YOUR PARTNER FOR HIGH<br />
SPEED STEELS, TOOL STEELS<br />
AND SPECIAL MATERIALS
High speed steels<br />
Hot work tool steels<br />
Cold work tool steels<br />
BÖHLER grade Chemical composition in % Standards<br />
C Cr Mo Ni V W Co Si Mn Others DIN / EN AISI<br />
S500 1.10 3.85 9.20 – 1.00 1.35 7.75 – – – 1.3247 M42<br />
HS2-10-1-8<br />
S600 0.91 4.05 5.00 – 1.75 6.20 – – – – 1.3343, HS6-5-2 ~ M2 reg. C<br />
~ 1.3554 LW<br />
S705 0.92 4.05 4.95 – 1.85 6.20 4.75 – – – 1.3243 ~ M41<br />
HS6-5-2-5<br />
S290 2.01 3.75 2.45 – 5.05 14.30 11.00 – – – – –<br />
S390<br />
S590<br />
S690<br />
S790<br />
1.64 4.75 2.00 – 4.80 10.40 7.98 – – – – –<br />
1.29 4.20 5.00 – 3.03 6.33 8.40 – – – 1.3244 –<br />
HS6-5-3-8<br />
1.35 4.13 5.00 – 4.13 5.88 – – – – ~ 1.3351 ~ M4<br />
~ HS6-5-4<br />
1.29 4.20 4.98 – 3.03 6.33 – – – – 1.3345 ~ M3 Cl.2<br />
HS6-5-3C<br />
BÖHLER grade Chemical composition in % Standards<br />
C Cr Mo Ni V W Co Si Mn Others DIN / EN AISI<br />
W100 0.29 2.65 – – 0.35 8.50 – 0.23 0.30 – 1.2581 ~ H21<br />
X30WCrV9-3<br />
W300 0.38 5.00 1.30 – 0.40 – – 1.05 0.40 – 1.2343 H11<br />
X38CrMoV5-1<br />
W302 0.39 5.15 1.38 – 0.95 – – 1.05 0.40 – 1.2344 H13<br />
X40CrMoV5-1<br />
W303 0.38 5.00 2.80 – 0.55 – – 0.40 0.40 – 1.2367 –<br />
X38CrMoV5-3<br />
0.50 4.50 3.00 – 0.60 – – 0.20 0.25 – – –<br />
W360<br />
W400 0.38 5.05 1.30 – 0.50 – – 0.20 0.32 – ~ 1.2343 ~ H11<br />
~ X37CrMoV5-1<br />
W403 0.38 5.00 2.80 – 0.65 – – 0.20 0.25 – ~ 1.2367 –<br />
~ X38CrMoV5-3<br />
BÖHLER grade Chemical composition in % Standards<br />
C Cr Mo Ni V W Co Si Mn Others DIN / EN AISI<br />
K100 2.00 11.50 – – – – – 0.25 0.33 – 1.2080 ~ D3<br />
X210Cr12<br />
K105 1.60 11.50 0.60 – 0.30 0.50 – 0.33 0.30 – 1.2601 –<br />
X165CrMoV12<br />
K107 2.10 11.50 – – – 0.70 – 0.25 0.38 – 1.2436 (~ D6)<br />
X210CrW12<br />
K110 1.55 11.25 0.75 – 0.75 – – 0.30 0.30 – 1.2379 D2<br />
X155CrVMo12-1<br />
K245 0.63 0.60 – – – – – 1.05 1.05 – 1.2101 –<br />
62SiMnCr4<br />
K340 1.10 8.25 2.10 – 0.50 – – 0.90 0.40 +Al – –<br />
+Nb<br />
K360 1.26 8.75 2.70 – 1.18 – – 0.90 0.35 +Al – –<br />
+Nb<br />
K390 2.47 4.23 3.80 0.21 9.00 1.00 2.00 0.55 0.42 – – –<br />
K455<br />
K460<br />
K890<br />
0.63 1.05 – – 0.18 1.95 – 0.60 0.30 – 1.2550 ~ S1<br />
60WCrV7<br />
0.95 0.55 – – 0.10 0.55 – 0.25 1.10 – 1.2510 O1<br />
100MnCrW4<br />
0.85 4.35 2.80 – 2.10 2.55 4.50 0.55 0.40 – – –<br />
Plastic mould steels<br />
BÖHLER grade Chemical composition in % Standards<br />
C Cr Mo Ni V W Co Si Mn Others DIN / EN AISI<br />
M238 0.38 1.95 0.20 1.10 – – – 0.30 1.45 – 1.2738 ~ P20 mod.<br />
40CrMnNiMo8-6-4<br />
M261 0.13 0.35 – 3.50 – – – 0.30 1.95 S =0.13, Al =1.15 – –<br />
Cu=1.20<br />
M303 0.28 14.45 0.95 0.85 – – – 0.25 0.65 +N – –<br />
–<br />
M310 0.38 14.25 – – 0.20 – – 0.70 0.43 – ~ 1.2083 ~ 420<br />
~ X42Cr13<br />
M315 0.045 12.60 – – – – – 0.30 0.93 S =0.10 – –<br />
Cu = 0,40<br />
M333 0.28 13.50 – – – – – 0.30 0.30 +N – –<br />
M340<br />
0.54 17.25 1.13 – 0.10 – – 0.43 0.40 +N – –<br />
M390<br />
M461<br />
1.91 20.00 1.00 – 4.00 0.60 – 0.60 0.30 – – –<br />
0.13 0.35 – 3.50 0.08 – – 0.30 1.95 Al =1.15 – –<br />
Cu=1.20
High speed steels<br />
Hot work tool steels<br />
Cold work tool steels<br />
BÖHLER grade Hardness after Hardening Quenchant °C Obtainable<br />
annealing temperature °C hardness HRc<br />
S500<br />
max. 280 HB 1170 – 1210 °C Oil, Vacuum, Salt 67 – 69 HRc<br />
bath (500 – 550 °C)<br />
S600<br />
max. 280 HB 1190 – 1230 °C Oil, Vacuum, Salt 64 – 66 HRc<br />
bath (500 – 550 °C)<br />
S705<br />
max. 280 HB 1190 – 1230 °C Oil, Vacuum, Salt 64 – 66 HRc<br />
bath (500 – 550 °C)<br />
S290<br />
max. 350 HB 1150 – 1210 °C salt bath Salt Bath, Gas 66 – 70 HRc<br />
1150 – 1190 °C vacuum<br />
S390<br />
max. 300 HB 1150 – 1230 °C Oil, Vacuum, Salt 65 – 69 HRc<br />
bath (500 – 550 °C)<br />
S590<br />
max. 300 HB 1075 – 1180 °C Oil, Vacuum, Salt 65 – 67 HRc<br />
bath (500 – 550 °C)<br />
S690<br />
max. 280 HB 1150 – 1200 °C Oil, Vacuum, Salt 64 – 66 HRc<br />
bath (500 – 550 °C)<br />
S790<br />
max. 280 HB 1050 – 1180 °C Oil, Vacuum, Salt 64 – 66 HRc<br />
bath (500 – 550 °C)<br />
BÖHLER grade Hardness after Hardening Quenchant °C Obtainable Aver. Rockwell C hardness after temp. at °C<br />
annealing temperature °C hardness HRc 400 500 550 600 650 700<br />
W100<br />
W300<br />
W302<br />
W303<br />
W360<br />
W400<br />
W403<br />
240 HB 1070 – 1150 °C Oil, Salt bath (500 – 550 °C) 48 – 52 HRc 50 51 52 50 46 38<br />
Air, Vacuum<br />
44 – 48 HRc<br />
205 HB 1000 – 1040 °C Oil, Salt bath (500 – 550 °C) 52 – 56 HRc 53 54 52 48 38 30<br />
Air, Vacuum<br />
50 – 54 HRc<br />
205 HB 1020 – 1080 °C Oil, Salt bath (500 – 550 °C) 52 – 56 HRc 54 55 54 50 40 32<br />
Air, Vacuum<br />
50 – 54 HRc<br />
205 HB 1030 – 1080 °C Oil, Salt bath (500 – 550 °C) 52 – 56 HRc 52 54 53 50 44 35<br />
Air, Vacuum<br />
50 – 54 HRc<br />
205 HB approx. 1050 °C Oil, Salt bath (500 – 550 °C) 52 – 57 HRc see tempering chart<br />
Air, Vacuum<br />
recommended<br />
205 HB 980 – 990 °C Oil, Salt bath (500 – 550 °C) 52 – 54 HRc 53 54 52 48 38 30<br />
Air, Vacuum<br />
50 – 53 HRc<br />
205 HB 1020 – 1030 °C Oil, Salt bath (500 – 550 °C) 52 – 54 HRc 52 54 53 50 44 35<br />
Air, Vacuum<br />
50 – 53 HRc<br />
BÖHLER grade Hardness after Hardening Quenchant °C Obtainable Average Rockwell C hardness after tempering at °C<br />
annealing temperature °C hardness HRc 100 200 300 400 500 520 550<br />
K100<br />
K105<br />
K107<br />
K110<br />
K245<br />
K340<br />
K360<br />
K390<br />
max. 248 HB 940 – 970 °C Oil, Air, Vacuum, Salt 63 – 65 HRc 64 62 59 57 – – –<br />
bath (500 – 550 °C)<br />
max. 250 HB 980 – 1010 °C Oil, Air, Vacuum, Salt 63 – 65 HRc 64 62 60 58 – – –<br />
bath (500 – 550 °C)<br />
max. 250 HB 950 – 980 °C Oil, Air, Vacuum, Salt 64 – 66 HRc 65 63 61 60 – – –<br />
bath (500 – 550 °C)<br />
max. 250 HB 1020 – 1040 °C Oil, Air, Vacuum, Salt 63 – 65 HRc 63 61 59 58 – – –<br />
bath (500 – 550 °C)<br />
max. 235 HB 830 – 860 °C Oil 59 – 62 HRc 61 60 57 51 – – –<br />
max. 235 HB 1040 – 1080 °C Oil, Air, Vacuum, Salt 61 – 63 HRc see tempering chart<br />
bath<br />
max. 250 HB 1040 – 1080 °C Oil, Air, Vacuum, Salt 61 – 64 HRc see tempering chart<br />
bath<br />
max. 280 HB 1030 – 1080 °C Oil, Vacuum 62 – 66 HRc see tempering chart<br />
K455<br />
K460<br />
K890<br />
max. 225 HB 870 – 900 °C Oil 58 – 62 HRc 60 59 56 53 – – –<br />
max. 220 HB 780 – 820 °C Oil, Salt bath 63 – 65 HRc 64 62 58 52 – – –<br />
(200 – 250 °C)<br />
max. 280 HB 1030 – 1180 °C Oil, Vacuum 58 – 64 HRc see tempering chart<br />
BÖHLER grade Hardness after Hardening Quenchant °C Tempering Obtainable<br />
annealing temperature °C temperature °C hardness HRc<br />
prehardened 290 – 330 HB or 311 – 354 HB (high hard)<br />
M238<br />
M261<br />
precipitation hardened 38 – 42 HRc<br />
M303<br />
prehardened 290 – 330 HB<br />
Plastic mould steels<br />
M310<br />
M315<br />
M333<br />
M340<br />
1)<br />
1)<br />
1)<br />
max. 200 HB 1000 – 1050 °C Gas, Salt bath, Oil 150 – 300 / 520 – 600 °C 50 – 54 HRc<br />
prehardened 276 – 319 HB<br />
max. 220 HB 1000 – 1030 °C Gas, Salt bath, Oil 150 – 300 / 520 – 600 °C 50 – 53 HRc<br />
max. 260 HB 980 – 1000 °C Gas, Salt bath, Oil 150 – 300 / 520 – 600 °C 53 – 58 HRc<br />
M390<br />
1)<br />
280 HB 1100 – 1180 °C Gas, Salt bath, Oil 150 – 300 / 520 – 600 °C 58 – 60 HRc<br />
M461<br />
precipitation hardened 38 – 42 HRc<br />
1) for certain applications sub zero treatment is recommended for dimensional stability
BÖHLER grade Red hardness Wear resistance Toughness Grindability Compressive<br />
strength<br />
S500<br />
S600<br />
High speed steels<br />
S705<br />
S290<br />
S390<br />
S590<br />
S690<br />
S790<br />
BÖHLER grade High-temperature High-temperature High-temperature Machinability<br />
strength toughness wear resistance<br />
W100<br />
Hot work tool steels<br />
W300<br />
W302<br />
W303<br />
W360<br />
W400<br />
W403<br />
BÖHLER grade Wear resistance Wear resistance Toughness Machinability Dimensional stability<br />
abrasive adhesive in heat treatment<br />
K100<br />
K105<br />
K107<br />
Cold work tool steels<br />
K110<br />
K245<br />
K340<br />
K360<br />
K390<br />
K455<br />
K460<br />
K890<br />
BÖHLER grade Polishability Corrosion Wear resistance Machinability Dimensional stability<br />
resistance<br />
during heat treatment<br />
Plastic mould steels<br />
M238<br />
M261<br />
M303<br />
M310<br />
M315<br />
M333<br />
M340<br />
n / a<br />
n / a<br />
n / a<br />
n / a<br />
M390<br />
M461<br />
n / a
SPECIALITIES<br />
Powder metallurgical steels<br />
FLOW OF MATERIAL<br />
Melting<br />
EAF 50t<br />
AOD<br />
Special materials subjected to vacuum refining or<br />
melting during at least one stage of manufacture.<br />
Secondary metallurgy<br />
VID<br />
Ladle furnace 1 VD Ladle furnace 2 VOD<br />
Plastic mould steels in ESR quality<br />
Cold work tool steels in ESR quality<br />
Casting<br />
BEST<br />
Ingot<br />
casting<br />
HCC<br />
~ 80%<br />
High speed steels in ESR quality<br />
Special Melting and<br />
Remelting<br />
VIM<br />
4 ESR 4 PESR 6 VAR<br />
Hot work tool steels in ESR quality with special<br />
heat treatment<br />
Gas<br />
Hot work tool steels in conventional quality with<br />
special heat treatment<br />
Hot Forming<br />
Induction<br />
Furnace<br />
Atomizing<br />
HIP<br />
FP RFM CM<br />
MLRM<br />
Special materials in ESR quality<br />
(excluding vacuum remelted)<br />
Special property and/or achievement characteristics<br />
Heat treatment,<br />
machining, testing<br />
PRODUCT RANGE<br />
Materials<br />
• High speed steels<br />
• Tool steels<br />
Cold work tool steels, Hot work tool steels,<br />
Plastic mould steels<br />
• Special materials<br />
Special constructional steels, Stainless steels,<br />
Creep resisting steels, Heat resisting steels, Valve<br />
steels, Steels with special physical properties,<br />
Steels for particular applications, Ni base alloys<br />
Products<br />
BAR STEEL rolled<br />
round: 12.5 – 150 mm<br />
square: 15 – 150 mm<br />
flat: width thickness<br />
15 – 60 mm 5 – 41 mm<br />
60 – 200 mm 5 – 86 mm<br />
100 – 300 mm 15 – 80 mm<br />
ROLLED WIRE<br />
rolled: dia. 5.0 – 13.5 mm<br />
drawn: dia. 1.0 – 12.0 mm<br />
precision shaped:<br />
round 1 – 28 mm Ø<br />
flat 0.5 – 40 mm 2<br />
BAR STEEL forged<br />
round, square: 90 – 1200 mm<br />
flat: width thickness<br />
100 50 mm minimum<br />
1600 1000 mm maximum<br />
Ratio width/thickness maximum 10:1<br />
BAR STEEL pre-machined<br />
IBO ECOMAX 12.5 – 315 mm<br />
(on request up to 900 mm)<br />
BRIGHT STEEL<br />
BRIGHT STEEL ground and polished<br />
ECOBLANK peeled and polished<br />
ECOFINISH band ground<br />
Surface finish: black<br />
(abrasive blasted); pickled; machined (turned,<br />
peeled, polished h 12 – h 9); ground – polished<br />
Forgings<br />
Open-die forgings of a gross weight of up to 45t:<br />
unmachined, premachined, machined ready for<br />
moun ting: drop forgings: machined. Machining<br />
of rolled, forged an cast components on state-ofthe-art<br />
machines.<br />
Industries<br />
aviation industry, turbine construction, toolmaking<br />
industry, general mechanical engineering, offshore<br />
industry, energy engineering, automotive industry,<br />
medical technology
Special materials<br />
Stainless chromium steels<br />
BÖHLER grade Standards<br />
EN / DIN AISI / ASTM *<br />
N114 ~ 1.4002 X7CrAl13 mod. - -<br />
Creep resisting and high temperature steels<br />
BÖHLER grade Standards<br />
EN / DIN AISI / ASTM *<br />
1)<br />
T200 < 1.4980 > X5NiCrTi26-15 660 *<br />
N400<br />
1)<br />
< 1.4313 > X4CrNi13-4 F6NM *<br />
T240<br />
1)<br />
~ 1.4962 X12CrNiWTi16-13 - -<br />
N545SA 3)<br />
N557<br />
N685<br />
N690<br />
N695<br />
1)<br />
1)<br />
1)<br />
~ 1.4116 X45CrMoV15 - -<br />
< 1.4122 > X35CrMo17 - -<br />
< 1.4112 > X90CrMoV18<br />
< 1.2361 > X91CrMoV18<br />
~ 440B<br />
< 1.4528 > X105CrCoMo18-2 - -<br />
< 1.4125 > X105CrMo17 440C<br />
T262<br />
T504<br />
T550<br />
T552<br />
1)<br />
2)<br />
1)<br />
2)<br />
1)<br />
1)<br />
< 1.4986 > X8CrNiMoBNb16-16 - -<br />
- - 422, 616<br />
< 1.4922 > X20CrMoV12-1 - -<br />
< 1.4923 > X22CrMoV12-1<br />
< 1.4926 > X21CrMoV12-1<br />
< 1.4938 > X11CrNiMo12 ~ XM32 *<br />
2)<br />
N700 < 1.4542 > X5CrNiCuNb16-4 630<br />
< 1.4548 > X5CrNiCuNb17-4-4<br />
1) also available in ISOEXTRA quality<br />
2) also available in conventional and VMR quality<br />
3) Special grade, please inquire<br />
Stainless chromium-nickel steels<br />
BÖHLER grade Standards<br />
EN / DIN ASTM / UNS *<br />
1)<br />
A903 < 1.4462 > X2CrNiMoN22-5-3 F51<br />
S31803 *<br />
1)<br />
A911SA < 1.4501 > X2CrNiMoCuWN25-7-4 S32760 *<br />
A926<br />
1)<br />
2)<br />
~ 1.4507 X2CrNiMoCuN25-6-3 - -<br />
1)<br />
A965SA < 1.4547 > X1CrNiMoCuN20-18-7 F44<br />
S31254 *<br />
1) also available in ISOEXTRA quality<br />
2) Special grade, please inquire<br />
Aircraft materials<br />
BÖHLER grade Standards<br />
EN / DIN AISI / ASTM* AMS AIR / AFNOR*<br />
1)<br />
V124SC 4) ~ 1.6565 - - 6414 - -<br />
V132<br />
V145<br />
V354<br />
V720<br />
V723<br />
V725<br />
N700<br />
N701<br />
N709<br />
A750<br />
T200<br />
T552<br />
1) also available in conventional and VMR quality<br />
2) also available in ISOEXTRA quality<br />
3) also available in EXTRA quality<br />
4) Special grade, please inquire<br />
4)<br />
2)<br />
2)<br />
4)<br />
4)<br />
2)<br />
2)<br />
4)<br />
2)<br />
4)<br />
3)<br />
3)<br />
~ 1.6928 300M * 6417 - -<br />
< 1.6604 > - - - - 30CND8 *<br />
< 1.7734 > - - - - 15CDV6<br />
< 1.7736 ><br />
< 1.6354 > Marage 300* 6514 ~ E-Z2NKD18<br />
< 1.6359 > ~ Marage 250* 6512 ~ E-Z2NKD18<br />
< 1.6356 > Marage 350* - - - -<br />
< 1.4548 > 630 * 5622 Z7CNU16-04*<br />
5643<br />
(17-4PH)<br />
< 1.4545 > XM12 * 5659<br />
(15-5PH)<br />
- -<br />
< 1.4534 > ~ XM13 * 5629 Z4CNDAT13-09*<br />
(PH13-8Mo)<br />
< 1.4546 > 347, 347H<br />
348, 348H<br />
5646 Z6CNNb18-10*<br />
< 1.4944 > 660 5731<br />
5732<br />
E-Z6NCT25<br />
< 1.4933 > ~ XM32 *<br />
< 1.4939 ><br />
5719 - -<br />
T651<br />
1)<br />
T655SC 1)<br />
T656<br />
T658<br />
T670<br />
T671<br />
D230<br />
1)<br />
2)<br />
1)<br />
2)<br />
1)<br />
1)<br />
2)<br />
2)<br />
< 1.4021 > X20Cr13 - -<br />
- - ~ 403<br />
- - (403Cb)<br />
< 1.4000 > X6Cr13 410S<br />
- - ~ XM25 *<br />
- - XM25 *<br />
< 1.7709 > 21CrMoV5-7 - -<br />
2)<br />
V344 < 1.7218 > 25CrMo4 ~ 4130, ~4130H<br />
< 1.7219 > 26CrMo4<br />
< 1.7258 > 24CrMo4<br />
1) also available in ISOEXTRA quality<br />
2) Special grade, please inquire<br />
Nickel-base alloys<br />
BÖHLER grade Standards<br />
EN / DIN<br />
UNS / ASTM* AMS<br />
L080A < 2.4631 > NiCr20TiAl HEV5 (SAE) - -<br />
< 2.4952 > NiCr20TiAl 80A *<br />
N07080<br />
1)<br />
L625 < 2.4856 > NiCr22Mo9Nb N06625 5666<br />
L718<br />
1) Special grade, please inquire<br />
1)<br />
< 2.4668 > NiCr19NbMo N07718 5662<br />
Valve steels<br />
BÖHLER grade Standards<br />
EN / DIN<br />
SAE<br />
H700 < 1.4718 > X45CrSi9-3 ~ HNV3<br />
1)<br />
H800 < 1.4873 > X45CrNiW18-9 - -<br />
H850 < 1.4871 > X53CrMnNiN21-9 EV8<br />
1)<br />
H854 < 1.4882 > X50CrMnNiNbN21-9 - -<br />
L306 < 2.4631 > NiCr20TiAl HEV5<br />
< 2.4952 > NiCr20TiAl<br />
1) Special grade, please inquire
Complementary program<br />
Case-hardening steels<br />
BÖHLER grade Standards<br />
EN / DIN<br />
SAE<br />
1)<br />
E110 < 1.6587 > 17CrNiMo6 - -<br />
1)<br />
E200 < 1.5752 > 14NiCr14 - -<br />
1)<br />
E220 < 1.5934 > LW - -<br />
< 1.5920 > 18CrNi8<br />
< 1.2722 > 19CrNi8<br />
1)<br />
E230 < 1.5924 > LW ~ 3215<br />
< 1.5919 > 15CrNi6<br />
1) Special grade, please inquire<br />
Heat treatable steels<br />
BÖHLER grade Standards<br />
EN / DIN<br />
AISI / SAE<br />
1)<br />
V155 < 1.6582 > 34CrNiMo6<br />
< 1.6583 > 35CrNiMo6<br />
- -<br />
1)<br />
V320 < 1.7223 > 41CrMo4<br />
< 1.7225 > 42CrMo4<br />
~ 4140<br />
~ 4140H<br />
1)<br />
V350 < 1.8514 > LW - -<br />
< 1.2307 > 29CrMoV9<br />
< 1.7707 > 30CrMoV9<br />
< 1.8519 > 31CrMoV9<br />
1) Special grade, please inquire<br />
Nitriding steels<br />
BÖHLER grade<br />
V350<br />
V820<br />
1) Special grade, please inquire<br />
1)<br />
Standards<br />
EN / DIN<br />
ASTM<br />
< 1.8514 > LW - -<br />
< 1.2307 > 29CrMoV9<br />
< 1.7707 > 30CrMoV9<br />
< 1.8519 > 31CrMoV9<br />
< 1.8550 > 34CrAlNi7 - -<br />
Comparison of BÖHLER grades with standard materials in order of greatest similarity. Deviations<br />
in chemical composition are indicated with ”~”. For < EN / DIN > the chemical composition<br />
of the BÖHLER grades is within the parameters of the standards.<br />
The principal difference between BÖHLER grades and standard materials is their considerably<br />
more limited tolerances in chemical composition, and therefore their improved and reproducible<br />
applicational properties.<br />
Stainless chromium steels<br />
BÖHLER grade Standards<br />
EN / DIN<br />
AISI<br />
1)<br />
N100 < 1.4006 > X12Cr13 403, 410<br />
1)<br />
N200 < 1.4016 > X6Cr17 430<br />
N310 < 1.4104 > X14CrMoS17 ~ 430F<br />
1)<br />
N320 < 1.4014 > LW ~ 420<br />
< 1.4021 > X20Cr13<br />
~ 1.2082 X21Cr13<br />
1)<br />
N335 < 1.4122 > X39CrMo17-1 - -<br />
1)<br />
N350 < 1.4057 > X17CrNi16-2<br />
< 1.2787 > X23CrNi17<br />
431<br />
N540 < 1.3541 > X45Cr13<br />
< 1.4034 > X46Cr13<br />
420<br />
1) Special grade, please inquire<br />
Stainless chromium-nickel steels<br />
BÖHLER grade Standards<br />
EN / DIN<br />
AISI<br />
1)<br />
A120 < 1.4401 > X5CrNiMo17-12-2 316<br />
1)<br />
A200 < 1.4404 > X2CrNiMo17-12-2 316L<br />
A300 < 1.4571 > X6CrNiMoTi17-12-2 316Ti<br />
1)<br />
A500 < 1.4314 > LW 304<br />
< 1.4301 > X5CrNi18-10<br />
< 1.3958 > X5CrNi18-11<br />
1)<br />
A506 < 1.4305 > X8CrNiS18-9 303<br />
1)<br />
A600 < 1.4306 > X2CrNi19-11 304L<br />
A700 < 1.4544 > LW 321, ~ 321H<br />
< 1.4878 > X12CrNiTi18-9<br />
< 1.4541 > X6CrNiTi18-10<br />
1)<br />
A750 < 1.4546 > X5CrNiNb18-10<br />
< 1.4550 > X6CrNiNb18-10<br />
347, 347H<br />
348, 348H<br />
1) Special grade, please inquire<br />
Heat resisting steels<br />
BÖHLER grade Standards<br />
EN / DIN<br />
ASTM<br />
1)<br />
H100 < 1.4762 > X10CrAl24 - -<br />
1)<br />
H160 < 1.4713 > X10CrAl7 - -<br />
1)<br />
H304 ~ 1.4821 X20CrNiSi25-4 ~ 327<br />
1)<br />
H520 ~ 1.4864<br />
~ 1.2786<br />
X12NiCrSi36-16<br />
X13NiCrSi36-16<br />
~ 30330<br />
H525 < 1.4841 > X15CrNiSi25-20<br />
~ 1.2782 X16CrNiSi25-20<br />
314<br />
1)<br />
H532 ~ 1.4841 X15CrNiSi25-20 310S, ~ 310<br />
1)<br />
H550 < 1.4828 > X15CrNiSi20-12<br />
~ 1.2780 X16CrNiSi20-12<br />
~ 305, ~ 308<br />
A700 < 1.4544 > LW 321, ~ 321H<br />
< 1.4541 > X6CrNiTi18-10<br />
< 1.4878 > X12CrNiTi18-9<br />
1) Special grade, please inquire
BÖHLER <strong>Nederland</strong><br />
Isolatorweg 30-32<br />
1014 AS Amsterdam<br />
Phone: +31(0)20-5817400<br />
Fax: +31(0)20-5817450<br />
E-mail: info@bohler.nl<br />
www.bohler.nl<br />
BÖHLER <strong>Bel</strong>gië<br />
Europark Oost 7<br />
B-9100 Sint-Niklaas<br />
Phone: +32(0)3 780 56 10<br />
Fax: +32(0)3 780 56 19<br />
E-mail: info@bohler.be<br />
www.bohler.be