H-3057D 25 alloy - Haynes International, Inc.

COLD-WORKED PROPERTIESTypical Tensile Properties, Cold-Worked and Aged Sheet*UltimateElongationTest Tensile 0.2% Yield inTemperature Strength Strength 2 in. (51 mm)Condition °F °C Ksi MPa Ksi MPa %15% CW 70 20 168 1160 136 940 31+ Age A 1200 650 128 885 104 715 2370 20 181 1250 152 1050 171000 540 151 1040 129 890 1920% CW 1200 650 144 995 128 885 8+ Age A 1400 760 108 745 97 670 21600 870 74 510 59 405 61800 980 43 295 33 230 570 20 191 1315 162 1115 16600 315 165 1140 132 910 2820% CW 1000 540 149 1025 124 855 23+ Age B 1200 650 140 965 119 820 131400 760 116 800 92 635 71600 870 71 490 50 345 91800 980 42 290 31 215 12*Limited data for cold-rolled 0.050-inch (1.3 mm) thick sheet.Age A = 700°F (370°C)/1 hourAge B = 1100°F (595°C)/2 hoursTypical Hardness at 70°F (20°C), Cold-Worked and Aged Sheet*Hardness, Rockwell C, After Indicated Level ofCold Work and Subsequent Aging TreatmentCold-Work 900°F (480°C) 1100°F (595°C)% None 5 Hours 5 HoursNone 24 25 255 31 33 3110 37 39 3915 40 44 4320 44 44 47*Limited data for cold-rolled 0.070-inch (1.8 mm) thick sheet.HAYNES ® 25 alloy8