F MD and XMD, at max. load, % min. Type I: 10; Type II: 15 64 21.8Elongation at 5% of max. load at 73.4 ±3.6 F, MD and XMD, % min. Type I: 30; Type II: 50 42.5Tear strength at 73.4 ±3.6 F, lbf, min Type I: 70; Type II: 80 102Low temperature flexibility, before and after heat conditioning, F, max. +32 +7 15.8Dimensional stability, % change, max. 1 ≤1High temperature stability, F min. 230 250Granule embedment, Grade G only, max. loss, grams 2