WOOD AND WOOD-BASED MATERIALS – PRODUCT OVERVIEW<br />
vINNApAS ®<br />
VINNAPAS ® Product Technical Data 1 Stabilization System Performance Attributes<br />
Grade Polymer Solids content Viscosity pH value Glass transition Protective Product benefit Water Heat Wood Setting Wood<br />
VINNAPAS ® Products PVAc Technology<br />
base 1 ± 1% (DIN EN Brookfield (ISO 976) temperature colloid / resistance resistance discolor- behavior to foil<br />
ISO 3251) RVT at 23 °C Tg (DSC) emulsifier (D2, D3, D4) (WATT91 / ation lamination<br />
(residue after 20 rpm (ISO approx. [˚C] system 2,3 DIN EN<br />
drying) [%] 2555) [mPa·s] 14257)<br />
VINNAPAS ® DP 500 VAc 50 ± 2 35,000 ± 5,000 4.5 – 5.5 33 PVOH Very low sedimentation D2 • • no • • • •<br />
VINNAPAS ® DP 600 VAc 60 ± 2 35,000 ± 6,000 4.0 – 5.5 33 PVOH Very low sedimentation D2 • • no • • • •<br />
VINNAPAS ® H 65 VAc 65 30,000 ± 10,000 4.0 – 5.0 40 PVOH High setting speed, edge lamination D2 • • no • • • • •<br />
VINNAPAS ® DPX 271 VAc 46 ± 2 approx. 10,000 approx. 5.0 30 PVOH Ultra low formaldehyde D3 1K, discoloration-free D3 • • no • • • n.a.<br />
VINNAPAS ® DPN 15 VAc 52 15,000 ± 3,000 2.5 – 3.5 28 PVOH All-around D3 1K binder D3 • • • yes • • • n.a.<br />
VINNAPAS ® DPN 16 VAc 52 ± 2 12,000 ± 2,000 2.5 – 3.5 28 PVOH All-around D3 1K binder, reduced discoloration D3 • • • reduced • • • n.a.<br />
VINNAPAS ® DPN 17 VAc 48 11,000 ± 2,000 2.5 – 3.5 28 PVOH All-around D3 1K binder, longer open time D3 • • • yes • • • n.a.<br />
VINNAPAS ® DPN 47 VAc 50 ± 2 18,000 ± 4,000 4.5 – 5.5 19 PVOH D4 2K binder D4 • • • yes • • • n.a.<br />
VINNAPAS ® Products VAE Technology<br />
VINNAPAS ® EP 14 VAc-E 55 5,500 ± 1,500 4.0 – 5.0 3 PVOH Binder for film to board lamination, higher green strength when n.a. • no • • • • •<br />
used as blending component in PU-based adhesives<br />
VINNAPAS ® EP 17 VAc-E 60 3,800 ± 1,000 4.0 – 5.0 3 PVOH / ST Binder for film to board lamination, higher green strength when n.a. • no • • • • •<br />
used as blending component in PU-based adhesives<br />
VINNAPAS ® EP 400 VAc-E 55 2,400 ± 400 4.0 – 5.0 5 PVOH Binder for film to board lamination, higher green strength when n.a. • no • • • • •<br />
used as blending component in PU-based adhesives<br />
VINNAPAS ® EP 441 VAc-E 55 approx. 4,000 4.0 – 5.0 5 PVOH Binder for film to board lamination, higher green strength when n.a. • no • • • • •<br />
used as blending component in PU-based adhesives<br />
VINNAPAS ® EP 8010 VAc-E 60 approx. 6,000 4.0 – 5.0 -10 PVOH / ST Specially designed for difficult-to-bond substrates n.a. • no • • • • •<br />
1 VAc = vinyl acetate<br />
A = acrylic ester<br />
E = ethylene<br />
2 PVOH = poly(vinyl alcohol)<br />
ST = surfactant<br />
3 All products are produced<br />
without APEO surfactants<br />
Legend for performance attributes<br />
• • • excellent • • high • medium<br />
n.a. = not applicable<br />
24 25