BioSciences - Polysciences, Inc.

Monomers
3-Chlorostyrene, 98% [2039-85-2] EH4d . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 138 .6 mp 62°/6mm Tg 90° n 20
D 1 .562 0 .1% BHT inhibitor
Can be used in synthesis of other styrene monomers, high refractive index
(~1 .6) polymers .
2-Cinnamoyloxyethyl acrylate [52049-17-9] HO4d . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 202 .3 n 20
D 1 .562 200ppm MEHQ C 6 H 5 CH=CHCO 2 CH 2 CH 2 OCOCH=CH 2
Photocrosslinking monomer .
Cinnamyl methacrylate [31736-34-2] U5d . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 202 .3 bp 141°/3mm n 20
D 1 .446 100 ppm MEHQ
C 6 H 5 CH=CHCH 2 OCOC(CH 3 )=CH 2
Photocrosslinking monomer .
Citraconic anhydride [616-02-4] H7bg . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 112 .1 bp 213-214° n20 D 1 .471 TSCA
Used for the reversible blocking of amino groups and for the dissociation
of nucleoprotein complexes .
Methods Enzymol., 25, 546 (1972); Biochem. J., 191, 269 (1980)
Copper (II) methacrylate [53721-10-1] X7d . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 233 .7 [H 2 C=C(CH 3 )CO 2 ] 2 Cu
Metal salt of methacrylic acid .
2-Cyanoethyl acrylate [106-71-8] BOVW6bd . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 125 .1 bp 90°/5mm n 20
D 1 .447 400-800 ppm MEHQ Tg 4° TSCA
Polar acrylate ester used in a wide range of applications including photocurable
resists for liquid crystal devices, photocurable polymer insulators
for multilayer circuitry, electroluminescent products, graft polymers for
controlled diffusion, vulcanization of rubbers and as an adhesion promoter .
trans-1,4-Cyclohexanediol dimethacrylate [38479-34-4] EHOV7d . . . . . . . . . . . . . . . . . . .
MW 252 .3 Light yellow liquid
O O
Crosslinking monomer .
O
O
Cyclohexyl acrylate, min 85% [3066-71-5] U7d . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 154 .1 bp 182-184° n 20
D 1 .467 200 ppm MEHQ Tg 19° TSCA
Bulky alkyl acrylate ester .
Cyclohexyl methacrylate, ~98% [101-43-9] EH4d . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
MW 168 .2 bp 71-74°/5mm n 20
D 1 .459 50 ppm MEHQ, 2 ppm phenothiazine
Tg 83° TSCA H 2 C=C(CH 3 )CO 2 C 6 H 11
Bulky alkyl methacrylate ester .
N,N’-Cystaminebisacrylamide, Electro Pure [60984-57-8] U6f . . . . . . . . . . . . . . . . . . . . .
MW 260 .4 mp 120-125° Requires Dry Ice
Reversible crosslinking monomer . Can be used to introduce mercaptan
groups into polymers by reducing to mercaptan after polymerization .
O
N
H
S S
O
O
O
N
H
O
O
Catalog Size
02042-5 5 g
24014-10 10 g
02092-5 5 g
01824-100 100 g
21222-25 25 g
01829-100 100 g
18912-10 10 g
02109-100 100 g
01837-100 100 g
09809-5 5 g