Matched Tooling Brochure - Scott Bader

Typical Properties for Crystic 15PA
when tested in accordance with the appropriate BS or BS EN ISO test method.
Typical Properties for Crystic 474PA
when tested in accordance with BS 2782.
Typical Properties
Liquid Gelcoat
Typical Properties
Liquid Resin
Viscosity @ 25 0 C
Typical Properties for Crystic 14PA
when tested in accordance with the appropriate BS or BS EN ISO test method.
Viscosity @ 25 0 C
Typical Properties for Crystic VE679PA
when tested in accordance with the appropriate BS or BS EN ISO test method.
Appearance
Typical Properties
Typical Properties
Liquid Resin
Red / Brown
Viscosity @ 25 0 C 37.35 sec -1 Poise 3.5
Viscosity @ 25 0 C 4500 sec -1 Poise 2.3
Specific Gravity @ 25 0 C 1.07
Stability in the dark @ 25 0 C months 3
Geltime @ 25 0 C using 2% Butanox LPT minutes 18
Geltime @ 25 0 C using 2% Butanox M50 minutes 23
Mechnical Properties
Thixotropic
Volatile content % 40
Stability in the dark @ 20 0 C months 3
Geltime @ 25 0 C (using 2% Butanox M50) minutesi 10
Liquid
Gelcoat
Thixotropic
Specific Gravity @ 25 0 C 1.07
Volatile content % 47
Stability in the dark @ 20 0 C months 3
Geltime @ 25 0 C (using 2% Butanox M50) minutesi 10
* **
Barcol hardness (GYZJ 934 - 1) 23 35
HDT 0
C 60 94***
Water absorption 24hrs @ 23 0 C mg 10 15
Tensile strength MPa 60 52
Tensile modulus GPa 2.7 3.0
Elongation at break % 4.3 2.1
Specific gravity @ 25 0 C 1.16 1.16
Appearance
* Curing schedule - 24hrs @20 0 C, 3hrs @80 0 C
** Curing schedule - 24hrs @20 0 C, 5hrs @80 0 C, 3hrs @120 0 C
Cloudy/Mauvish
Viscosity @ 25 0 C 37.35 sec -1 Poise 5.3
Viscosity @ 25 0 C 4500 sec -1 Poise 3.4
Specific Gravity @ 25 0 C 1.10
Volatile content % 38
Acid Value mg KOH/g 23
Stability in the dark @ 20 0 C months 6
Geltime @ 25 0 C (using 2% Butanox M50) months 12
Mechnical Properties
Barcol Hardness (Model GYZJ 934-1) 48
HDT 0
C 112
Water absorption 24hrs @ 23 0 C mg 28
Tensile strength MPa 57
Tensile modulus MPa 3700
Elongation at break % 1.8
Specific gravity @ 25 0 C 1.22
Volumetric shrinkage % 8.2
Typical Properties for Crystic RTR 4000PA
when tested in accordance with the appropriate BS or BS EN ISO test method.
Appearance
Typical Properties
Liquid Resin
Light Brown
Viscosity @ 25 0 C (ICI Cone & Plate) Poise 5
Specific Gravity @ 25 0 C 1.35
Volatile content % 25 - 30%
Geltime @ 25 0 C (using 1% Butanox M50) minutes 35 - 40
Stability (at less than 20 0 C in original container) months 3
Mechanical Properties
HDT 0 C 63
Tensile strength** MPa 114
Tensile Modulus** MPa 8075
Elongation at Break** % 2.0
* Curing schedule - 24hrs @20 0 C, 16hrs @40 0 C
** Curing schedule - 24hrs @20 0 C, 3hrs @80 0 C
*** Curing schedule - 24hrs @20 0 C, 5hrs @80 0 C, 3hrs @120 0 C
* Curing schedule - 24hrs @ 20 0 C, 16hrs@40 0 C
** Tests carried out on resin reinforced with 28% 450g/m 2 CSM.
Technology that takes the Lead
Head office, UK +44 1933 663100 France +33 22 66 27 66 Scandinavia +46 346 10100 Germany +49 961 401 84474 Croatia +385 1 240 6440 Eastern Europe +420 48 5228 344
Spain +34 93 553 1162 U.S.A +1 330 920 4410 South Africa +27 31 736 8500 Middle East +971 488 35025 Asia +86 (21) 52987778 / +86 (21) 52988887
ATC Formulated Polymers (Canada) +1 905 681 8112 Satyen Scott Bader Pvt Ltd (India) +91 22 4220 1555
email: composites@scottbader.com
MTS/02/13