OptiBond XTR SS_E.qxp - Kerr

OptiBond XTR SS_E.qxp 25.2.2011 10:32 Pagina 1
Order Information
35121 OptiBond XTR Unidose Kit 18 ml
Kit Contains: 50 x Unidose Self-Etching Primer (0.18 ml each),
50 x Unidose Universal Adhesive (0.18 ml each),
100 Applicators, Directions for Use, 1 Technique Guide.
35122 OptiBond XTR Bottle Kit 10 ml
Kit Contains: 1 Bottle Self-Etching Primer (5 ml),
1 Bottle Universal Adhesive (5 ml),
100 Applicators and 25 Four-Cavity Mixing Wells,
Directions for Use and 1 Technique Guide.
Easy Application Technique
One protocol for both direct and indirect procedure, no additional steps are necessary.
1 2
20 SEC 5SEC
15 SEC 5 SEC 10 SEC
Your practice is our inspiration.
OptiBond XTR
Self-Etch, Light-Cure Universal Adhesive System
35123 OptiBond XTR Primer Refill 5 ml
1 x Self-Etching Primer (5 ml) and Directions for Use.
35124 OptiBond XTR Adhesive Refill 5 ml
1 x Universal Adhesive (5 ml) and Directions for Use.
1. Apply OptiBond XTR
PRIMER to enamel/dentin
using scrubbing motion.
2. Air thin with medium
air pressure.
3. Shake OptiBond XTR
ADHESIVE briefly. Apply to
enamel/dentin surface using
light brushing motion.
4. Air thin with medium air
pressure and then strong
air for at least 5 seconds.
5. Light cure.
Case courtesy of Dr. Joseph Sabbagh
Desired shiny surface of cured adhesive
layer after application.
Indirect Restoration Surface Preparation
OptiBond TM XTR
Unmatched power for all your direct and indirect restorations
1. Ceramic/porcelain
restoration.
1. Metal and Zirconia
restoration.
2. Etch with hydrofluoric
acid etchant.
60 psi
15 psi
3. Apply XTR adhesive,
air thin and light cure.
2. Sandblast. 3. Apply XTR adhesive,
air thin and light cure.
Ready for cementation
OptiBond XTR Adhesive is applied
directly on the surface of indirect
restoration and light cured.
No additional primer for porcelain,
metal or zirconia is needed.
Application of OptiBond XTR
Adhesive directly onto ceramic
crown.
Application of OptiBond XTR
Adhesive on zirconia abutment.
Outstanding bond strengths to dentin and enamel.
Extraordinary performance for long-lasting restorations, enhanced
marginal integrity, and reduced microleakage.
Self-etch.
Minimizes post-operative sensitivity, maximizes patient comfort.
Direct and indirect restorations.
A true universal adhesive – eliminates the need for multiple
bonding agents.
Proven OptiBond Technology.
Dependable clinical performance and reliability.
1. Composite
restoration.
2. Sandblast. 3. Apply XTR adhesive,
air thin and light cure.
Adper EasyBond, Clearfil SE, Xeno IV, Calibra, Variolink II, RelyX ARC, Fluorocore 2, Core Paste XP, Build-It, Absolute Dentine,
LuxaCore and Multilink Automix trademarks are properties of their respective owners.
KerrHawe SA Via Strecce 4, P.O. Box 272, 6934 Bioggio, Switzerland Freephone: 00800 41 05 05 05 Fax: ++41 91 610 05 14 www.kerrdental.eu
Your practice is our inspiration.
Universal compatibility.
Enables use with all resin cements, light-cured or self-cured
core build-up materials and dental substrates.
P49000 E

OptiBond XTR SS_E.qxp 25.2.2011 10:32 Pagina 2
OptiBond XTR
Predictable. Reliable. Extraordinary.
Universal Solutions by OptiBond XTR
Low Film Thickness
OptiBond XTR stands apart as the only bonding agent that embodies both
the power and durability of a total-etch adhesive and the simplified protocol
of a self-etch technique. Universal compatibility enables use for all direct and
indirect restorations. The unique chemistry of an enhanced self-etch primer
and optimized adhesive in this 2-bottle system brings outstanding bond
strengths to uncut enamel and dentin.
Inspired by:
Is it even possible –
a self-etch adhesive with
the strength of a total-etch?
It is. And Kerr has made it happen.
- Dr. Marc Geissberger
Tthe uniqueness of OptiBond XTR stands in universal solutions it offers.
OptiBond XTR was designed to accommodate different needs for various
indications and different application techniques.
5µm
Low film thickness of OptiBond XTR is advantage for
indirect restorations placement.
Research
OptiBond XTR employs Kerr’s well-proven GPDM technology, ternary
solvent system, filled adhesive and optimized formulation to produce
outstanding adhesion for direct and indirect procedures.
• Independent testing demonstrates statistically superior enamel and
dentin bond strength.
• Enhanced primer provides superior self-etching power on enamel
and exceptional penetration into dentin.
• Optimized adhesive offers efficient polymerization and increased
hydrophobicity to boost mechanical strength, bond durability, and
marginal integrity.
Microshear Bond Strength
(MPa)
40
30
20
10
0
Bond Strength Data on Dentine and Enamel
39.0
24.7
OptiBond TM XTR
31.5
23.0
Adper TM Easy Bond
35.2
Study conducted by Prof. Lorenzo Breschi, University of Trieste. Data available upon request.
Dentine
Cut Enamel
25.3
OptiBond TM Solo Plus
Effective Enamel Etching
OptiBond XTR
Magnification at 50,000x. Kerr R&D.
Well defined hybrid layer
Clear, long resin tags with penetration into lateral
dentin tubule branches (2,000x).
Leading 6 th Generation
Bonding Agent
Magnification at 50,000x. Kerr R&D.
XTR Penetration into
lateral tubule branches.
Direct Applications
• Self-etch technology assures increased adhesion to dentine and reduced
post-operative sensitivity.
• Enhanced bond strength to cut and uncut enamel.
Shear Bond Strength
(MPa)
50
40
30
20
10
0
40.4 41.0 40.4
33.0
OptiBond TM
XTR
Comparative Bond Strength Data
on Cut and Uncut Enamel
OptiBond FL
33.2
28.6
ClearFil ® SE
Bond
Study Conducted at University of North Carolina, Department of Operative Dentistry.
Data available upon request.
18.1
Cut Enamel
Uncut Enamel
26.8
Xeno ® IV
Indirect Applications
• Universal compatibility with resin cements assures high bond strength
to dentine and enamel when used with various resin cements.
Shear Bond Strength
on Dentine (MPa)
50
40
30
20
10
0
29.7
Calibra ®
OptiBond XTR in combination
with various resin cements
23.9
Variolink ® II
41.7
29.9
RelyX ARC NX3
• Exceptional bond strength results with light-cured or self-cured core
build-up materials, thanks to the universal compatibility of OptiBond XTR.
Shear Bond Strength
on Dentine (MPa)
50
40
30
20
10
0
26.0
Fluorcore 2
OptiBond XTR in combination
with various core build-up materials
26.3
Core Paste XP
35.7
Build-it ®
36.4
Absolute
Dentin
37.4
LuxaCore ®
41.7
NX3
Kerr internal data. Available upon request.
Kerr internal data. Available upon request.
• OptiBond XTR in combination with NX3 gives great
variability for light cure as well as total dark cure mode
use depending on clinical needs.
Shear Bond Strength
(MPa)
Shear bond strength of tested
adhesive/cement systems in total dark
cure mode*
30
20
10
0
OptiBond XTR
NX3 Dual-Cure
Study conducted by Dr. Carlos Munoz, University of Buffalo.
Data available upon request.
29
26.6
Primer A + Primer B
Multilink ® Automix
* The adhesive as well as cement were not light cured, self-cure mode only.
www.kerrdental.eu/optibondxtr
Your practice is our inspiration.