Welding Inspection & Metallurgy API ICP Self Study Notes

More documents

Recommendations

Info

Pearlite Pearlite is a phase mixture consisting of alternating platelets of ferrite and cementite (α+ Fe 3 C), which grows by conversion from austenite. A steel containing 0.77 wt% carbon can consist solely of pearlite if cooled sufficiently slowly from austenite (see figure 1). Under the microscope it can have an iridescent mother of pearl appearance, hence the name.
Page 1 and 2:
Welding Inspection & Metallurgy API
Page 3 and 4:
Content: 10 METALLURGY 10.1 General
Page 5 and 6:
10.2 THE STRUCTURE OF METALS AND AL
Page 8 and 9:
http://www.sv.vt.edu/classes/MSE209
Page 10 and 11:
Phase Diagram http://www.azom.com/a
Page 12 and 13:
10.2.1 The Structure of Castings Th
Page 14 and 15:
HAZ- Heat Affected Zone
Page 16 and 17:
HAZ http://www.oocities.org/ferrit
Page 18 and 19:
1mm / 1mm 0.2mm 0.2+1+1= 2.2 mm API
Page 20 and 21:
Steel & Alloy- Grains
Page 22 and 23:
Steel & Alloy- Microvoid Coalescenc
Page 24 and 25:
Minimizing trace elements or “inc
Page 26 and 27:
Casting
Page 28 and 29:
Discussion: Why Wrought products ar
Page 30 and 31:
Wrought materials may consist of on
Page 32:
Hypoeutectic Steel - Annealed
Page 36 and 37:
Steel & Alloy- Annealed Pearlite
Page 38 and 39:
1055 Steel Annealed 1055, used in s
Page 40 and 41:
4140 Steel http://en.wikipedia.org/
Page 42 and 43:
4140 Steel Q&T
Page 44 and 45:
The metallurgy of each weld area is
Page 46 and 47:
Dendritic - usually solidify in the
Page 48 and 49:
Dendrite- usually solidify in the s
Page 50 and 51:
Weld Macro- CS
Page 52 and 53:
The heat-affected zone (HAZ) is adj
Page 54 and 55:
http://www.twi-global.com/technical
Page 56 and 57:
Overlay Welding
Page 58 and 59:
The third component in a welded joi
Page 60 and 61:
An important factor in selecting sh
Page 62 and 63:
10.3.1 Melting Temperature The melt
Page 64 and 65:
Phase Diagram
Page 66 and 67:
Phase Diagram http://www.calphad.co
Page 69 and 70:
10.3.3 Electrical Conductivity The
Page 71 and 72:
Aluminum Welds
Page 73:
Metals with a high coefficient of t
Page 76 and 77:
Weld porosity
Page 78 and 79:
A gas with a higher density is more
Page 80 and 81:
Tensile testing - Tensile /Yield St
Page 82 and 83:
Page 84 and 85:
Page 86 and 87:
Charpy Testing Samples
Page 88 and 89:
Charpy impact testing
Page 90 and 91:
Hardness testing- Hardness tester
Page 92 and 93:
Hardness testing
Page 94 and 95:
Hardness testing
Page 96 and 97:
Ductility- Bend Tests
Page 98 and 99:
10.4.1 Tensile and Yield Strength T
Page 100 and 101:
For design purposes, the maximum us
Page 102 and 103:
Note 1 A= proportional limit, B=ela
Page 104:
Tensile Testing
Page 107 and 108:
Actual tensile testing plot Elastic
Page 109 and 110: Elongation is the increase in gage
Page 111 and 112: The design of items should be based
Page 113: Bend Testing
Page 117 and 118: ASTM E290- Guided bend testing
Page 119 and 120: Bend Testing
Page 121 and 122: Bend Testing
Page 123 and 124: Knoop and Vickers Hardness Tester
Page 125 and 126: http://wes.ir/files/6936303material
Page 129: Rockwell hardness testing differs f
Page 132 and 133: Vickers hardness testing follows th
Page 135 and 136: http://www.twi-global.com/technical
Page 137: The type of notch and the impact te
Page 141 and 142: Online Metallurgy Course: http://ww
Page 143 and 144: Online Metallurgy Course http://210
Page 145 and 146: Online Metallurgy Course-Steel Maki
Page 147 and 148: Steels - The Structure of Engineeri
Page 149 and 150: Steels - The Structure of Engineeri
Page 151 and 152: Crystal Structures
Page 154 and 155: Phase Diagram
Page 156 and 157: Austenite
Page 158 and 159: This is a hypereutectoid alloy and
Page 162 and 163: Low carbon steel with a microstruct
Page 164 and 165: Figure 1. Part of the equilibrium d
Page 166 and 167: Martensite Martensite is commonly f
Page 168 and 169: Martensite https://www.flickr.com/s
Page 170 and 171: The strain energy involved in the m
Page 172 and 173: Figure 1. Part of the equilibrium d
Page 174 and 175: Bainite https://www.flickr.com/phot
Page 176 and 177: Proof Stress Re0.2% Since it is dif
Page 178 and 179: STEEL Steel is an alloy of iron, wi
Page 180 and 181: Aluminum Cables
Page 182 and 183: 10.5 PREHEATING
Page 184 and 185: Preheating
Page 186 and 187: Preheating
Page 188 and 189: • Bring temperature up to preheat
Page 190 and 191: Preheat can be applied using severa
Page 192 and 193: The temperature of PWHT is selected
Page 194 and 195: Discussion: However there may also
Page 196 and 197: Typical PWHT Chart Insertion temper
Page 198 and 199: PWHT Chart
Page 200 and 201: PWHT
Page 210 and 211:
PWHT
Page 212 and 213:
PWHT- Local
Page 214 and 215:
PWHT- Local
Page 216 and 217:
PWHT- Local
Page 218 and 219:
PWHT- Local
Page 220 and 221:
PWHT- Equipments
Page 222 and 223:
PWHT- Equipments
Page 224 and 225:
PWHT- Equipments
Page 226 and 227:
PWHT- Equipments
Page 228 and 229:
Fun-Photo: Induction Bending Pipe b
Page 230 and 231:
Fun-Photo: Induction Bending Pipe b
Page 232 and 233:
Other factors can also affect harde
Page 234 and 235:
http://www.azom.com/article.aspx?Ar
Page 237 and 238:
Welding variables, such as heat inp
Page 239 and 240:
Welding- Plate thickness & Weld Geo
Page 241 and 242:
Weld Macro- Geometry
Page 243 and 244:
Page 245 and 246:
Page 247 and 248:
The simplest means to determine har
Page 249 and 250:
Jominy Bar
Page 251 and 252:
Jominy Bar
Page 253 and 254:
It may be important for the welding
Page 255 and 256:
Typical Hardness Values Table 11—
Page 257 and 258:
HIC
Page 259 and 260:
HIC- Hydrogen Induced Cracking
Page 261 and 262:
TTT Curve
Page 263 and 264:
Martensite
Page 265 and 266:
10.8 MATERIAL TEST REPORTS Material
Page 267 and 268:
Billets/Ingots
Page 269 and 270:
Billets/Ingots
Page 271 and 272:
Billets/Ingots
Page 273 and 274:
Billets/Ingots
Page 275 and 276:
Billets/Ingots
Page 277 and 278:
Billets/Ingots
Page 279 and 280:
Product analysis- Pipe
Page 281 and 282:
For the purposes of this publicatio
Page 283 and 284:
Ductile to brittle transition tempe
Page 285 and 286:
Fracture toughness
Page 287 and 288:
Charpy impact testing
Page 289 and 290:
Elevated mechanical property testin
Page 291 and 292:
Further Reading
Page 293 and 294:
Quiz 1) See the figure below for po
Page 295 and 296:
c) 50% coarse pearlite + 25% bainit
Page 297 and 298:
10.9 WELDABILITY OF STEELS
Page 299 and 300:
Weldability is related to many fact
Page 301 and 302:
The addition of carbon generally ma
Page 303 and 304:
Typically, ■ ■ ■ Steels with
Page 305 and 306:
The simplest weldability tests are
Page 307 and 308:
Weldability Test- Cruciform testing
Page 309 and 310:
Another approach to measuring susce
Page 311 and 312:
10.10 WELDABILITY OF HIGH-ALLOYS Th
Page 313 and 314:
Hot Shortness: • solidification c
Page 315 and 316:
Ferrite Meter
Page 318 and 319:
Coefficients of Linear Thermal Expa
Page 320 and 321:
Sensitized Austenitic SS Common to
Page 322 and 323:
Weld Decay http://www.corrosionclin
Page 324 and 325:
Inert Backing Gas
Page 326 and 327:
Inert Backing Gas
Page 328 and 329:
Inert Backing Gas
Page 330:
Inert Backing Gas http://www.foodpr
Page 333 and 334:
Inert Backing Gas
Page 335 and 336:
Inert Backing Gas http://www.juncti
Page 337 and 338:
Inert Backing Gas
Page 339 and 340:
Inert Backing Gas
Page 341 and 342:
One of the main differences between
Page 343 and 344:
Sluggish tendency- LOF
Page 345 and 346:
Wider Bevel Angle & Thinner Root Fa
Page 347 and 348:
Nickel Welding: The faster a nickel
Page 349 and 350:
Content: 11 REFINERY AND PETROCHEMI
Page 351 and 352:
11.2 HOT TAPPING AND IN-SERVICE WEL
Page 353 and 354:
Hot Tapping
Page 355 and 356:
Hot Tapping
Page 357 and 358:
Hot Tapping
Page 359 and 360:
Hot Tapping
Page 361 and 362:
Hot Tapping
Page 363 and 364:
Burn Through
Page 365 and 366:
11.2.1 Electrode Considerations Hot
Page 367 and 368:
Cellulosic type electrodes (e.g., E
Page 369 and 370:
If the normal flow of liquids excee
Page 371 and 372:
Points to consider: Is it 36” or
Page 373 and 374:
Case Study: 1. Is it 36” or great
Page 375 and 376:
Case Study: Is it 36” or greater
Page 377 and 378:
Page 379 and 380:
Page 381 and 382:
Page 383 and 384:
11.2.3 Other Considerations To avoi
Page 386 and 387:
11.2.4 Inspection Inspection tasks
Page 388 and 389:
GMAW-S LOF
Page 390 and 391:
Due to this inherent nature of the
Page 392 and 393:
The quick freeze characteristic, wh
Page 394 and 395:
Hazards
Page 396 and 397:
Mechanical Integrity
Page 398 and 399:
Happy Inspectors
Page 400:
ICP Status http://myicp.api.org/Dir
show all

Welding Inspection & Metallurgy API ICP Self Study Notes