Antagon Interaction

Vacumat 2500Stand-bytemp.Finaltemp.DryingtimeHeatingrateHold timeTime vacuümON1 st paste opaque firing 400°C 915°C 7.0 60 2.0 1.82 nd paste opaque firing 400°C 910°C 7.0 60 2.0 1.8Margin firing 500°C 895°C 4.0 60 2.0 1.71 st dentin firing 500°C 895°C 6.0 60 2.0 1.52 nd dentin firing 500°C 890°C 4.0 60 2.0 1.5Glaze firing 500°C 885°C 4.0 60 0.5 0.0Correction mass firing 500°C 830°C 4.0 60 2.0 1.0Important:The firing temperatures indicated are target values.Temperatures may vary from one ceramic furnaceto another and must be adapted accordingly.Choice of ceramic alloy:Antagon Interaction can be easily fired on enamelingalloys with a thermal expansion coefficient between13.8 and 14.9 µm/m.K (25-500°C).Quick cooling down to 14.0 µm/m.K – 0 min.Normal cooling down to 14.3 µm/m.K – 2 min.Slow cooling down from 14.4 µm/m.K – 5-7 min.Austromat 30011 st opaque firing C400 T180 T240 • L9V9 T060 • C915 T60 VO T60 CO LO T2 C4002 nd opaque firing C400 T180 T240 • L9V9 T060 • C915 T60 VO T60 CO LO T2 C4001 st dentin firing C500 T120 T180 • L9V9 T060 • C895 T60 VO T60 CO LO T2 C5002 nd dentin firing C500 T120 T120 • L9V9 T060 • C890 T60 VO T60 CO LO T2 C500Glazefiring C500 T120 T120 • L9 T060 • C885 T60 CO LO T2 C500MarginfiringC500 T120 T180 • L9V9 T060 • C895 T60 VO T60 CO LO T2 C500Correction massfiringC500 T120 T90 • L9V9 T060 • C830 T60 VO T60 CO LO T2 C500Programat P90/P95Standbytemp.HeatingrateFiringtemp.ClosingtimeHold timeVacuumONVacuumOFF1 st paste opaque firing 400°C 60 915°C 7 1 450°C 915°C2 nd paste opaque firing 400°C 60 910°C 7 1 450°C 910°CMargin firing 450°C 60 895°C 4-5 1 450°C 895°C1 st dentin firing 450°C 60 895°C 5-7 1 450°C 895°C2 nd dentin firing 450°C 60 890°C 3-5 1 450°C 890°CGlaze firing 450°C 60 885°C 4 0,5-1 450°C –Correction mass firing 400°C 60 830°C 4 1-2 450°C 830°C17