Deformable alloy 5083 has a resistance associated to a<br />
good mechanical plasticity.<br />
Microbonding of 357.0 and 5083 aluminum alloys is made<br />
with AlTi5B1 and AlSr10 nanostructured prealloys and<br />
pressed briquettes as bands produced by melt spinning<br />
ultra-fast freezing . This method produces cooling rates up<br />
to 105 K/s and can produce nano or cvasicristaline<br />
structures with properties far beyond that of other methods<br />
and in appreciable quantities. High-speed solidification<br />
process parameters applied to AlSr10 and AlTi5B1<br />
prealloys have the following values:-melting temperature<br />
of 1100 ° C keeping the 1300 ° C, the distance of the<br />
crucible - disk is1.5 mm, disk - crucible angle of 70<br />
degrees, diameter 1 mm hole crucible, pressure applied<br />
and demonstrated 1.5 bars of 1200rot wheel<br />
revolutions/min. 1500rot/min respectively. Obtained strips<br />
were pressed into briquettes of Ф 30 mmx4 mm at room<br />
temperature and with a force of 5 tons of force.<br />
6.3.<br />
The Electrochemical Process for Obtaining Ni-Zn-P<br />
Title<br />
Double Layer Thin Film for Anticorrosive Application<br />
Vasile Soare, Marian Buraga, Ionut Constantin, Ioan<br />
Authors<br />
Carcea, Mihail Tarcolea, Ana Maria Popescu<br />
Research and Development National Institute INCDMNR-<br />
Institution IMNR<br />
“Gheorghe Asachi” Technical University of <strong>Iasi</strong><br />
Patent no. Patent application No. A/01259/2011<br />
The invention concerns a process for producing thin films<br />
of double layer alloy NiZnP, through an autocatalytic and<br />
electrochemical codeposition process in two stages: in<br />
autocatalytic stage of deposition, the deposition bath<br />
consists of nickel sulfate solution, zinc sulphate, sodium<br />
Description hypophosphite, with concentrations: 40÷60 g/l NiSO4<br />
•7H2O, 10÷20 g/l ZnSO4, 10÷20 g/l NaH2PO2•H2O, using<br />
as complexing and stabilization agents citric acid pH and<br />
ammonium chloride, pH adjusting agents, sodium<br />
hydroxide solution and agents to improve adhesion and<br />
film structure deposited thiourea and lactic acid.<br />
Codeposition electrochemical process in an electrolysis<br />