94 2 0 1 1 - 2 0 1 2 T E C H N I C A L P R O D U C T S Ceramic Alloys ALLOYS Indication Inlays, onlays, partial crowns, single crowns, telescope and conus crowns, PFM crowns, posts, short and long span bridges, implant superstructures Indication Inlays, onlays, partial crowns, single crowns, telescope and conus crowns, PFM crowns, posts, short and long span bridges Indication Inlays, onlays, partial crowns, single crowns, telescope and conus crowns, PFM crowns, posts, short and long span bridges, implant superstructures, partial dentures Indication Inlays, onlays, partial crowns, single crowns, telescope and conus crowns, PFM crowns, posts, short and long span bridges, implant superstructures, partial dentures Indication Inlays, onlays, partial crowns, single crowns, telescope and conus crowns, PFM crowns, posts, short and long span bridges, implant superstructures, partial dentures Indication Single crowns, telescope and conus crowns, PFM crowns, posts, short and long span bridges Casting Temp (°C)
P H O N E O R D E R S : 8 0 0 - 5 3 3 - 6 8 2 5 F A X O R D E R S : 8 0 0 - 5 9 8 - 4 5 6 9 95 Ceramic Alloys CALLISTO ® 75 PD Copper-free Noble ceramic alloy with exceptional melting, casting, and polishing characteristics for pressing and layering techniques. Indication Inlays, onlays, partial crowns, single crowns, telescope and conus crowns, PFM crowns, posts, short and long span bridges, implant superstructures, partial dentures Advantages •Over 85% precious metal content, yet still highly economical - 2.5% Gold, 75.2% Palladium, and a low density of 10.8 •Copper free noble alloy for optimized oxidation, finishing, and polishing - Lighter oxide color and toughest bond strength •Unique, low CTE range significantly reduces processing time - No long term cooling required •Ideal for all layering and pressing porcelains - Seamless integration for optimum performance and esthetic results •Excellent melting and casting characteristics - Easy processing, fewer remakes, lower fabrication cost INDICATIONS Inlays and onlays, 3/4 crowns, crowns, telescope and conus crowns, PFM crowns,posts, short and long span bridges, implant superstructure partial dentures. Technical Data Color White Density (g/cm3) 10.8 Melting range (°F) 2066 – 2365 Melting range (°C) 1130 – 1296 Elongation (%) 40.0 Vickers Hardness 230 Pre-Solder: HGPKF 1030 Y, HGPKF 1015 Y Post-Solder: LFWG Laser Welding: Laser Ceramic White ALLOYS ALLOYS CALLISTO ® IMPLANT 33 Low density, reduced-gold ceramic alloy with physical properties to support a wide range of indications. CALLISTO ® IMPLANT 60 Economical, Palladium-based ceramic alloy designed especially for implant superstructures. Advantages • Inexpensive, reduced-gold alloy with a low density for increased economic efficiency • Wide indication range, particularly suitable for implant superstructures Technical Data Color White • Excellent physical properties: particularly high strengths values, especially for long-span Density (g/cm3) 12.6 restorations Melting range (°F) 2040 – 2380 • Convenient handling and polishing properties Melting range (°C) 1115 – 1305 Elongation (%) 35.0 INDICATIONS Vickers Hardness 235 Inlays, Onlays, ¾ crowns, crowns, ceramic crowns, PFM crowns, Telescopic- and conus crowns, posts, short- and long-span bridges, partial dentures, implant superstructures Pre-Solder: HGPKF 1030 Y Post-Solder: LFWG, .585 Fine Solder Laser Welding: Laser Ceramic White Advantages • High stability • Economical due to low density • High corrosion resistance • Excellent milling properties • Low melting range INDICATIONS Onlays, 3/4 crowns, crowns, telescope and conus crowns, PFM crowns,posts, short and long span bridges, implant superstructure partial dentures. Technical Data Type 4 Colour White Density (g/cm³) 10.8 Melting range (°C) 1100–1260 Melting range (°F) CTE 25 – 500 °C 14.5 CTE 20 – 600 °C 14.8 Elongation (%) 19.0 Modulus of elasticity (MPa) 130,000 Vickers hardness 275 0.2% proof stress (MPa) 610 Pre-Solder: HGPKF 1030 Y Post-Solder: .650, .615, .585 Fine Solder Laser Welding: Laser Ceramic Yellow PdF CALLISTO ® IMPLANT 78 Silver and Copper-free high-gold impant alloy featuring excellent strength and casting properties. COLADO ® CC Economical, Cobalt-Chromium alternative to precious alloys specifically for ceramic and composite veneers. Advantages • Ag- and Cu-free • 96% precious metal content • Very high strength • Excellent casting and flow properties • Even grain size distribution (16–25 µm) INDICATIONS Onlays, Partial crowns, Single crowns, Telescope and conus crowns, PFM crowns, Root canal posts, Short- and long-span bridges, Implant superstructures, Model casts, partial dentures Technical Data Type 4 Colour White Density (g/cm³) 17.6 Melting range (°C) 1135–1250 Melting range (°F) CTE 25 – 500 °C 13.9 CTE 20 – 600 °C 14.0 Elongation (%) 5.0 Modulus of elasticity (MPa) 110.000 Vickers hardness 240 0.2% proof stress (MPa) 600 Advantages • Wide range of indications, especially suitable for implant superstructures and the press technique • Outstanding bonding strength with Technical Data Color White veneering materials (ceramics and composites) Density (g/cm3) 8.5 • Excellent melting and casting properties for a Melting range (°F) 2147 – 2525 F homogeneous microstructure • Convenient handling and polishing properties Melting range (°C) 1175 – 1385 C • Tested and certified biocompatibility (high Elongation (%) 9.0 corrosion resistance) Vickers Hardness 340 • Coordinated compatibility with the Ivoclar Vivadent product system INDICATIONS Crowns, Telescope and conus crowns, partial crowns, Partial crowns, Posts, Short- and long-span bridges, Implant superstructures, Partial dentures Pre-Solder: SHFWC Solder Post-Solder: LFWG Laser Welding: Laser Ceramic White Pre-Solder: HGPKF 1030 Y, Post-Solder: .650, .585 Fine Solder Laser Welding: Laser Ceramic Yellow PdF
Change language