All you need is Kerr Adhesives Restorative Procedure OptiBond Respected by leading opinion leaders, perceived as the gold standard of the adhesive technology OptiBond family provides performance, versatility and predictable results. ... the name that stands for adhesive brilliance... OptiBond Family Total-etch Self-etch Chemistry Behind GPDM Adhesive Monomer No. of steps 3 2 1 Gel Etchant All OptiBond adhesives comprise the unique proprietary chemistry which made OptiBond TM FL the gold standard among bonding agents. Proven GPDM adhesive monomers are effective in creating a superb bond with minimized risk of microleakage and post-operative sensitivity. Primer Adhesive 4 th generation 5 th generation 7 th generation GPDM = Glycero-Phosphate-1.3 Dimethacrylate 9
OptiBond OptiBond OptiBond FL Solo Plus All-In-One Years in market 15 years 10 years 3 years Application Direct procedure • • • Indirect procedure - • • Etching Yes Yes No Application time 1:30 min. 1:10 min. 0:55 min. Bond strength Mpa To dentine 32 MPa 31 MPa 36 MPa To enamel 33 MPa 34 MPa 26 MPa Properties Filler load 48% 15% 7% Works on wet or dry dentine • • • Film thickness ~60 µ ~10 µ ~5 µ Radiopacity 267% Al - - Solvent Water Ethanol Water, Ethanol, Ethanol Acetone Packaging Storage conditions Ambient Ambient Refrigeration temperature temperature 2 °C to 8 °C Bottle content Primer Bottle 8 ml Adhesive Bottle 8 ml 5 ml 5 ml Unidose content 0.1 ml 0.1 ml 0.18 ml Filled adhesive technology The technology of filled adhesives was first time ever introduced by Kerr in its OptiBond FL adhesive. Glass Filler in OptiBond Adhesive: • Reinforces the dentin tubules for high bond strengths and protection against microleakage • Releases fluoride over the long-term • Decreases polymerization shrinkage • Works as a shock absorber and thermal barrier between the restorative material and the tooth • Virtually eliminates post-operative sensitivity • Works well in dry, moist or wet environment 10 Your practice is our inspiration.
- Page 1 and 2: Clinical Guide for Restorative Proc
- Page 3 and 4: Everyday challenge in restorative p
- Page 5 and 6: STEP PRODUCT KERR PRODUCTS Adhesion
- Page 7 and 8: Finishing and polishing Flexible di
- Page 9: systems. Although they were the fir
- Page 13 and 14: OptiBond FL Application Guide Opti
- Page 15 and 16: OptiBond Solo Plus Application Gui
- Page 17 and 18: OptiBond All-In-One Application Gu
- Page 19 and 20: for resistance, biocompatibility, a
- Page 21 and 22: When two monomers combine the molec
- Page 23 and 24: Improved Handling Handling Comparis
- Page 25 and 26: 7) Etching for 15 seconds with Gel
- Page 27 and 28: 7) Application of a thin layer of P
- Page 29 and 30: 9) First layer of Herculite XRV Ult
- Page 31 and 32: 30 Your practice is our inspiration
- Page 33 and 34: Tungsten carbide finishing burs var
- Page 35 and 36: Surface treatment of composite fill
- Page 37 and 38: Interproximal Surfaces Surface Roug
- Page 39 and 40: Abrasive coating OptiDisc Kerr 200
- Page 41 and 42: Usage on different surfaces Compari
- Page 43 and 44: Herculite XRV References 1. Effect
- Page 45: KerrHawe SA | Via Strecce 4 | P.O.B
OptiBond OptiBond OptiBond <br />
FL Solo Plus All-In-One<br />
Years in market 15 years 10 years 3 years<br />
Application<br />
Direct procedure • • •<br />
Indirect procedure - • •<br />
Etching Yes Yes No<br />
Application time 1:30 min. 1:10 min. 0:55 min.<br />
Bond strength Mpa<br />
To dentine 32 MPa 31 MPa 36 MPa<br />
To enamel 33 MPa 34 MPa 26 MPa<br />
Properties<br />
Filler load 48% 15% 7%<br />
Works on wet or dry dentine • • •<br />
Film thickness ~60 µ ~10 µ ~5 µ<br />
Radiopacity 267% Al - -<br />
Solvent Water Ethanol Water, Ethanol,<br />
Ethanol<br />
Acetone<br />
Packaging<br />
Storage conditions Ambient Ambient Refrigeration<br />
temperature temperature 2 °C to 8 °C<br />
Bottle content<br />
Primer Bottle 8 ml<br />
Adhesive Bottle 8 ml<br />
5 ml 5 ml<br />
Unidose content 0.1 ml 0.1 ml 0.18 ml<br />
Filled adhesive technology<br />
The technology of filled adhesives was first<br />
time ever introduced by <strong>Kerr</strong> in its OptiBond FL<br />
adhesive.<br />
Glass Filler in OptiBond Adhesive:<br />
• Reinforces the dentin tubules for high bond<br />
strengths and protection against microleakage<br />
• Releases fluoride over the long-term<br />
• Decreases polymerization shrinkage<br />
• Works as a shock absorber and thermal barrier<br />
between the restorative material and the tooth<br />
• Virtually eliminates post-operative sensitivity<br />
• Works well in dry, moist or wet environment<br />