TYPICAL TENSILE PROPERTIES<br />
Tensile Data (plate)*<br />
Test<br />
Temperature<br />
°F (°C)<br />
70 (21)<br />
200 (93)<br />
400 (204)<br />
600 (316)<br />
800 (427)<br />
1000 (538)<br />
1200 (649)<br />
1400 (760)<br />
1600 (871)<br />
1800 (982)<br />
2000 (1093)<br />
2100 (1149)<br />
2200 (1204)<br />
* Hot-Rolled and Solution-Annealed<br />
Tensile Data (Sheet)*<br />
* Solution-Annealed<br />
Test<br />
Temperature<br />
°F (°C)<br />
70 (21)<br />
1000 (538)<br />
1200 (649)<br />
1400 (760)<br />
1600 (871)<br />
1800 (982)<br />
2000 (1093)<br />
2100 (1149)<br />
2200 (1204)<br />
Ultimate<br />
Tensile<br />
Strength<br />
Ksi MPa<br />
111.2 767<br />
104.0 717<br />
97.9 675<br />
91.9 634<br />
87.7 605<br />
81.8 564<br />
75.8 523<br />
62.1 428<br />
38.3 264<br />
20.4 140<br />
10.8 74<br />
6.0 41<br />
4.4 30<br />
Ultimate<br />
Tensile<br />
Strength<br />
Ksi MPa<br />
110.0 758<br />
82.5 569<br />
75.3 519<br />
61.1 421<br />
34.9 241<br />
18.7 129<br />
9.8 68<br />
6.6 46<br />
4.8 33<br />
Yield Strength<br />
at 0.2% Offset<br />
Ksi MPa<br />
45.6 314<br />
40.4 279<br />
33.8 233<br />
27.6 190<br />
26.0 179<br />
25.5 176<br />
25.7 177<br />
24.7 170<br />
22.1 152<br />
10.8 74<br />
5.0 34<br />
2.3 16<br />
1.6 11<br />
13<br />
Yield Strength<br />
at 0.2% Offset<br />
Ksi MPa<br />
51.2 353<br />
32.7 225<br />
31.2 215<br />
30.7 212<br />
15.9 110<br />
9.5 66<br />
4.7 32<br />
2.8 19<br />
2.0 14<br />
Elongation in<br />
1.340 in. (34.0 mm)<br />
%<br />
68<br />
69<br />
71<br />
74<br />
76<br />
76<br />
70<br />
73<br />
85<br />
90<br />
88<br />
113<br />
110<br />
Elongation in<br />
2 in. (50.8 mm)<br />
%<br />
63<br />
73<br />
62<br />
47<br />
41<br />
51<br />
53<br />
107<br />
91<br />
Reduction<br />
of Area<br />
%<br />
73<br />
74<br />
74<br />
70<br />
68<br />
69<br />
67<br />
64<br />
84<br />
98<br />
98<br />
94<br />
94<br />
HAYNES ® <strong>HR</strong>-160 ® <strong>alloy</strong>