OK Flux 10.87 – High speed<br />
flux with perfect wetting<br />
OK Flux 10.87 is an<br />
agglomerated, low-basicity flux<br />
for submerged arc welding. It<br />
gives perfect wetting and<br />
excellent weld bead<br />
appearance in butt, overlap<br />
and fillet welds at high welding<br />
speeds.<br />
OK Flux 10.87 is used for<br />
single and multi-wire<br />
procedures and works equally<br />
well on DC and AC current. It is<br />
intended for a limited number<br />
of passes and plate thickness<br />
up to 25mm.<br />
The main application area for<br />
OK Flux 10.87 is in the<br />
production of air compressor<br />
tanks, LPG bottles and fire<br />
extinguishers. A flat weld bead<br />
and smooth, clean surface with<br />
excellent slag detachability is<br />
achieved, also when the<br />
second run has been preheated<br />
by the first run. Other<br />
industries with similar<br />
requirements also make use of<br />
OK Flux 10.87, including<br />
general construction and the<br />
automotive industry.<br />
Classification flux Basicity index Density Grain size<br />
EN 760: SA AR 1 95 AC 0.4 ~ 1.2 kg/dm3 0.2 - 1.6 mm<br />
Slag type Polarity Alloy transfer<br />
Aluminate-rutile DC+ / AC Very high Si alloying, neutral on Mn<br />
Flux consumption<br />
kg flux / kg wire<br />
Voltage DC+ AC<br />
26 0.6 0.5<br />
30 0.9 0.7<br />
34 1.2 1.0<br />
38 1.5 1.3<br />
Classification<br />
1,0<br />
0,8<br />
0,6<br />
0,4<br />
0,2<br />
0,0<br />
% Si pick-up<br />
from flux<br />
450 A<br />
750 A<br />
% Si in wire<br />
-0,2<br />
0,05 0,10 0,15 0,20 0,25 0,30<br />
Single wire, ø 4.0 mm, DC+, 30 V, 60 cm/min<br />
1,8<br />
1,4<br />
1,0<br />
0,6<br />
0,2<br />
-0,2<br />
-0,6<br />
-1,0<br />
% Mn pick-up<br />
from flux<br />
450 A<br />
750 A<br />
% Mn in wire<br />
0,5 1,0 1,5 2,0<br />
Wire<br />
Weld metal<br />
OK Autrod EN / AWS EN / AW AWS / AW AWS / PWHT<br />
12.10 S1 / EL12 S 35 A AR S1 A5.17: F6AZ-EL12 A5.17: F6PZ-EL12<br />
12.20 S2 / EM12 S 42 A AR S2 A5.17: F7AZ-EM12 A5.17: F6PZ-EM12<br />
12.22 S2Si / EM12K S 42 A AR S2Si A5.17: F7AZ-EM12K A5.17: F6PZ-EM12K<br />
Typical weld metal chemical composition (%), DC+<br />
C Si Mn Cr Ni Mo Other<br />
With OK Autrod<br />
12.10 0.05 0.8 0.6<br />
12.20 0.05 0.8 1.0<br />
12.22 0.05 0.9 1.0<br />
Typical weld metal mechanical properties, DC+<br />
ReL / Rp0.2<br />
(MPa)<br />
Rm<br />
(MPa)<br />
A4 / A5<br />
(%)<br />
CVN<br />
(J at °C)<br />
With OK Autrod +20 0<br />
12.10 370 470 25 50 25 AW<br />
12.20 410 500 25 50 25 AW<br />
12.22 420 510 25 50 25 AW<br />
12.10 345 445 25 50 25 SR<br />
12.20 360 480 25 50 25 SR<br />
12.22 400 490 25 50 25 SR<br />
AW/<br />
SR<br />
For more information view the Product Data Sheets or contact ESAB.<br />