CREEP AND STRESS-RUPTURE STRENGTHS<br />
Plate - 2050°F (1121°C) Solution Anneal<br />
Temperature<br />
°F (°C)<br />
1100 593<br />
1200 649<br />
1300 704<br />
1400 760<br />
1500 816<br />
1600 871<br />
1700 927<br />
1800 982<br />
* Extrapolation<br />
Creep Percent<br />
1.0<br />
Rupture<br />
1.0<br />
Rupture<br />
1.0<br />
Rupture<br />
1.0<br />
Rupture<br />
1.0<br />
Rupture<br />
1.0<br />
Rupture<br />
1.0<br />
Rupture<br />
1.0<br />
Rupture<br />
100 Hours<br />
29.4 (203)<br />
45.5 (315)<br />
18.9 (131)<br />
32.2 (223)<br />
12.5 (86)<br />
22.9 (158)<br />
8.5 (59)<br />
16.4 (113)<br />
5.9 (41)<br />
11.7 (81)<br />
4.2 (29)<br />
8.4 (58)<br />
3.0 (21)<br />
6.1 (42)<br />
2.2 (15)<br />
4.4 (30)<br />
Comparative Stress-Rupture Strengths<br />
Temperature<br />
°F (°C)<br />
1200 649<br />
1300 704<br />
1400 760<br />
1500 816<br />
1600 871<br />
1700 927<br />
1800 982<br />
Temperature<br />
°F (°C)<br />
1200 649<br />
1300 704<br />
1400 760<br />
1500 816<br />
1600 871<br />
1700 927<br />
1800 982<br />
<strong>HR</strong>-160 ®<br />
15.6<br />
10.8<br />
7.4<br />
5.1<br />
3.6<br />
2.5<br />
1.8<br />
<strong>HR</strong>-160**<br />
11.0<br />
7.4<br />
5.0<br />
3.4<br />
2.4<br />
1.6<br />
1.2<br />
RA333 ®<br />
16.5<br />
12.0<br />
9.2<br />
5.7<br />
3.1<br />
1.8<br />
1.05<br />
11.5<br />
8.4<br />
6.5<br />
3.7<br />
1.9<br />
1.05<br />
0.58<br />
13.0<br />
* Ksi can be converted to MPa (megapascals) by multiplying by 6.895<br />
** Extrapolation<br />
8.0<br />
5.3<br />
3.7<br />
2.5<br />
1.2<br />
0.8<br />
HAYNES ® <strong>HR</strong>-160 ® <strong>alloy</strong> 14<br />
Approximate Initial Stress, Ksi (MPa)<br />
to Produce Specified Creep in<br />
1000 Hours<br />
20.4 (141)<br />
32.2 (223)<br />
13.1 (91)<br />
22.4 (154)<br />
8.7 (60)<br />
15.7 (108)<br />
6.0 (41)<br />
11.0 (76)<br />
4.1 (28)<br />
7.7 (53)<br />
2.9 (20)<br />
5.5 (38)<br />
2.1 (14)<br />
3.9 (27)<br />
1.5 (10)<br />
2.8 (19)<br />
7.6<br />
-<br />
2.7<br />
-<br />
1.0<br />
-<br />
0.33<br />
10,000 Hours<br />
14.4* (100)<br />
22.9 (158)<br />
9.3* (64)<br />
15.6 (108)<br />
6.2* (43)<br />
10.8 (75)<br />
4.2* (29)<br />
7.4 (51)<br />
2.9* (20)<br />
5.1 (35)<br />
2.1* (14)<br />
3.6 (25)<br />
1.5* (10)<br />
2.5 (17)<br />
1.1* (8)<br />
1.8 (12)<br />
10,000 Hours Rupture Strenths (Ksi*)<br />
800HT<br />
17.5<br />
11.0<br />
7.3<br />
5.2<br />
3.5<br />
1.9<br />
1.2<br />
RA330<br />
11.0<br />
-<br />
4.3<br />
-<br />
1.7<br />
-<br />
0.63<br />
253 MA<br />
14.0<br />
8.5<br />
5.2<br />
3.75<br />
2.5<br />
1.65<br />
1.15<br />
100,000 Hours Rupture Strenths (Ksi*)<br />
RA333 800HT RA330 253 MA RA85H<br />
8.7<br />
4.6<br />
3.9<br />
2.1<br />
1.45<br />
0.97<br />
0.7<br />
RA85H<br />
12.0<br />
-<br />
5.0<br />
-<br />
2.1<br />
-<br />
0.9<br />
8.0<br />
-<br />
3.2<br />
-<br />
1.3<br />
-<br />
0.5<br />
309<br />
309<br />
11.6<br />
-<br />
100,000 Hours*<br />
16.0<br />
-<br />
5.45<br />
-<br />
1.86<br />
-<br />
0.63<br />
- -<br />
16.3 (113)<br />
- -<br />
11.0 (76)<br />
- -<br />
7.4 (51)<br />
- -<br />
5.0 (34)<br />
- -<br />
3.4 (23)<br />
- -<br />
2.4 (17)<br />
- -<br />
1.6 (11)<br />
- -<br />
1.2 (8)<br />
3.8<br />
-<br />
1.25<br />
-<br />
0.41<br />
310<br />
9.3<br />
-<br />
3.9<br />
-<br />
1.65<br />
-<br />
0.69<br />
310<br />
6.5<br />
-<br />
2.6<br />
-<br />
1.06<br />
-<br />
0.42