Material Properties_VG708 (FFO)x - Simrit

Material Properties:VG708 (FFO)NOTE - All testing done on AS568-214 size O-ringsOriginal Properties AMS-7254 VG708Hardness, IRHD, ASTM D1415 70±5 72Tensile Strength, psi, ASTM D1414 600 min. 917Ultimate Elongation, %, ASTM D1414 100 min. 162Specific Gravity, g/cc, ASTM D297 Report 1.89Temperature Retraction, ASTM D1329TR-10, degrees F -49 or colder -56Air Aging ASTM D573, 70 hrs. at 400°FHardness change, Shore A, ASTM D1415 -5 to +5 +1% Tensile Strength change, ASTM D1414 -25 max. -12.4% Elongation change, ASTM D1414 -25 max. -21ASTM Fuel B fluid immersion, ASTM D471 and ASTM D1414, 70 hrs. at 73°FIRHD Hardness change, ASTM D1415 -15 to 0 -7% Tensile Strength change, ASTM D1414 -30 max. -18.8% Elongation change, ASTM D1414 -20 max. -4.3% Volume change, ASTM D471 0 to +15 +13.1AS1241 Type V fluid immersion, ASTM D471 and ASTM D1414, 70 hrs. at 300°FIRHD Hardness change, ASTM D1415 -15 to 0 -3% Tensile Strength change, ASTM D1414 -20 max. +5.2% Elongation change, ASTM D1414 -20 max. +5.6% Volume change, ASTM D471 0 to +12 +6.3Compression Set, ASTM D395 Method B and ASTM D1414, 70 hrs. at 300°F in AS1241 Type V fluid% Permanent set 20 max. 4.9Compression Set, ASTM D395 Method B and ASTM D1414, 500 hrs. at 300°F in A1241 Type V fluid% Permanent set 45 max. 4.9AMS 3023 fluid immersion, ASTM D471 and ASTM D1414, 70 hrs. at 400°FIRHD Hardness change, ASTM D1415 -10 to 0 -2% Tensile Strength change, ASTM D1414 -20 max. +5.8% Elongation change, ASTM D1414 -20 max. -3.7% Volume change, ASTM D471 0 to +5 +2.7Compression Set, ASTM D395 Method B and ASTM D1414, 70 hrs. at 400°F in AMS 3023 fluid% Permanent set 35 max. 13.5Compression Set, ASTM D395 Method B and ASTM D1414, 500 hrs. at 400°F in AMS 3023 fluid% Permanent set 70 max. 65.7© Copyright 2013The information contained herein is believed to be reliable, but no representation, guarantees or warranties of any kindare made to its accuracy or suitability for any purpose. The information presented herein is based on laboratory testingand does not necessarily indicate end product performance. Full scale testing and end product performance are theresponsibility of the user.www.simrit.com866-274-6748

MIL-H-83282 fluid immersion, ASTM D471 and ASTM D1414, 70 hrs. at 275°FIRHD Hardness change, ASTM D1415 -10 to 0 -4% Tensile Strength change, ASTM D1414 -20 max. +3.8% Elongation change, ASTM D1414 -20 max. -3.7% Volume change, ASTM D471 0 to +5 +1.9Compression Set, ASTM D395 Method B and ASTM D1414, 70 hrs. at 275°F in MIL-H-83282 fluid% Permanent set 20 max. 8.4Compression Set, ASTM D395 Method B and ASTM D1414, 1000 hrs. at 275°F in MIL-H-83282 fluid% Permanent set 40 max. 31.6Temperature Retraction, ASTM D1329, after fluid immersion for 70 hrs. at 275°F in MIL-H-83282 fluidTR-10, degrees F -49 or colder -56Compression Set, ASTM D395 Method B and ASTM D1414, 70 hrs. at 400°F% Permanent set 45 max. 32.5© Copyright 2013The information contained herein is believed to be reliable, but no representation, guarantees or warranties of any kindare made to its accuracy or suitability for any purpose. The information presented herein is based on laboratory testingand does not necessarily indicate end product performance. Full scale testing and end product performance are theresponsibility of the user.www.simrit.com866-274-6748