TABLE 6.6. RESULTS OF STATIC TESTS OF BRAZED A-NICKEL T-JOINTS IN<br />
NaF-ZrF4-UF4 (53.5-40-6.5 mole X) AT 150OoF FOR 100 hr<br />
Brazing Alloy Weight Weight<br />
Corn pas it i on Change Change Metal lographic Notes<br />
(wt %) (9) (%)<br />
69 Ni-20 Cr-11 Si -0.0017 -0.055<br />
100 cu -0.0006 -0.019<br />
82 Au-18 Ni -0.001 -0.036<br />
80 Au-20 Cu<br />
90 Ni-10 P -0.0004 -<br />
60 Pd-40 Ni -0.0016 -<br />
60 Pd-37 Ni-3 Si + 0.0008 + 0.027<br />
Surface attack to a depth of 16 mils along entire braze fillet<br />
Surface attack to a depth of 0.5 mil along entire braze fillet<br />
Braze fillet appeared to be unattacked<br />
No attack on braze fillet surface<br />
No attack on braze fillet surface<br />
No attack on braze fillet surface<br />
No attack on braze fillet surface<br />
TABLE 6.7. RESULTS OF STATIC TESTS OF BRAZED A-NICKEL T-JOINTS IN<br />
SODIUM HYDROXIDE FOR 100 hr AT 1100 AND 150OoF<br />
4 Brazing Allay Weight Weight Test<br />
%- Composition Change Change Temperature Metallographic Notes<br />
- * (wt %) (9) (%I (OF)<br />
t-<br />
+3<br />
d<br />
- . t<br />
69 Ni-20 Cr-11 Si 1500 Braze failed completely<br />
+ 0.0024 + 0.093 1100 Braze ottacked completely<br />
100 cu - .0.0118 -0.408 1500 Braze attacked completely; large voids appear<br />
throughout<br />
-0.001 1 -0.038 1100 Uniform surface attack on braze to a deDth of 3 mils<br />
82 Au-18 Ni -0.00.4 -0.144 1500 Nonuniform surface attack on braze to depth of 1 mil<br />
-0.0007 -0.022 1100 No attack on surface of braze<br />
60 Pd-3 of 6 mills<br />
J<br />
83