Consumeables Catalog - Lincoln Electric

Typical Applications
Screw augers
Ore chutes and wearplates
Crusher rolls
Ripper teeth
Welding Positions
Flat & Horizontal
DEPOSIT COMPOSITION (1)
1 Layer
2 Layers
4 Layers
%C %Mn %Si %Cr
3.7
4.9
5.7
HARDFACING FLUX-CORED SELF-SHIELDED (FCAW-S) WIRE
1.3
1.6
1.8
Lincore®
0.7
1.0
1.1
65-O
Severe Abrasion
Deposits include higher carbon and chrome
levels than Lincore ® Key Features
60-O
Recommended for use on wear plate, coal
pulverizer rolls, earth engaging tools, and on
slurry pipe and elbows
To be used on carbon, low alloy, manganese,
stainless steels and cast iron
Limited to four layers
DIAMETERS / PACKAGING
Diameter 50 lb (22.7 kg)
500 lb (227 kg)
Coil
Speed-Feed ® in (mm)
Drum
7/64 (2.8) ED026077 ED026083
MECHANICAL PROPERTIES (1)
1 Layer
Rockwell Hardness (R ) C
2 Layers 4 Layers
57 60 64
TYPICAL OPERATING PROCEDURES
Diameter, Polarity
Wire Feed Speed Voltage Approx. Current Deposition Rate
ESO - in (mm)
m/min (in/min) (Volts)
(Amps)
kg/hr (lb/hr)
1.9 (75)
27
225
3.2 (7.0)
2.5 (100)
28
280
4.4 (9.6)
7/64 in (2.8 mm), DC+
3.8 (150)
30
360
7.5 (16.6)
1-1/8 (30)
5.1 (200)
31
420
8.9 (19.7)
6.4 (250)
32
480
11.1 (24.4)
7.6 (300)
33
500
13.5 (29.8)
4 layers of Lincore 65-O
Condition Rockwell Hardness C
As-Welded
63
Aged at 1200°F (650°C) for 2 hours
56
Aged at 1400°F (760°C) for 2 hours
54
NOTE: Postweld heat treatment up to 1400°F (760°C) will not affect abrasion resistance very significantly, but will affect hardness to some extent.
Typical results are shown above:
IMPORTANT: SPECIAL VENTILATION AND/OR EXHAUST REQUIRED
Fumes from the normal use of some welding products can contain significant quantities of components - such as chromium and manganese - which can lower the 5.0 mg/m3 maximum exposure guideline for general welding fume.
BEFORE USE, READ AND UNDERSTAND THE MATERIAL SAFETY DATA SHEET (MSDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER.
(1) Composition and properties depend upon dilution. Single layer deposit properties depend upon base metal and/or build-up material.
19.9
26.2
30.8
WELDING CONSUMABLES CATALOG ı 259