Work and results<br />
SP2.4 – Nanolayering<br />
Development of a fluorine doped tin oxide (FTO,<br />
SnO2:F) coating technique on temperature<br />
resistant polyimide.<br />
The FTO is deposited by atmospheric pressure<br />
chemical vapor deposition (APCVD) onto a temporary<br />
substrate (typical size 5x5 cm) that is heat<br />
resistant. Afterwards, a thin layer (ca 2-3 microns)<br />
of polyimide precursor is spin-coated onto<br />
the FTO layer and a firing at 400°C for 10 minutes<br />
transforms the precursor solution into practically<br />
transparent temperature resistant polyimide.<br />
By selectively destroying the lift-off layer, the<br />
FTO coated (~15 ohm/sq surface resistivity) polyimide<br />
film is released.<br />
SP2.6 - Nanoclustering<br />
Opened high-pressure autoclave showing<br />
the native nano-TiO2 suspension.<br />
Various nano-TiO2 types deposited on<br />
microscope slides as reference layers.<br />
NAPOLYDE, T. Meyer, Solaronix<br />
Nanocristalline TiO2 particles with a particle size<br />
from 5 to 37 nm (pure anatase phase) have been<br />
prepared by SOLARONIX as dispersions in vehicles<br />
such as a water/alcohol mix, pure ethanol,<br />
butanol- and terpineol-based screen-print vehicle.<br />
The TiO2 was prepared with a hydrothermal<br />
process allowing particle size selection with time<br />
and temperature parameters during the autoclave<br />
step (Oswald ripening). Sol-gel material<br />
(Bohemite) received from CSEM was modified<br />
for doctor-blade printing and a comparison TiO2<br />
solution was prepared for a sublimation nanostructuring<br />
experiment. Nano-TiO2-coated samples<br />
have been prepared and delivered to (i)<br />
SIEMENS regarding thermocatalytic effects, (ii)<br />
ELCERAM for sensor applications, and to (iii)<br />
CSEM for the CSEM "WIOS"-biochip for improving<br />
device sensitivity.<br />
Sampling of Partners (CSEM, ELCERAM, EADS,<br />
SIEMENS, KONARKA TUW) with nanocristalline<br />
TiO2 formulated to their specifications.<br />
Thanks to the Ti-Nanoxide T20 product, the partner<br />
ELCERAM was able to produce humidity<br />
sensors having a linear response, simplifying the<br />
sensor readout by the on-chip electronics.<br />
About 30 different sorts of TiO2 materials have<br />
been prepared so far to the various partners.<br />