BISCO DENTAL PRODUCTS CANADA - dentes.sk

CORE MATERIALS
BIS-CORE
Dual-Cured Core Build-Up
Combined with ALL-BOND 3 ® , ALL-BOND 2 ® or ONE-STEP ® PLUS,
BIS-CORE will provide a restorative core that exhibits excellent
retention and resistance to compressive forces.
BENEFITS Features & Benefits
Dual-cured composite with an adaptable working time
Available in two radiopaque shades which allows for both conventional and aesthetic
fixed restorations
Highlights and Facts
% Filled
(Weight/Volume)
Particle
Size Range
Diametral
Tensile Strength
Compressive
Strength
Flexural
Strength
Flexural
Modulus
Self-Cure
78 / 60
0.04 - 9 µm
49 MPa
311.5 MPa
98.5 MPa
12.6 GPa
Light-Cure
78 / 60
0.04 - 9 µm
54 MPa
313.5 MPa
103 MPa
13.2 GPa
At Room Temperature (22°C/72°F):
Ordering Information
• 2 Syr Pkg Opaque or Natural (5g Base & 5g Catalyst)
• Refi ll Syringe (5g)
Working Time:
Setting Time:
W / paste Catalyst: Minimum 1 Minute 30 Seconds
W / paste Catalyst: Maximum 5 Minutes 30 Seconds
CORE-FLO
Self-Cured Flowable Core Build-Up
CORE-FLO’s creamy consistency allows it to be used for post
cementation and core build-up in one easy application.
Highlights and Facts
% Filled
(Weight/Volume)
Particle
Size Range
Diametral
Tensile Strength
Compressive
Strength
Flexural
Strength
Flexural
Modulus
69/56
0.04-9 µm
48.5 MPa
255 MPa
95.5 MPa
8 GPa
At Room Temperature (22°C/72°F):
Working
Time:
Setting
Time:
Minimum 1 Minute 30 Seconds
Maximum 3 Minutes 30 Seconds
CORE-FLO is a flowable, fast-setting,
self-cured core build-up composite.
Its creamy consistency allows it to be
syringed directly into the canal for optimal
adaptation. Available in two shades:
OPAQUE and NATURAL.
• Recommended for both cementation of posts and core build-up in one application.
• Ideal as a syringeable core material.
Ordering Information
• Opaque 2 Syringe Kit (4g Base and 4g Catalyst)
• Econo Pkg Opaque or Natural (Jars: 28g Base and 28g Catalyst)
26
1-800-667-8811 / www.biscocanada.com