EMI suppressionwww.kolektor.comElectromagnetic disturbances are suppressed with the use of <strong>cores</strong> manufactured with 19G, 22G, 12G, 32G, 15G, 45G, 35G,55G and 75G. They differ in permeability as well as in a frequency and loss characteristics. Toroids and U <strong>cores</strong> are the bestchoice for this purpose. For application where an air gap is required, the L (pot) core is the most suitable solution.Toroids: (Fig.19)DesignationUncoated dimensions - 02 version Coated dimensions - 04 version Ie Ae Ved1 [mm] d2 [mm] h [mm] d1 [mm] d2 [mm] h [mm] mm mm2 mm3-09**T * 06 / 03 03 5,8 ±0,25 3,0 ±0,20 3,0 ±0,15 / / / noT * 06 / 04 04 6,30 ±0,25 3,8 ±0,20 4,0 ±0,15 / / / 15,2 3,75 57 noT * 10 / 06 04 10,0 ±0,25 6,0 ±0,20 4,0 ±0,20 ≤ 10,75 ≥ 5,45 ≤ 4,8 24,1 7,83 188 noT * 12 / 07 05 12,5 ±0,30 7,5 ±0,20 5,0 ±0,20 ≤ 13,4 ≥ 6,9 ≤ 5,9 30,1 12,2 368 noT * 13 / 07 03 13,0 ±0,30 7,0 ±0,25 3,0 ±0,15 ≤ 13,9 ≥ 6,35 ≤ 3,85 noT * 13 / 08 05 13,3 ±0,30 8,3 ±0,30 5,0 ±0,20 ≤ 14,2 ≥ 7,6 ≤ 5,9 33,9 12,5 423 noT * 14 / 08 04 13,4 ±0,30 7,5 ±0,20 4,0 ±0,20 ≤ 14,3 ≥ 6,9 ≤ 4,8 32,8 11,8 387 noT * 14 / 09 05 14,0 ±0,40 9,0 ±0,30 5,0 ±0,20 ≤ 15,0 ≥ 8,3 ≤ 5,9 noT * 14 / 09 09 14,0 ±0,40 9,0 ±0,30 9,0 ±0,30 ≤ 15,0 ≥ 8,3 ≤ 10,0 35,0 22,0 774 noT * 15 / 07 09 15,5 ±0,40 7,5 ±0,30 9,0 ±0,30 ≤ 16,5 ≥ 6,8 ≤ 10,0 33,1 34,3 1140 noT * 16 / 08 07 16,0 ±0,40 8,0 ±0,30 7,0 ±0,30 ≤ 17,1 ≥ 6,3 ≤ 8,0 noT * 16 / 10 06 16,0 ±0,40 9,6 ±0,30 6,1 ±0,20 ≤ 17,1 ≥ 8,9 ≤ 7,0 38,5 19,5 751,5 noT * 18 / 06 08 18,0 ±0,40 5,8 ±0,30 8,0 ±0,30 ≤ 19,0 ≥ 5,1 ≤ 9,0 noT * 19 / 11 08 18,9 ±0,40 11,0 ±0,35 8,0 ±0,30 ≤ 19,9 ≥ 10,25 ≤ 9,0 43,0 30,8 1325 noT * 20 / 10 07 20,0 ±0,50 9,8 ±0,35 7,0 ±0,30 ≤ 21,1 ≥ 9,0 ≤ 8,0 46,8 35,7 1670 yesT * 20 / 11 15 20,0 ±0,50 10,5 ±0,35 15,0 ±0,40 ≤ 21,1 ≥ 9,75 ≤ 16,1 44,7 69,0 3077 yesT * 22 / 14 07 22,1 ±0,50 13,7 ±0,4 7,0 ±0,30 ≤ 23,30 ≥ 12,8 ≤ 8,1 56,1 29,4 1646 noT * 22 / 14 13 22,1 ±0,50 13,7 ±0,4 13,0 ±0,35 ≤ 23,30 ≥ 12,8 ≤ 14,15 yesT * 23 / 12 07 22,5 ±0,50 12,3 ±0,4 7,0 ±0,30 ≤ 23,7 ≥ 11,9 ≤ 8,1 51,5 35,7 1383 noT * 25 / 15 10 25,0 ±0,60 15,0 ±0,4 10,0 ±0,30 ≤ 26,3 ≥ 14,1 ≤ 11,1 60,2 48,9 2994 yesT * 26 / 14 10 26,0 ±0,60 14,5 ±0,4 10,0 ±0,30 ≤ 27,3 ≥ 13,6 ≤ 11,1 60,1 55,9 3316 yesT * 26 / 14 15 26,0 ±0,60 14,5 ±0,4 15,0 ±0,40 ≤ 27,3 ≥ 13,6 ≤ 16,2 60,1 83,8 5042 yesT * 26 / 14 20 26,0 ±0,60 14,5 ±0,4 20,0 ±0,60 ≤ 27,3 ≥ 13,6 ≤ 21,4 60,1 111,8 5720 yesT * 28 / 15 20 27,5 ±0,60 14,9 ±0,4 20,0 ±0,60 ≤ 28,8 ≥ 14,0 ≤ 21,4 62,2 122,1 7640 noT * 29 / 19 15 29,5 ±0,90 19,0 ±0,6 15,0 ±0,40 ≤ 31,1 ≥ 18,0 ≤ 16,2 73,8 77,0 5680 noT * 30 / 20 07 29,5 ±0,90 20,0 ±0,5 7,0 ±0,30 ≤ 31,1 ≥ 19,0 ≤ 8,1 noT * 32 / 19 15 31,5 ±1,00 19,0 ±0,6 14,9 ±0,40 ≤ 33,1 ≥ 17,8 ≤ 16,1 76,0 86,9 6607 noT * 34 / 20 13 34,0 ±0,90 20,5 ±0,5 12,5 ±0,35 ≤ 35,6 ≥ 19,5 ≤ 13,65 yesT * 36 / 23 10 36,0 ±0,90 23,0 ±0,6 10,0 ±0,30 ≤ 37,6 ≥ 21,9 ≤ 11,1 89,6 63,9 5730 yesT * 36 / 23 15 36,0 ±0,90 23,0 ±0,6 15,0 ±0,40 ≤ 37,6 ≥ 21,9 ≤ 16,2 89,7 95,6 8750 yesT * 40 / 24 16 40,0 ±1,2 24,0 ±0,7 16,0 ±0,50 ≤ 41,9 ≥ 22,8 ≤ 17,3 96,3 125 12060 yesT * 42 / 26 18 42,0 ±1,2 26,0 ±0,6 18,0 ±0,70 ≤ 43,9 ≥ 24,8 ≤ 19,5 102 141 26640 yesT * 44 / 24 22 44,5 ±1,2 24,35 ±0,7 22,0 ±0,70 ≤ 45,7 ≥ 23,15 ≤ 23,5 noT * 50 / 34 30 50,0 ±0,8 34,0 ±0,6 30,0 ±0,50 ≤ 51,6 ≥ 32,8 ≤ 31,3 128,7 237 30516 noT * 56 / 32 18 55,5 ±1,6 32,3 ±0,9 18,0 ±0,70 ≤ 57,9 ≥ 30,9 ≤ 19,5 132 202 26640 yesT * 58 / 41 18 58,3 ±1,0 40,8 ±0,8 17,6 ±0,40 ≤ 60,1 ≥ 39,6 ≤ 18,8 noT * 63 / 38 25 63,0 ±1,8 38,0 ±1,0 25,0 ±0,80 ≤ 65,3 ≥ 36,0 ≤ 26,6 152 300 45600 noT * 85 / 62 20 85,0 ±1,8 62,0 ±1,1 20,0 ±0,7 ≤ 87,6 ≥ 60,4 ≤ 21,5 231 228 52620 noT * 87 / 56 13 87,0 ±1,8 56,0 ±1,1 12,7 ±0,35 ≤ 89,5 ≥ 54,4 ≤ 13,85 217,5 193 42133 noLEGEND ** VERSION COAT THICKNESS Vrms* Material -02 chamfered / /-05 deburred / /-04 epoxy coated ≈ 0,15 mm T10 through T20 ≥ 1,5 kV-04 epoxy coated ≈ 0,25 mm > T20 ≥ 2,0 kV-09 with plastic caps ≈ 0,55 mm ≥ 2,5 kV18
www.kolektor.comToroids – AL valuesAL value [nH]Designation High permeability materials High frequency materials* material type 19G 22G 42G 12G 32G 52G 2C 1Fµi 4300 6000 8000 10000 12000 15000 300 80tolerance +30/-20% +30/-20% +25/-25% +30/-30% +30/-30% +30/-30% +30/-20% +30/-20%T * 06 / 03 03 1720 2400 3200 4000 4800 6000 120 32T * 06 / 04 04 1740 2400 3200 4040 4850 6050 120 32T * 10 / 06 04 1760 2450 3250 4090 4900 6100 120 32T * 12 / 07 05 2200 3050 4000 5100 6100 150 40T * 13 / 07 03 1430 2000 2650 3300 4000 105 27T * 13 / 08 05 5340 2830 3700 4700 5700 140 38T * 14 / 08 04 2000 2780 3650 4640 5550 140 37T * 14 / 09 05 1900 2650 3250 4400 5300 130 35T * 14 / 09 09 3400 4770 6350 7900 9500 240 64T * 15 / 07 09 5600 7840 10400 13000 15500 380 105T * 16 / 08 07 4170 5820 7700 9700 11600 290 80T * 16 / 10 06 2650 3700 4900 6130 7350 185 50T * 18 / 06 08 7800 10850 14400 18100 540 145T * 19 / 11 08 3700 5200 6900 8650 260 70T * 20 / 10 07 4300 6000 7800 10000 300 80T * 20 / 11 15 8300 11600 15000 19300 580 155T * 22 / 14 07 2900 4000 5300 6900 200 53T * 22 / 14 13 5340 7450 9900 12150 370 100T * 23 / 12 07 3630 5070 6700 8450 250 67T * 25 / 15 10 4300 6000 7650 10000 300 80T * 26 / 14 10 5000 7000 9200 11650 350 93T * 26 / 14 15 7500 10500 13800 17500 525 140T * 26 / 14 20 10000 14000 18500 23000 700 185T * 28 / 15 20 10500 14700 19500 24500 735 195T * 29 / 19 15 5600 7800 10400 13000 390 104T * 30 / 20 07 2340 3260 4300 5400 160 43T * 32 / 19 15 5900 8250 11000 13700 410 110T * 34 / 20 13 5450 7600 10000 12650 380 105T * 36 / 23 10 3850 5350 7000 8960 270 70T * 36 / 23 15 5780 7800 10200 13400 400 110T * 40 / 24 16 7000 9800 13500 490 130T * 42 / 26 18 7400 10350 13700 520 140T * 44 / 24 22 11400 15900 21200T * 50 / 34 30 10000 13000 18500T * 56 / 32 18 8900 11650 15600T * 58 / 41 18 5300 7500 10500T * 63 / 38 25 10200 14200 19000T * 85 / 62 20 5300 7400T * 87 / 56 13 4800 6700 9000Ordering example: for toroidsShape of coreMaterialDimensionVersionT 19G 22/14 07 -04Ordering example: for other <strong>cores</strong>Shape of coreMaterialDimensionTolerance of A LvalueE 45G 12 06 04 - 00Fig. 1919